ObjectiveTo establish the multi-technique characteristic profiles of Alumen by X-ray diffraction（XRD）， Fourier-transform infrared spectroscopy（FTIR） and thermogravimetric-differential thermal analysis（TG-DTA）， and to explore the spectral characteristics for rapid identification of Alumen and its potential adulterant， Ammonium alum. MethodsA total of 27 batches of Alumen samples from 8 production regions were collected for preliminary identification based on visual characteristics. The PDF standard cards of XRD were used to differentiate Alumen from A. alum， and the XRD characteristic profiles of Alumen were established， and then the common peaks were screened. Based on hierarchical clustering analysis（HCA） and orthogonal partial least squares-discriminant analysis（OPLS-DA）， the characteristic information that could be used for identification of Alumen was selected with variable importance in the projection（VIP） value>1. FTIR characteristic profiles of Alumen were established， and key wavenumbers for identification were screened by HCA and OPLS-DA with VIP value>1. Meanwhile， the thermogravimetric differences between Alumen and A. alum were analyzed by TG-DTA， and the thermogravimetric traits that could be used for identification were screened. ResultsAlumen and A. alum could not be effectively distinguished by traits alone. However， by comparing the PDF standard cards of XRD， 15 batches of Alumen and 12 batches of A. alum could be distinguished. In the XRD profiles， 10 characteristic peaks were confirmed， corresponding to diffraction angles of 14.560°， 24.316°， 12.620°， 32.122°， 17.898°， 34.642°， 27.496°， 46.048°， 40.697° and 21.973°. In the FTIR profiles， 4 wavenumber ranges（399.193-403.050， 1 186.010-1 471.420， 1 801.190-2 620.790， 3 612.020-3 997.710 cm^-1） and 12 characteristic wavenumbers（1 428.994， 1 430.922， 1 432.851， 1 434.779， 1 436.708， 1 438.636， 1 440.565， 1 442.493， 1 444.422， 1 446.350， 1 448.279， 1 450.207 cm^-1） were identified. In the TG-DTA profiles， there were characteristic decomposition peaks of ammonium ion and mass reduction features near 555.34 ℃ for A. alum. These characteristics could serve as important criteria for distinguishing the authenticity of Alumen. ConclusionXRD， FTIR and TG-DTA can be used to rapidly detect Alumen and A. alum， and combined with the discriminant features selected through chemometrics， the rapid and accurate identification of Alumen and A. alum can be achieved. The research findings provide new approaches for the rapid identification of Alumen.

ObjectiveTo investigate the processing technology of calcined Haematitum based on the concept of quality by design（QbD） and to assess its health risk. MethodsTaking whole iron content， Fe²⁺ dissolution content and looseness as critical quality attributes（CQAs）， and calcination temperature， calcination time， spreading thickness and particle size as critical process parameters（CPPs） determined by the failure mode and effect analysis（FMEA）， the processing technology of calcined Haematitum was optimized by orthogonal test combined with analytic hierarchy process-criteria importance through intercriteria correlation（AHP-CRITIC） hybrid weighting method. The contents of heavy metals and harmful elements were determined by inductively coupled plasma mass spectrometry， and the health risk assessment was carried out by daily exposure（EXP）， target hazard quotient（THQ） and lifetime cancer risk（LCR）， and the theoretical value of the maximum limit was deduced. ResultsThe optimal processing technology for calcined Haematitum was calcination at 650 ℃， calcination time of 1 h， particle size of 0.2-0.5 cm， spreading thickness of 1 cm， and vinegar quenching for 1 time［Haematitum-vinegar（10：3）］. The contents of 5 heavy metals and harmful elements in 13 batches of calcined Haematitum were all decreased with reductions of up to 5-fold. The cumulative THQ of 2 batches of samples was>1， while the cumulative THQ of all batches of Haematitum was>1. The LCR of As in 1 batches of Haematitum was 1×10^-6-1×10^-4， and the LCR of the rest was<1×10^-6， and the LCRs of calcined Haematitum were all<1×10^-6， indicating that the carcinogenic risk of calcined Haematitum was low， but special attention should still be paid to Haematitum medicinal materials. Preliminary theoretical values of the maximum limits of Cu， As， Cd， Pb and Hg were formulated as 1 014， 25， 17， 27， 7 mg·kg^-1. ConclusionThe optimized processing technology of calcined Haematitum is stable and feasible， and the contents of heavy metals and harmful elements are reduced after processing. Preliminary theoretical values of the maximum limits of Cu， As， Cd， Pb and Hg are formulated to provide a scientific basis for the formulation of standards for the limits of harmful elements in Haematitum.

ObjectiveBased on the concept of quality by design（QbD）， the processing process of calcined Pyritum was optimized， and its X-ray diffraction（XRD） fingerprint was established. MethodsThe safety， effectiveness and quality controllability of calcined Pyritum were taken as the quality profile（QTPP）， the color， hardness， metallic luster， phase composition， the contents of heavy metals and hazardous elements were taken as the critical quality attributes（CQAs）， and the calcination temperature， calcination time， paving thickness and particle size were determined as the critical process parameters（CPPs）. Differential thermal analysis， X-ray diffraction（XRD） and inductively coupled plasma mass spectrometry（ICP-MS） were used to analyze the correlation between the calcination temperature and CQAs of calcined Pyritum. Then， based on the criteria importance through intercriteria correlation（CRITIC）-entropy weight method， the optimal processing process of calcined Pyritum was optimized by orthogonal test. Powder XRD was used to analyze the phase of calcined Pyritum samples processed according to the best process， and the mean and median maps of calcined Pyritum were established by the superposition of geometric topological figures， and similarity evaluation and cluster analysis were carried out. ResultsThe results of single factor experiments showed that the physical phase of Pyritum changed from FeS₂ to Fe₇S₈ during the process of temperature increase， the color gradually deepened from dark yellow， and the contents of heavy metals and harmful elements decreased. The optimized processing process of calcined Pyritum was as follows：calcination temperature at 750 ℃， calcination time of 2.5 h， paving thickness of 3 cm， particle size of 0.8-1.2 cm， vinegar quenching 1 time［Pyritum-vinegar（10∶3）］. After calcination， the internal structure of Pyritum was honeycomb-shaped， which was conducive to the dissolution of active ingredients. XRD fingerprints of 13 batches of calcined Pyritum characterized by 10 common peaks were established. The similarities of the relative peak intensities of the XRD fingerprints of the analyzed samples were>0.96， and it could effectively distinguish the raw products and unqualified products. ConclusionTemperature is the main factor affecting the quality of calcined Pyritum. After processing， the dissolution of the effective components in Pyritum increases， and the contents of heavy metals and harmful substances decrease， reflecting the function of processing to increase efficiency and reduce toxicity. The optimized processing process is stable and feasible， and the established XRD fingerprint can be used as one of the quality control standards of calcined Pyritum.

ObjectiveTo explore the quantity-quality transfer process of medicinal materials， decoction pieces and standard decoction of Haliotidis Concha（Haliotis discus hannai） by analyzing the physical phase and compositional changes， so as to provide references for the effective control of its quality. MethodsA total of 20 batches of Haliotidis Concha（H. discus hannai） from different habitats were collected and prepared into corresponding calcined products and standard decoction， and the content of CaCO₃ of the three samples were determined and the extract yield and transfer rate of CaCO₃ were calculated. The changes in elemental composition and their relative contents were investigated by X-ray fluorescence spectrometry（XRF）， X-ray diffraction（XRD） was used to study the changes in the phase compositions of the three samples and to establish their respective XRD specific chromatogram. Fourier transform infrared spectrometry（FTIR） was used to study the changes in the chemical composition and content changes of the three samples and to establish their respective FTIR specific chromatogram， while combining hierarchical cluster analysis（HCA）， principal component analysis（PCA） and orthogonal partial least squares-discriminant analysis（OPLS-DA） to find the common and differential characteristics， in order to explore the quantity-quality transfer relationship in the preparation process of standard decoction of Haliotidis Concha（H. discus hannai）. ResultsThe CaCO₃ contents of the 20 batches of medicinal materials， decoction pieces and standard decoction of Haliotidis Concha（H. discus hannai） were 93.87%-98.95%， 96.02%-99.97% and 38.29%-51.96%， respectively， and the extract yield of standard decoction was 1.71%-2.37%， and the CaCO₃ transfer rate of decoction pieces-standard decoction was 0.68%-1.27%. XRF results showed that the elemental species and their relative contents contained in Haliotidis Concha and its calcined products had a high degree of similarity， and although there was no obvious difference in the elemental species contained in decoction pieces and standard decoction， the difference in the relative contents was obvious， which was mainly reflected in the decrease of the relative content of element Ca and the increase of the relative content of element Na. XRD results showed that Haliotidis Concha mainly contained CaCO₃ of aragonite and calcite， while calcined Haliotidis Concha only contained CaCO₃ of calcite， and standard decoction mainly contained CaCO₃ of calcite and Na₂CO₃ of natrite. FTIR results showed that there were internal vibrations of O-H， C-H， C=O， HCO₃^- and CO₃^2- groups in Haliotidis Concha， while O-H， HCO₃^- and CO₃^2- groups existed in the calcined products and standard decoction. ConclusionThe changes of Haliotidis Concha and calcined Haliotidis Concha are mainly the increase of CaCO₃ content， the transformation of CaCO₃ aragonite crystal form to calcite crystal form and the absence of organic components after calcination， and the changes of calcined products and standard decoction are mainly the decrease of CaCO₃ content and the increase of Na₂CO₃ relative content. The method established in the study is applicable to the quality control of the shellfish medicines-decoction pieces- standard decoction， which provides a new idea for the study of quality control of dispensing granules of shellfish medicines.

ObjectiveTo establish the multi-technique characteristic profiles of Alumen by X-ray diffraction（XRD）， Fourier-transform infrared spectroscopy（FTIR） and thermogravimetric-differential thermal analysis（TG-DTA）， and to explore the spectral characteristics for rapid identification of Alumen and its potential adulterant， Ammonium alum. MethodsA total of 27 batches of Alumen samples from 8 production regions were collected for preliminary identification based on visual characteristics. The PDF standard cards of XRD were used to differentiate Alumen from A. alum， and the XRD characteristic profiles of Alumen were established， and then the common peaks were screened. Based on hierarchical clustering analysis（HCA） and orthogonal partial least squares-discriminant analysis（OPLS-DA）， the characteristic information that could be used for identification of Alumen was selected with variable importance in the projection（VIP） value>1. FTIR characteristic profiles of Alumen were established， and key wavenumbers for identification were screened by HCA and OPLS-DA with VIP value>1. Meanwhile， the thermogravimetric differences between Alumen and A. alum were analyzed by TG-DTA， and the thermogravimetric traits that could be used for identification were screened. ResultsAlumen and A. alum could not be effectively distinguished by traits alone. However， by comparing the PDF standard cards of XRD， 15 batches of Alumen and 12 batches of A. alum could be distinguished. In the XRD profiles， 10 characteristic peaks were confirmed， corresponding to diffraction angles of 14.560°， 24.316°， 12.620°， 32.122°， 17.898°， 34.642°， 27.496°， 46.048°， 40.697° and 21.973°. In the FTIR profiles， 4 wavenumber ranges（399.193-403.050， 1 186.010-1 471.420， 1 801.190-2 620.790， 3 612.020-3 997.710 cm^-1） and 12 characteristic wavenumbers（1 428.994， 1 430.922， 1 432.851， 1 434.779， 1 436.708， 1 438.636， 1 440.565， 1 442.493， 1 444.422， 1 446.350， 1 448.279， 1 450.207 cm^-1） were identified. In the TG-DTA profiles， there were characteristic decomposition peaks of ammonium ion and mass reduction features near 555.34 ℃ for A. alum. These characteristics could serve as important criteria for distinguishing the authenticity of Alumen. ConclusionXRD， FTIR and TG-DTA can be used to rapidly detect Alumen and A. alum， and combined with the discriminant features selected through chemometrics， the rapid and accurate identification of Alumen and A. alum can be achieved. The research findings provide new approaches for the rapid identification of Alumen.

ObjectiveTo investigate the processing technology of calcined Haematitum based on the concept of quality by design（QbD） and to assess its health risk. MethodsTaking whole iron content， Fe²⁺ dissolution content and looseness as critical quality attributes（CQAs）， and calcination temperature， calcination time， spreading thickness and particle size as critical process parameters（CPPs） determined by the failure mode and effect analysis（FMEA）， the processing technology of calcined Haematitum was optimized by orthogonal test combined with analytic hierarchy process-criteria importance through intercriteria correlation（AHP-CRITIC） hybrid weighting method. The contents of heavy metals and harmful elements were determined by inductively coupled plasma mass spectrometry， and the health risk assessment was carried out by daily exposure（EXP）， target hazard quotient（THQ） and lifetime cancer risk（LCR）， and the theoretical value of the maximum limit was deduced. ResultsThe optimal processing technology for calcined Haematitum was calcination at 650 ℃， calcination time of 1 h， particle size of 0.2-0.5 cm， spreading thickness of 1 cm， and vinegar quenching for 1 time［Haematitum-vinegar（10：3）］. The contents of 5 heavy metals and harmful elements in 13 batches of calcined Haematitum were all decreased with reductions of up to 5-fold. The cumulative THQ of 2 batches of samples was>1， while the cumulative THQ of all batches of Haematitum was>1. The LCR of As in 1 batches of Haematitum was 1×10^-6-1×10^-4， and the LCR of the rest was<1×10^-6， and the LCRs of calcined Haematitum were all<1×10^-6， indicating that the carcinogenic risk of calcined Haematitum was low， but special attention should still be paid to Haematitum medicinal materials. Preliminary theoretical values of the maximum limits of Cu， As， Cd， Pb and Hg were formulated as 1 014， 25， 17， 27， 7 mg·kg^-1. ConclusionThe optimized processing technology of calcined Haematitum is stable and feasible， and the contents of heavy metals and harmful elements are reduced after processing. Preliminary theoretical values of the maximum limits of Cu， As， Cd， Pb and Hg are formulated to provide a scientific basis for the formulation of standards for the limits of harmful elements in Haematitum.

ObjectiveBased on the concept of quality by design（QbD）， the processing process of calcined Pyritum was optimized， and its X-ray diffraction（XRD） fingerprint was established. MethodsThe safety， effectiveness and quality controllability of calcined Pyritum were taken as the quality profile（QTPP）， the color， hardness， metallic luster， phase composition， the contents of heavy metals and hazardous elements were taken as the critical quality attributes（CQAs）， and the calcination temperature， calcination time， paving thickness and particle size were determined as the critical process parameters（CPPs）. Differential thermal analysis， X-ray diffraction（XRD） and inductively coupled plasma mass spectrometry（ICP-MS） were used to analyze the correlation between the calcination temperature and CQAs of calcined Pyritum. Then， based on the criteria importance through intercriteria correlation（CRITIC）-entropy weight method， the optimal processing process of calcined Pyritum was optimized by orthogonal test. Powder XRD was used to analyze the phase of calcined Pyritum samples processed according to the best process， and the mean and median maps of calcined Pyritum were established by the superposition of geometric topological figures， and similarity evaluation and cluster analysis were carried out. ResultsThe results of single factor experiments showed that the physical phase of Pyritum changed from FeS₂ to Fe₇S₈ during the process of temperature increase， the color gradually deepened from dark yellow， and the contents of heavy metals and harmful elements decreased. The optimized processing process of calcined Pyritum was as follows：calcination temperature at 750 ℃， calcination time of 2.5 h， paving thickness of 3 cm， particle size of 0.8-1.2 cm， vinegar quenching 1 time［Pyritum-vinegar（10∶3）］. After calcination， the internal structure of Pyritum was honeycomb-shaped， which was conducive to the dissolution of active ingredients. XRD fingerprints of 13 batches of calcined Pyritum characterized by 10 common peaks were established. The similarities of the relative peak intensities of the XRD fingerprints of the analyzed samples were>0.96， and it could effectively distinguish the raw products and unqualified products. ConclusionTemperature is the main factor affecting the quality of calcined Pyritum. After processing， the dissolution of the effective components in Pyritum increases， and the contents of heavy metals and harmful substances decrease， reflecting the function of processing to increase efficiency and reduce toxicity. The optimized processing process is stable and feasible， and the established XRD fingerprint can be used as one of the quality control standards of calcined Pyritum.

ObjectiveTo explore the quantity-quality transfer process of medicinal materials， decoction pieces and standard decoction of Haliotidis Concha（Haliotis discus hannai） by analyzing the physical phase and compositional changes， so as to provide references for the effective control of its quality. MethodsA total of 20 batches of Haliotidis Concha（H. discus hannai） from different habitats were collected and prepared into corresponding calcined products and standard decoction， and the content of CaCO₃ of the three samples were determined and the extract yield and transfer rate of CaCO₃ were calculated. The changes in elemental composition and their relative contents were investigated by X-ray fluorescence spectrometry（XRF）， X-ray diffraction（XRD） was used to study the changes in the phase compositions of the three samples and to establish their respective XRD specific chromatogram. Fourier transform infrared spectrometry（FTIR） was used to study the changes in the chemical composition and content changes of the three samples and to establish their respective FTIR specific chromatogram， while combining hierarchical cluster analysis（HCA）， principal component analysis（PCA） and orthogonal partial least squares-discriminant analysis（OPLS-DA） to find the common and differential characteristics， in order to explore the quantity-quality transfer relationship in the preparation process of standard decoction of Haliotidis Concha（H. discus hannai）. ResultsThe CaCO₃ contents of the 20 batches of medicinal materials， decoction pieces and standard decoction of Haliotidis Concha（H. discus hannai） were 93.87%-98.95%， 96.02%-99.97% and 38.29%-51.96%， respectively， and the extract yield of standard decoction was 1.71%-2.37%， and the CaCO₃ transfer rate of decoction pieces-standard decoction was 0.68%-1.27%. XRF results showed that the elemental species and their relative contents contained in Haliotidis Concha and its calcined products had a high degree of similarity， and although there was no obvious difference in the elemental species contained in decoction pieces and standard decoction， the difference in the relative contents was obvious， which was mainly reflected in the decrease of the relative content of element Ca and the increase of the relative content of element Na. XRD results showed that Haliotidis Concha mainly contained CaCO₃ of aragonite and calcite， while calcined Haliotidis Concha only contained CaCO₃ of calcite， and standard decoction mainly contained CaCO₃ of calcite and Na₂CO₃ of natrite. FTIR results showed that there were internal vibrations of O-H， C-H， C=O， HCO₃^- and CO₃^2- groups in Haliotidis Concha， while O-H， HCO₃^- and CO₃^2- groups existed in the calcined products and standard decoction. ConclusionThe changes of Haliotidis Concha and calcined Haliotidis Concha are mainly the increase of CaCO₃ content， the transformation of CaCO₃ aragonite crystal form to calcite crystal form and the absence of organic components after calcination， and the changes of calcined products and standard decoction are mainly the decrease of CaCO₃ content and the increase of Na₂CO₃ relative content. The method established in the study is applicable to the quality control of the shellfish medicines-decoction pieces- standard decoction， which provides a new idea for the study of quality control of dispensing granules of shellfish medicines.

The phase changes and quantity-quality transfer of 17 batches of Ostreae Concha(Ostrea rivularis) during the raw material-calcined decoction pieces-standard decoction process were analyzed. The content of calcium carbonate(CaCO_3), the main component, was determined by chemical titration, and the extract yield and transfer rate were calculated. The CaCO_3 content in the raw material, calcined decoction pieces, and standard decoction was 94.39%-98.80%, 95.03%-99.22%, and 84.58%-90.47%, respectively. The process of raw material to calcined decoction pieces showed the yield range of 96.85% to 98.55% and the CaCO_3 transfer rate range of 96.92% to 99.27%. The process of calcined decoction pieces to standard decoction showed the extract yield range of 2.86% to 5.48% and the CaCO_3 transfer rate range of 2.59% to 5.13%. The results of X-ray fluorescence(XRF) assay showed that the raw material, calcined decoction pieces, and standard decoction mainly contained Ca, Na, Mg, Si, Br, Cl, Al, Fe, Cr, Mn, and K. The chemometric results showed an increase in the relative content of Cr, Fe, and Si from raw material to calcined decoction pieces and an increase in the relative content of Mg, Al, Br, K, Cl, and Na from calcined decoction pieces to standard decoction. X-ray diffraction(XRD) was employed to establish XRD characteristic patterns of the raw material, calcined decoction pieces, and standard decoction. The XRD results showed that the main phase of all three was calcite, and no transformation of crystalline form or generation of new phase was observed. Fourier transform infrared spectroscopy(FTIR) was employed to establish the FTIR characteristic spectra of the raw material, calcined decoction pieces, and standard decoction. The FTIR results showed that the raw material had internal vibrations of O-H, C-H, C=O, C-O, and CO■ groups. Due to the loss of organic matter components after calcination, no information about the vibrations of C-H, C=O, and C-O groups was observed in the spectra of calcined decoction pieces and standard decoction. In summary, this study elucidated the quantity-quality transfer and phase changes in the raw material-calcined decoction pieces-standard decoction process by determining the CaCO_3 content, calculating the extract yield and transfer rate, and comparing the element changes, FTIR characteristic spectra, and XRD characteristic pattern. The results were reasonable and reliable, laying a foundation for the subsequent process research and quality control of the formula granules of calcined Ostreae Concha(O. rivularis Gould), and providing ideas and methods for the quality control of the whole process of raw material-decoction pieces-standard decoction-formula granules of Ostreae Concha and other testacean traditional Chinese medicine.
Drugs, Chinese Herbal/isolation & purification* ; Calcium Carbonate/analysis* ; Quality Control

Guided by the concept of quality by design(QbD), this study optimizes the calcination and quenching process of calcined Magnetitum and establishes the XRD characteristic spectra of calcined Magnetitum, providing a scientific basis for the formulation of quality standards. Based on the processing methods and quality requirements of Magnetitum in the Chinese Pharmacopoeia, the critical process parameters(CPPs) identified were calcination temperature, calcination time, particle size, laying thickness, and the number of vinegar quenching cycles. The critical quality attributes(CQAs) included Fe mass fraction, Fe~(2+) dissolution, and surface color. The weight coefficients were determined by combining Analytic Hierarchy Process(AHP) and the criteria importance though intercrieria correlation(CRITIC) method, and the calcination process was optimized using orthogonal experimentation. Surface color was selected as a CQA, and based on the principle of color value, the surface color of calcined Magnetitum was objectively quantified. The vinegar quenching process was then optimized to determine the best processing conditions. X-ray diffraction(XRD) was used to establish the characteristic spectra of calcined Magnetitum, and methods such as similarity evaluation, cluster analysis, and orthogonal partial least squares-discriminant analysis(OPLS-DA) were used to evaluate the quality of the spectra. The optimized calcined Magnetitum preparation process was found to be calcination at 750 ℃ for 1 h, with a laying thickness of 4 cm, a particle size of 0.4-0.8 cm, and one vinegar quenching cycle(Magnetitum-vinegar ratio 10∶3), which was stable and feasible. The XRD characteristic spectra analysis method, featuring 9 common peaks as fingerprint information, was established. The average correlation coefficient ranged from 0.839 5-0.988 1, and the average angle cosine ranged from 0.914 4 to 0.995 6, indicating good similarity. Cluster analysis results showed that Magnetitum and calcined Magnetitum could be grouped together, with similar compositions. OPLS-DA discriminant analysis identified three key characteristic peaks, with Fe_2O_3 being the distinguishing component between the two. The final optimized processing method is stable and feasible, and the XRD characteristic spectra of calcined Magnetitum was initially established, providing a reference for subsequent quality control and the formulation of quality standards for calcined Magnetitum.
X-Ray Diffraction/methods* ; Drugs, Chinese Herbal/chemistry* ; Quality Control ; Particle Size