BACKGROUND: Poly (lactic acid) (PLA) is a biodegradable polyester that has been exploited for a variety of biomedical applications, including tissue engineering. The incorporation of b-tricalcium phosphate (TCP) into PLA has imparted bioactivity to the polymeric matrix. METHODS: We have modified a 90%PLA-10%TCP composite with SiO2 and MgO (1, 5 and 10 wt%), separately, to further enhance the material bioactivity. Filaments were prepared by extrusion, and scaffolds were fabricated using 3D printing technology associated with fused filament fabrication. RESULTS: The PLA-TCP-SiO2 composites presented similar structural, thermal, and rheological properties to control PLA and PLA-TCP. In contrast, the PLA-TCP-MgO composites displayed absence of crystallinity, lower polymericmolecular weight, accelerated degradation ratio, and decreased viscosity within the 3D printing shear rate range. SiO2 andMgO particles were homogeneously dispersed within the PLA and their incorporation increased the roughness and protein adsorption of the scaffold, compared to a PLA-TCP scaffold. This favorable surface modification promoted cell prolif-eration, suggesting that SiO2 and MgO may have potential for enhancing the bio-integration of scaffolds in tissueengineering applications. However, high loads of MgO accelerated the polymeric degradation, leading to an acid environment that imparted the composite biocompatibility. The presence of SiO2 stimulated mesenchymal stem cells differentiation towards osteoblast; enhancing extracellular matrix mineralization, alkaline phosphatase (ALP) activity, and bonerelated genes expression. CONCLUSION The PLA-10%TCP-10%SiO2 composite presented the most promising results, especially for bone tissue regeneration, due to its intense osteogenic behavior. PLA-10%TCP-10%SiO2 could be used as an alternative implant forbone tissue engineering application.

PURPOSE: This study incorporated the nanomaterial, nanostructured silver vanadate decorated with silver nanoparticles (AgVO3), into heat-cured resin (HT) at concentrations of 2.5%, 5%, and 10% and compared the adhesion of multispecies biofilms, surface characteristics, and mechanical properties with conventional heat-cured (HT 0%) and printed resins. MATERIALS AND METHODS: AgVO3 was incorporated in mass into HT powder. A denture base resin was used to obtain printed samples. Adhesion of a multispecies biofilm of Candida albicans, Candida glabrata, and Streptococcus mutans was evaluated by colony-forming units per milliliter (CFU/mL) and metabolic activity. Wettability, roughness, and scanning electron microscopy (SEM) were used to assess the physical characteristics of the surface. The mechanical properties of flexural strength and elastic modulus were tested. RESULTS: HT 10%-AgVO3 showed efficacy against S. mutans; however, it favored C. albicans CFU/mL (P < .05). The printed resin showed a higher metabolically active biofilm than HT 0% (P < .05). There was no difference in wettability or roughness between groups (P > .05). Irregularities on the printed resin surface and pores in HT 5%-AgVO3 were observed by SEM. HT 0% showed the highest flexural strength, and the resins incorporated with AgVO3 had the highest elastic modulus (P < .05). CONCLUSION The incorporation of 10% AgVO3 into heat-cured resin provided antimicrobial activity against S. mutans in a multispecies biofilm did not affect the roughness or wettability but reduced flexural strength and increased elastic modulus. Printed resin showed higher irregularity, an active biofilm, and lower flexural strength and elastic modulus than heat-cured resin.

Purpose: In industrialized countries, air pollutants levels have been monitored closely for environmental and research issues. Using Italian data, we aimed to investigate the association between air pollutants levels and semen parameters in a cohort of non-Finnish white-European men presenting for couple’s infertility. Materials and Methods: Complete demographic and laboratory data from 1,152 infertile men consecutively assessed between January 2015 and January 2018 were analyzed. Semen analyses were based on the 2010 World Health Organization reference criteria. Health-significant comorbidities were scored with the Charlson Comorbidity Index (CCI). We analyzed the annual average level of the three main markers of air pollution (Pm10, Pm2.5, and NO2) between 2014 and 2018. Descriptive statistics, linear and logistic regression analyses tested the association between air pollutants levels and semen parameters. Results: Of 1,152 men, 87 (7.55%) had normal sperm parameters at first semen analysis. Of 1,065 patients with abnormal semen analyses, 237 (22.25%), 324 (30.42%), and 287 (26.95%) patients presented 1, 2 or 3 abnormalities, respectively, and 217 (20.38%) were azoospermic. At linear regression analysis, Pm10, Pm2.5, and NO2 were negatively associated with sperm morphology (Pm10: β=-0.5288 µg/m3, p=0.001; Pm2.5: β=-0.5240 µg/m3, p=0.019; NO2: β=-0.4396 µg/m3, p<0.0001). Furthermore, the adjusted odds of normal sperm morphology <4% were 1.06 (95% confidence interval [CI], 1.03–1.09; p=0.007) for Pm10, 1.07 (95% CI, 1.03–1.11; p=0.007) for Pm 2.5, and 1.03 (95% CI, 1.02–1.05; p=0.001) for NO2, respectively. Conclusions In a large homogenous cohort of infertile men, Pm10, Pm 2.5, and NO2 levels were negatively associated with sperm morphology. Conversely, no clear association was observed with other macroscopic sperm parameters.

Background: Due to the poor outcomes associated with the impairment of physical function and muscle strength in patients on maintenance dialysis, it is important to understand the factors that may influence physical function and muscle strength. The aim of this study was to explore the factors associated with physical function in hemodialysis and peritoneal dialysis patients. Methods: Patients with chronic kidney disease on dialysis for at least 3 months, aged 18 years old or above, were enrolled. Physical function was assessed by handgrip strength, gait and sit-to-stand tests, and the Short Physical Performance Battery (SPPB). Clinical and laboratory data were collected to verify the association with physical function parameters through binary logistic regression. Results: One-hundred ninety patients on maintenance dialysis were included; 140 patients (73.7%) on hemodialysis and 50 (26.3%) on peritoneal dialysis. The mean age was 57.3 ± 14.9 years, 109 (57.4%) were male, and 87 (45.8%) were older than 60 years. The median SPPB was 8.0 points (6.0–10.0 points) and the mean ± standard deviation of handgrip strength was 24.7 ± 12.2 kg. Binary logistic regression showed that age, type of renal replacement therapy, diabetes mellitus, and serum creatinine were significantly associated with both higher 4-meter gait test times and lower SPPB scores. Only age and diabetes mellitus were associated with higher sit-to-stand test times, while age and ferritin were associated with lower handgrip strength. Conclusion Age, diabetes mellitus, serum creatinine, and hemodialysis modality are factors related to physical function in dialysis patients.

Background: Due to the poor outcomes associated with the impairment of physical function and muscle strength in patients on maintenance dialysis, it is important to understand the factors that may influence physical function and muscle strength. The aim of this study was to explore the factors associated with physical function in hemodialysis and peritoneal dialysis patients. Methods: Patients with chronic kidney disease on dialysis for at least 3 months, aged 18 years old or above, were enrolled. Physical function was assessed by handgrip strength, gait and sit-to-stand tests, and the Short Physical Performance Battery (SPPB). Clinical and laboratory data were collected to verify the association with physical function parameters through binary logistic regression. Results: One-hundred ninety patients on maintenance dialysis were included; 140 patients (73.7%) on hemodialysis and 50 (26.3%) on peritoneal dialysis. The mean age was 57.3 ± 14.9 years, 109 (57.4%) were male, and 87 (45.8%) were older than 60 years. The median SPPB was 8.0 points (6.0–10.0 points) and the mean ± standard deviation of handgrip strength was 24.7 ± 12.2 kg. Binary logistic regression showed that age, type of renal replacement therapy, diabetes mellitus, and serum creatinine were significantly associated with both higher 4-meter gait test times and lower SPPB scores. Only age and diabetes mellitus were associated with higher sit-to-stand test times, while age and ferritin were associated with lower handgrip strength. Conclusion Age, diabetes mellitus, serum creatinine, and hemodialysis modality are factors related to physical function in dialysis patients.

Purpose: Little is known regarding the accuracy of clinical magnetic resonance imaging (MRI) protocols with acceptable scan times in sinus graft assessment. The aim of this study was to evaluate the correlations between MRI and cone-beam computed tomographic (CBCT) measurements of maxillary sinus grafts using 2 different clinical MRI imaging protocols. Materials and Methods: A total of 15 patients who underwent unilateral sinus lift surgery with biphasic calcium phosphate were included in this study. CBCT, T1-weighted MRI, and T2-weighted MRI scans were taken 6 months after sinus lift surgery. Linear measurements of the maximum height and buccolingual width in coronal images, as well as the maximum anteroposterior depth in sagittal images, were performed by 2 trained observers using CBCT and MRI Digital Imaging and Communication in Medicine files. Microcomputed tomography (micro-CT) was also performed to confirm the presence of bone tissue in the grafted area. Correlations between MRI and CBCT measurements were assessed with the Pearson test. Results: Significant correlations between CBCT and MRI were found for sinus graft height (T1-weighted, r=0.711 and p<0.05; T2-weighted, r=0.713 and p<0.05), buccolingual width (T1-weighted, r=0.892 and p<0.05; T2-weighted, r=0.956 and p<0.05), and anteroposterior depth (T1-weighted, r=0.731 and p<0.05; T2-weighted, r=0.873 and p<0.05). The presence of bone tissue in the grafted areas was confirmed via micro-CT. Conclusion Both MRI pulse sequences tested can be used for sinus graft measurements, as strong correlations with CBCT were found. However, correlations between T2-weighted MRI and CBCT were slightly higher than those between T1-weighted MRI and CBCT.

Objective: To evaluate the anti Candida activity of Hyptis martiusii decoction and its major compound, caffeic acid alone or in the presence of fluconazole, as well as their cytotoxic effect. Methods: The decoction was characterized using high performance liquid chromatography coupled with diode array detector. For the antifungal activity, the minimum inhibitory concentration (MIC) and the potential effect of the decoction with the fluconazole were evaluated by microdilution method using 96-well microtiter trays. The osmotic fragility test was performed using erythrocytes under saline stress. All tests were performed in triplicate. Results: The chemical characterization of the decoction was performed by high performance liquid chromatography and revealed the presence of seven compounds, including caffeic acid as major constituent. The antifungal tests demonstrated that both decoction (DHm) and caffeic acid obtained from Hyptis martiusii presented MIC and MFC ≥ 4096 μg/mL against Candida albicans and Candida tropicalis strains. However, in the presence of fluconazole, DHm and caffeic acid presented IC

This study aimed to show that the physicochemical proprieties obtained by Fourier transform infrared spectroscopy (FTIR), thermogravimetry (TG), and scanning electronic microscopy (SEM) can be useful tools for evaluating the quality of active pharmaceutical ingredients (APIs) and pharmaceutical products. In addition, a simple, sensitive, and efficient method employing HPLC-DAD was developed for simulta-neous determination of lidocaine (LID), ciprofloxacin (CFX) and enrofloxacin (EFX) in raw materials and in veterinary pharmaceutical formulations. Compounds were separated using a Gemini C18 (250 mm × 4.6 mm, 5 μm) Phenomenex ? column, at a temperature of 25 °C, with a mobile phase containing 10 mM of phosphoric acid (pH 3.29): acetonitrile (85.7:14.3, v/v) and a flow rate of 1.5 mL/min. Physicochemical characterization by TG, FTIR, and SEM of raw materials of LID, CFX, and EFX provided information useful for the evaluation, differentiation, and qualification of raw materials. Finally, the HPLC method was proved to be useful for evaluation of raw material and finished products, besides satisfying the need for an analytical method that allows simultaneous determination of EFX, CFX, and LID, which can also be extended to other matrices and applications.

OBJECTIVES: Chitosan has been widely investigated and used. However, the literature does not refer to the shelf life of this solution. This study evaluated, through the colorimetric titration technique and an analysis of dentin micro-hardness, the shelf life of 0.2% chitosan solution. MATERIALS AND METHODS: Thirty human canines were sectioned, and specimens were obtained from the second and third slices, from cemento-enamel junction to the apex. A 0.2% chitosan solution was prepared and distributed in 3 identical glass bottles (v1, v2, and v3) and 3 plastic bottles (p1, p2, and p3). At 0, 7, 15, 30, 45, 60, 90, 120, 150, and 180 days, the specimens were immersed in each solution for 5 minutes (n = 3 each). The chelating effect of the solution was assessed by micro-hardness and colorimetric analysis of the dentin specimens. 17% EDTA and distilled water were used as controls. Data were analyzed statistically by two-way and Tukey-Kramer multiple comparison (α = 0.05). RESULTS: There was no statistically significant difference among the solutions with respect to the study time (p = 0.113) and micro-hardness/time interaction (p = 0.329). Chitosan solutions and EDTA reduced the micro-hardness in a similar manner and differed significantly from the control group (p < 0.001). Chitosan solutions chelated calcium ions throughout the entire experiment. CONCLUSIONS: Regardless of the storage form, chitosan demonstrates a chelating property for a minimum period of 6 months.
Calcium ; Chelating Agents ; Chitosan* ; Colorimetry* ; Dentin* ; Edetic Acid ; Glass ; Humans ; Ions ; Plastics ; Product Packaging* ; Water

Objective To investigate the antifungal activity of the fern species Lygodium venustum (L. venustum) and Pityrogramma calomelanos (P. calomelanos) against Candida albicans and Candida tropicalis strains. Methods The microdilution method was used to evaluate the antifungal activity, as well as the modulating effects of ethanolic extracts of these plants in combination with fluconazole. The minimum inhibitory concentration (MIC), minimum fungicide concentration and morphological changes were also determined. Results The extract obtained from L. venustum presented a MIC > 8 192 μg/mL, while the extract obtained from and P. calomelanos presented a MIC = 8 192 μg/mL, indicating that they present weak antifungal activity. However, combination of the extracts with Fluconazole potentiated the antifungal activity of this drug. At different experimental conditions, such as concentration of the extract and type of strain, the extracts inhibited hyphae and pseudohyphae formation, indicating that these fern species can affect the morphology of the fungi. Conclusions The extracts obtained from the fern species L. venustum and P. calomelanos dose not present significant antifungal activity. However, P. calomelanos potentiates the activity of fluconazole and both extracts inhibits the morphological changes in Candida species, indicating that they have potential pharmacological activity as modulators of fungal biology. Therefore, novel studies are required to characterize the interference of these extracts in the virulence and pathogenicity of Candida species as well as the potential of fern species to treat fungal infections.