OBJECTIVE: To investigate the preparation and properties of the novel silica (SiO ₂)/hydroxyapatite (HAP) whiskers porous ceramics scaffold. METHODS: The HAP whiskers were modified by the SiO ₂ microspheres using the Stöber method. Three types of SiO ₂/HAP whiskers were fabricated under different factors (for the No.1 samples, the content of tetraethoxysilane, stirring time, calcination temperature, and soaking time were 10 mL, 12 hours, 560℃, and 0.5 hours, respectively; and in the No.2 samples, those were 15 mL, 24 hours, 650℃, and 2 hours, respectively; while those in the No.3 samples were 20 mL, 48 hours, 750℃, and 4 hours, respectively). The phase and morphology of the self-made HAP whisker and 3 types of SiO ₂/HAP whiskers were detected by the X-ray diffraction analysis and scanning electron microscopy. Taken the self-made HAP whisker and 3 types of SiO ₂/HAP whiskers as raw materials, various porous ceramic materials were prepared using the mechanical foaming method combined with extrusion molding method, and the low-temperature heat treatment. The pore structure of porous ceramics was observed by scanning electron microscopy. Its porosity and pore size distribution were measured. And further the axial compressive strength was measured, and the biodegradability was detected by simulated body fluid. Cell counting kit 8 method was used to conduct cytotoxicity experiments on the extract of porous ceramics. RESULTS: The SiO ₂ microspheres modified HAP whiskers and its porous ceramic materials were prepared successfully, respectively. In the SiO ₂/HAP whiskers, the amorphous SiO ₂ microspheres with a diameter of 200 nm, uniform distribution and good adhesion were attached to the surface of the whiskers, and the number of microspheres was controllable. The apparent porosity of the porous ceramic scaffold was about 78%, and its pore structure was composed of neatly arranged longitudinal through-holes and a large number of micro/nano through-holes. Compared with HAP whisker porous ceramic, the axial compressive strength of the SiO ₂/HAP whisker porous ceramics could reach 1.0 MPa, which increased the strength by nearly 4 times. Among them, the axial compressive strength of the No.2 SiO ₂/HAP whisker porous ceramic was the highest. The SiO ₂ microspheres attached to the surface of the whiskers could provide sites for the deposition of apatite. With the content of SiO ₂ microspheres increased, the deposition rate of apatite accelerated. The cytotoxicity level of the prepared porous ceramics ranged from 0 to 1, without cytotoxicity. CONCLUSION SiO ₂/HAP whisker porous ceramics have good biological activity, high porosity, three-dimensional complex pore structure, good axial compressive strength, and no cytotoxicity, which make it a promising scaffold material for bone tissue engineering.
Animals ; Durapatite ; Porosity ; Vibrissae ; Apatites ; Ceramics ; Silicon Dioxide

Ameloblasts are specialized cells derived from the dental epithelium that produce enamel, a hierarchically structured tissue comprised of highly elongated hydroxylapatite (OHAp) crystallites. The unique function of the epithelial cells synthesizing crystallites and assembling them in a mechanically robust structure is not fully elucidated yet, partly due to limitations with in vitro experimental models. Herein, we demonstrate the ability to generate mineralizing dental epithelial organoids (DEOs) from adult dental epithelial stem cells (aDESCs) isolated from mouse incisor tissues. DEOs expressed ameloblast markers, could be maintained for more than five months (11 passages) in vitro in media containing modulators of Wnt, Egf, Bmp, Fgf and Notch signaling pathways, and were amenable to cryostorage. When transplanted underneath murine kidney capsules, organoids produced OHAp crystallites similar in composition, size, and shape to mineralized dental tissues, including some enamel-like elongated crystals. DEOs are thus a powerful in vitro model to study mineralization process by dental epithelium, which can pave the way to understanding amelogenesis and developing regenerative therapy of enamel.
Mice ; Animals ; Durapatite/metabolism* ; Dental Enamel/metabolism* ; Ameloblasts/metabolism* ; Amelogenesis ; Stem Cells ; Organoids

Ginsenoside Rb1, the effective constituent of ginseng, has been demonstrated to play favorable roles in improving the immunity system. However, there is little study on the osteogenesis and angiogenesis effect of Ginsenoside Rb1. Moreover, how to establish a delivery system of Ginsenoside Rb1 and its repairment ability in bone defect remains elusive. In this study, the role of Ginsenoside Rb1 in cell viability, proliferation, apoptosis, osteogenic genes expression, ALP activity of rat BMSCs were evaluated firstly. Then, micro-nano HAp granules combined with silk were prepared to establish a delivery system of Ginsenoside Rb1, and the osteogenic and angiogenic effect of Ginsenoside Rb1 loaded on micro-nano HAp/silk in rat calvarial defect models were assessed by sequential fluorescence labeling, and histology analysis, respectively. It revealed that Ginsenoside Rb1 could maintain cell viability, significantly increased ALP activity, osteogenic and angiogenic genes expression. Meanwhile, micro-nano HAp granules combined with silk were fabricated smoothly and were a delivery carrier for Ginsenoside Rb1. Significantly, Ginsenoside Rb1 loaded on micro-nano HAp/silk could facilitate osteogenesis and angiogenesis. All the outcomes hint that Ginsenoside Rb1 could reinforce the osteogenesis differentiation and angiogenesis factor's expression of BMSCs. Moreover, micro-nano HAp combined with silk could act as a carrier for Ginsenoside Rb1 to repair bone defect.
Alginates/pharmacology* ; Animals ; Bone Regeneration ; Cell Differentiation ; Durapatite/pharmacology* ; Ginsenosides ; Osteogenesis ; Rats ; Silk/pharmacology* ; Tissue Scaffolds

OBJECTIVES: The purpose of the study was to evaluate the effect of hydroxyapatite (HA)-based desensiti-zing agents and determine their influence on the bonding performance of mild universal adhesives. METHODS: Mid-coronal dentin samples were sectioned from human third molars and prepared for a dentin-sensitive model. According to desensitizing applications, they were randomly divided into four groups for the following treatments: no desensitizing treatment (control), Biorepair toothpaste (HA-based desensitizing toothpaste) treatment, Dontodent toothpaste (HA-based desensitizing toothpaste) treatment, and HA paste treatment. Dentin tubular occlusion and occluded area ratios were evaluated by scanning electron microscopy (SEM). Furthermore, All-Bond Universal, Single Bond Universal, and Clearfil Universal Bond were applied to the desensitized dentin in self-etch mode. The wettability and surface free energy (SFE) of desensitized dentin were evaluated by contact angle measurements. Bonded specimens were sectioned into beams and tested for micro-tensile bond strength to analyze the effect of desensitizing treatment on the bond strength to dentin of universal adhesives. RESULTS: SEM revealed that the dentin tubule was occluded by HA-based desensitizing agents, and the area ratios for the occluded dentin tubules were in the following order: HA group>Biorepair group>Dontodent group (P<0.05). Contact angle analysis demonstrated that HA-based desensitizing agents had no statistically significant influence on the wettability of the universal adhesives (P>0.05). The SFE of dentin significantly increased after treatment by HA-based desensitizing agents (P<0.05). The micro-tensile bond strength test showed that HA-based desensitizing toothpastes always decreased the μTBS values (P<0.05), whereas the HA paste group presented similar bond strength to the control group (P>0.05), irrespective of universal adhesive types. CONCLUSIONS HA-based desensitizing agents can occlude the exposed dentinal tubules on sensitive dentin. When mild and ultra-mild universal adhesives were used for subsequent resin restoration, the bond strength was reduced by HA-based desensitizing toothpastes, whereas the pure HA paste had no adverse effect on bond strength.
Humans ; Dental Cements/analysis* ; Dentin/chemistry* ; Durapatite/pharmacology* ; Tensile Strength ; Toothpastes

OBJECTIVE: To compare treatment effect of monolateral and circular external fixator in infectious tibial nonunion and to explore external fixation structure with better osteogenic ability and fewer complications. METHODS: A retrospective analysis was performed on 150 patients with infectious tibial nonunion admitted from January 2010 to December 2014. Patients who met the inclusion and exclusion criteria were divided into monolateral fixator group and circular fixator group according to the type of external fixation. Demographic and perioperative data of the two groups were collected. New bone quality was assessed by pixels ratio, treatment effect was assessed by complications. Notes for treatment was explored by case analysis. RESULTS: A total of 64 patients with infectious mid-tibial nonunion were included, 26 in monolateral fixator group and 38 in circular fixator group. There was no difference in demographic data between two groups. The pixel ratio of new bone between two groups was from 0.91 to 0.97 with an average of (0.94±0.03), and from 0.93 to 0.97 with an average of(0.95±0.02), respectively, with no statistical significance (P>0.05). The external fixation index was from 34.1 to 50.6 with an average of (42.3±8.3) days /cm in monolateral fixator group and from 44.5 to 56.1 with an average of (45.8±10.3) days/cm in the circular fixator group, and the difference was not statistically significant (P>0.05). There were 7 cases (26.9%) of complications in monolateral fixator group and 5 cases (13.2%) in circular fixator group, the difference was not statistically significant (P>0.05), but 5 cases of foot ptosis in monolateral fixator group and none in circular fixator group. The time of weight bearing in monolateral fixator group was later than that in circular fixator group, and the difference was statistically significant (P<0.05). CONCLUSION Monolateral and circular fixators can achieve equivalent bone formation in the treatment of infected tibial nonunion. Circular fixator is recommended for patients with severe osteoporosis or concomitant medical diseases requiring early weight bearing. Hydroxyapatite coated screws are recommended if a monolateral external fixator is selected when the expected enlarged length is long and the fixation time is long and close monitoring of the ankle movement is required to avoid foot droop.
Humans ; Tibial Fractures/surgery* ; Retrospective Studies ; External Fixators ; Tibia/surgery* ; Treatment Outcome ; Hydroxyapatites

Objective: To study the effect of hydroxyapatite (HA) based agents on the bonding properties of universal adhesive with different application modes, and to provide evidence for the use of adhesives after desensitization treatment. Methods: Sixty impacted third molars were extracted and selected (acquired from Department of Oral and Maxillofacial Surgery, College of Stomatology, Xi'an Jiaotong University). Four third molars were used to prepare 1 mm thick dentin disks and treated with 1% citric acid to simulate sensitive tooth models. The dentin surfaces were observed by scanning electron microscope (SEM) after treating with no desensitization (control group), desensitized by HA based toothpaste Biorepair and Dontodent Sensitive respectively (desensitizing toothpaste A group and B group), or HA paste treatment (desensitizing paste group ) (n=2 per group). The remaining teeth were selected to expose the mid-coronal dentin and establish dentin sensitivity models. Then, the specimens were divided into 4 former groups and received corresponding treatment. Each group was randomly divided into 2 subgroups, and intermediately strong universal adhesive (G-Premio Bond) was applied on the desensitized dentin by either etch-and-rinse mode or self-etch mode. Resin-dentin slice specimens (n=4 per subgroup), microtensile specimens (n=20 per subgroup) and slice specimens (n=6 per subgroup) were prepared. The microstructure and nanoleakage of the adhesive interfaces were observed by scanning electron microscopy (SEM). The microtensile strength (bond strength) and fracture mode were tested and recorded. The water permeability of the adhesive interface was observed by laser scanning confocal microscopy (LSCM). Results: SEM showed that desensitizing toothpaste and desensitizing paste could partially or entirely occlude most of the dentin tubules. For the etch-and-rinse mode, the bond strength of specimens treated with toothpaste A [(40.98±4.60) MPa], toothpaste B [(40.89±4.64) MPa] and HA paste [(41.48±3.65) MPa] was significantly higher than that of the control group [(38.58±4.28) MPa] (F=3.89,P<0.05). There was no statistically significant difference in bond strength among the 4 subgroups for self-etch modes (F=0.48,P>0.05). After desensitization, the bond strength of the control group and desensitizing groups in the self-etch mode was significantly higher than that in the etch-and-rinse mode (P<0.05). The overall fracture modes were mixed failure and interfacial failure in the control group and desensitizing groups. SEM showed speckled silver-stained particles deposited along the bottom of the hybrid layer on the bond interface of etch-and-rinse mode, and there were few silver-stained particles deposited on the bond interface of self-etch mode. LSCM showed continuous linear penetration in the hybrid layer of etch-and-rinse mode subgroups and discontinuous linear penetration in the hybrid layer of self-etch mode subgroups. Conclusions: HA based desensitizers have no adverse effect on the bond strength of intermediately strong universal adhesive and show good bonding performance accompanied with the self-etch mode.
Adhesives ; Dental Bonding ; Dental Cements ; Dentin ; Dentin-Bonding Agents ; Durapatite ; Humans ; Materials Testing ; Microscopy, Electron, Scanning ; Resin Cements ; Tensile Strength

OBJECTIVES: To investigate the dynamic process of the self-assembly behaviors of a full-length human amelogenin (AM) and its functional fragments tyrosine-rich amelogenin peptide (TRAP) and leucine-rich amelogenin peptide(LRAP) METHODS: The full-length human AM and its functional fragments, TRAP and LRAP, were reassembled and purified RESULTS: When pH=8, the full-length human AM and TRAP assembly started spontaneously and formed "nanospheres" after 15 min.The nanospheres formed by TRAP existed independently, with a uniform size but without obvious internal structures. The full-length AM was assembled hierarchically, which formed "nanospheres" and further extended in all directions, formed a chain structure, and then aggregated into a net. The self-assembly behavior of LRAP was not obvious. Proteins mostly existed in the form of monomers without "nanosphere" formation. Only few oligomers were observed. The full-length AM was induced independently for 3 days to form rod-shaped HA crystals. TRAP and LRAP proteins were added, after 3 days the crystal elongation was obvious in the c axis, but the growth in plane A and plane B was poor. CONCLUSIONS The self-assembly and mineralization behaviors of full-length human AM, TRAP, and LRAP were consistent with the directional growth mechanism of HA crystals
Amelogenin ; Dental Enamel Proteins ; Durapatite ; Humans

OBJECTIVES: This study was performed to evaluate the occlusion of monetite paste on dentine tubule and provide a new potential method for treating dentine hypersensitivity. METHODS: Calcium oxide, strontium chloride, and polyethylene glycol phosphate were mixed in a certain proportion and ground in a planetary ball mill. The reaction was carried out by adjusting the pH to obtain monetite and hydroxyapatite paste. The morphological characteristics of the paste were observed through scanning electron microscope (SEM). The structure and composition were analyzed through X-ray diffraction (XRD) and Fourier transform infrared spectrometer (FTIR). The extracted third molar was selected to undergo demineralization to establish the RESULTS: XRD and FTIR showed that the composition of the paste was mainly monetite, and the composition of hydroxyapatite paste was mainly composed of hydroxyapatite. SEM revealed that the size of the crystal particles of the synthesized paste was tens to hundreds of nanometers. Monetite and hydroxyapatite paste could produce a thicker mineralization layer on the dentin surface, and the mineralization of the dentin tubules of monetite was deeper than that of hydroxyapatite paste. The microhardness of the monetite paste group was significantly less than those of the hydroxyapatite paste groups ( CONCLUSIONS Monetite paste could effectively block the exposed dentin tubules and be used for treating dentin hypersensitivity.
Calcium Phosphates ; Dentin ; Dentin Sensitivity ; Durapatite ; Humans ; Microscopy, Electron, Scanning

Increasing demands for esthetic dental treatment, zirconia, which has high mechanical and esthetic properties, had been applied more and more in clinics. Therefore, assessment of biocompatibility of zirconia is necessary. In this article, a review of in vivo studies of zirconia compatibility was performed. In vivo studies showed zirconia had great biocompatibility both on soft and hard tissue. Studies with various animals and patients reported high biocompatibility of zirconia. In terms of bone synthesis and bone adhesion, zirconia showed similar biocompatible properties to titanium. On the other hand, zirconia could be used as implant. For using as an implant, various methods of Hydroxyapatite (HA) coating had been suggested. Since HA coating on titanium implant showed some problems such as low bonding strength and degeneration of HA, HA-zirconia composite, HA-coated zirconia, and HA-zirconia functionally graded material (FGM) or intermediate layer of alumina had been proposed. These methods showed higher bonding strength and biocompatibility.
Aluminum Oxide ; Animals ; Durapatite ; Hand ; Humans ; Titanium

Skeletal mineralization is initiated in matrix vesicles (MVs), the small extracellular vesicles derived from osteoblasts and chondrocytes. Calcium and inorganic phosphate (Pi) taken up by MVs form hydroxyapatite crystals, which propagate on collagen fibrils to mineralize the extracellular matrix. Insufficient calcium or phosphate impairs skeletal mineralization. Because active vitamin D is necessary for intestinal calcium absorption, vitamin D deficiency is a significant cause of rickets/osteomalacia. Chronic hypophosphatemia also results in rickets/osteomalacia. Excessive action of fibroblast growth factor 23 (FGF23), a key regulator of Pi metabolism, leads to renal Pi wasting and impairs vitamin D activation. X-linked hypophosphatemic rickets (XLH) is the most common form of hereditary FGF23-related hypophosphatemia, and enhanced FGF receptor (FGFR) signaling in osteocytes may be involved in the pathogenesis of this disease. Increased extracellular Pi triggers signal transduction via FGFR to regulate gene expression, implying a close relationship between Pi metabolism and FGFR. An anti-FGF23 antibody, burosumab, has recently been developed as a new treatment for XLH. In addition to various forms of rickets/osteomalacia, hypophosphatasia (HPP) is characterized by impaired skeletal mineralization. HPP is caused by inactivating mutations in tissue-nonspecific alkaline phosphatase, an enzyme rich in MVs. The recent development of enzyme replacement therapy using bone-targeting recombinant alkaline phosphatase has improved the prognosis, motor function, and quality of life in patients with HPP. This links impaired skeletal mineralization with various conditions, and unraveling its pathogenesis will lead to more precise diagnoses and effective treatments.
Absorption ; Alkaline Phosphatase ; Calcium ; Chondrocytes ; Collagen ; Diagnosis ; Durapatite ; Enzyme Replacement Therapy ; Extracellular Matrix ; Extracellular Vesicles ; Familial Hypophosphatemic Rickets ; Fibroblast Growth Factors ; Gene Expression ; Humans ; Hypophosphatasia ; Hypophosphatemia ; Metabolism ; Miners ; Osteoblasts ; Osteocytes ; Prognosis ; Quality of Life ; Receptors, Fibroblast Growth Factor ; Rickets ; Signal Transduction ; Vitamin D ; Vitamin D Deficiency