ObjectiveTo establish the multi-technique characteristic profiles of Alumen by X-ray diffraction（XRD）， Fourier-transform infrared spectroscopy（FTIR） and thermogravimetric-differential thermal analysis（TG-DTA）， and to explore the spectral characteristics for rapid identification of Alumen and its potential adulterant， Ammonium alum. MethodsA total of 27 batches of Alumen samples from 8 production regions were collected for preliminary identification based on visual characteristics. The PDF standard cards of XRD were used to differentiate Alumen from A. alum， and the XRD characteristic profiles of Alumen were established， and then the common peaks were screened. Based on hierarchical clustering analysis（HCA） and orthogonal partial least squares-discriminant analysis（OPLS-DA）， the characteristic information that could be used for identification of Alumen was selected with variable importance in the projection（VIP） value>1. FTIR characteristic profiles of Alumen were established， and key wavenumbers for identification were screened by HCA and OPLS-DA with VIP value>1. Meanwhile， the thermogravimetric differences between Alumen and A. alum were analyzed by TG-DTA， and the thermogravimetric traits that could be used for identification were screened. ResultsAlumen and A. alum could not be effectively distinguished by traits alone. However， by comparing the PDF standard cards of XRD， 15 batches of Alumen and 12 batches of A. alum could be distinguished. In the XRD profiles， 10 characteristic peaks were confirmed， corresponding to diffraction angles of 14.560°， 24.316°， 12.620°， 32.122°， 17.898°， 34.642°， 27.496°， 46.048°， 40.697° and 21.973°. In the FTIR profiles， 4 wavenumber ranges（399.193-403.050， 1 186.010-1 471.420， 1 801.190-2 620.790， 3 612.020-3 997.710 cm^-1） and 12 characteristic wavenumbers（1 428.994， 1 430.922， 1 432.851， 1 434.779， 1 436.708， 1 438.636， 1 440.565， 1 442.493， 1 444.422， 1 446.350， 1 448.279， 1 450.207 cm^-1） were identified. In the TG-DTA profiles， there were characteristic decomposition peaks of ammonium ion and mass reduction features near 555.34 ℃ for A. alum. These characteristics could serve as important criteria for distinguishing the authenticity of Alumen. ConclusionXRD， FTIR and TG-DTA can be used to rapidly detect Alumen and A. alum， and combined with the discriminant features selected through chemometrics， the rapid and accurate identification of Alumen and A. alum can be achieved. The research findings provide new approaches for the rapid identification of Alumen.

ObjectiveTo investigate the processing technology of calcined Haematitum based on the concept of quality by design（QbD） and to assess its health risk. MethodsTaking whole iron content， Fe²⁺ dissolution content and looseness as critical quality attributes（CQAs）， and calcination temperature， calcination time， spreading thickness and particle size as critical process parameters（CPPs） determined by the failure mode and effect analysis（FMEA）， the processing technology of calcined Haematitum was optimized by orthogonal test combined with analytic hierarchy process-criteria importance through intercriteria correlation（AHP-CRITIC） hybrid weighting method. The contents of heavy metals and harmful elements were determined by inductively coupled plasma mass spectrometry， and the health risk assessment was carried out by daily exposure（EXP）， target hazard quotient（THQ） and lifetime cancer risk（LCR）， and the theoretical value of the maximum limit was deduced. ResultsThe optimal processing technology for calcined Haematitum was calcination at 650 ℃， calcination time of 1 h， particle size of 0.2-0.5 cm， spreading thickness of 1 cm， and vinegar quenching for 1 time［Haematitum-vinegar（10：3）］. The contents of 5 heavy metals and harmful elements in 13 batches of calcined Haematitum were all decreased with reductions of up to 5-fold. The cumulative THQ of 2 batches of samples was>1， while the cumulative THQ of all batches of Haematitum was>1. The LCR of As in 1 batches of Haematitum was 1×10^-6-1×10^-4， and the LCR of the rest was<1×10^-6， and the LCRs of calcined Haematitum were all<1×10^-6， indicating that the carcinogenic risk of calcined Haematitum was low， but special attention should still be paid to Haematitum medicinal materials. Preliminary theoretical values of the maximum limits of Cu， As， Cd， Pb and Hg were formulated as 1 014， 25， 17， 27， 7 mg·kg^-1. ConclusionThe optimized processing technology of calcined Haematitum is stable and feasible， and the contents of heavy metals and harmful elements are reduced after processing. Preliminary theoretical values of the maximum limits of Cu， As， Cd， Pb and Hg are formulated to provide a scientific basis for the formulation of standards for the limits of harmful elements in Haematitum.

ObjectiveBased on the concept of quality by design（QbD）， the processing process of calcined Pyritum was optimized， and its X-ray diffraction（XRD） fingerprint was established. MethodsThe safety， effectiveness and quality controllability of calcined Pyritum were taken as the quality profile（QTPP）， the color， hardness， metallic luster， phase composition， the contents of heavy metals and hazardous elements were taken as the critical quality attributes（CQAs）， and the calcination temperature， calcination time， paving thickness and particle size were determined as the critical process parameters（CPPs）. Differential thermal analysis， X-ray diffraction（XRD） and inductively coupled plasma mass spectrometry（ICP-MS） were used to analyze the correlation between the calcination temperature and CQAs of calcined Pyritum. Then， based on the criteria importance through intercriteria correlation（CRITIC）-entropy weight method， the optimal processing process of calcined Pyritum was optimized by orthogonal test. Powder XRD was used to analyze the phase of calcined Pyritum samples processed according to the best process， and the mean and median maps of calcined Pyritum were established by the superposition of geometric topological figures， and similarity evaluation and cluster analysis were carried out. ResultsThe results of single factor experiments showed that the physical phase of Pyritum changed from FeS₂ to Fe₇S₈ during the process of temperature increase， the color gradually deepened from dark yellow， and the contents of heavy metals and harmful elements decreased. The optimized processing process of calcined Pyritum was as follows：calcination temperature at 750 ℃， calcination time of 2.5 h， paving thickness of 3 cm， particle size of 0.8-1.2 cm， vinegar quenching 1 time［Pyritum-vinegar（10∶3）］. After calcination， the internal structure of Pyritum was honeycomb-shaped， which was conducive to the dissolution of active ingredients. XRD fingerprints of 13 batches of calcined Pyritum characterized by 10 common peaks were established. The similarities of the relative peak intensities of the XRD fingerprints of the analyzed samples were>0.96， and it could effectively distinguish the raw products and unqualified products. ConclusionTemperature is the main factor affecting the quality of calcined Pyritum. After processing， the dissolution of the effective components in Pyritum increases， and the contents of heavy metals and harmful substances decrease， reflecting the function of processing to increase efficiency and reduce toxicity. The optimized processing process is stable and feasible， and the established XRD fingerprint can be used as one of the quality control standards of calcined Pyritum.

ObjectiveTo explore the quantity-quality transfer process of medicinal materials， decoction pieces and standard decoction of Haliotidis Concha（Haliotis discus hannai） by analyzing the physical phase and compositional changes， so as to provide references for the effective control of its quality. MethodsA total of 20 batches of Haliotidis Concha（H. discus hannai） from different habitats were collected and prepared into corresponding calcined products and standard decoction， and the content of CaCO₃ of the three samples were determined and the extract yield and transfer rate of CaCO₃ were calculated. The changes in elemental composition and their relative contents were investigated by X-ray fluorescence spectrometry（XRF）， X-ray diffraction（XRD） was used to study the changes in the phase compositions of the three samples and to establish their respective XRD specific chromatogram. Fourier transform infrared spectrometry（FTIR） was used to study the changes in the chemical composition and content changes of the three samples and to establish their respective FTIR specific chromatogram， while combining hierarchical cluster analysis（HCA）， principal component analysis（PCA） and orthogonal partial least squares-discriminant analysis（OPLS-DA） to find the common and differential characteristics， in order to explore the quantity-quality transfer relationship in the preparation process of standard decoction of Haliotidis Concha（H. discus hannai）. ResultsThe CaCO₃ contents of the 20 batches of medicinal materials， decoction pieces and standard decoction of Haliotidis Concha（H. discus hannai） were 93.87%-98.95%， 96.02%-99.97% and 38.29%-51.96%， respectively， and the extract yield of standard decoction was 1.71%-2.37%， and the CaCO₃ transfer rate of decoction pieces-standard decoction was 0.68%-1.27%. XRF results showed that the elemental species and their relative contents contained in Haliotidis Concha and its calcined products had a high degree of similarity， and although there was no obvious difference in the elemental species contained in decoction pieces and standard decoction， the difference in the relative contents was obvious， which was mainly reflected in the decrease of the relative content of element Ca and the increase of the relative content of element Na. XRD results showed that Haliotidis Concha mainly contained CaCO₃ of aragonite and calcite， while calcined Haliotidis Concha only contained CaCO₃ of calcite， and standard decoction mainly contained CaCO₃ of calcite and Na₂CO₃ of natrite. FTIR results showed that there were internal vibrations of O-H， C-H， C=O， HCO₃^- and CO₃^2- groups in Haliotidis Concha， while O-H， HCO₃^- and CO₃^2- groups existed in the calcined products and standard decoction. ConclusionThe changes of Haliotidis Concha and calcined Haliotidis Concha are mainly the increase of CaCO₃ content， the transformation of CaCO₃ aragonite crystal form to calcite crystal form and the absence of organic components after calcination， and the changes of calcined products and standard decoction are mainly the decrease of CaCO₃ content and the increase of Na₂CO₃ relative content. The method established in the study is applicable to the quality control of the shellfish medicines-decoction pieces- standard decoction， which provides a new idea for the study of quality control of dispensing granules of shellfish medicines.

ObjectiveTo establish the multi-technique characteristic profiles of Alumen by X-ray diffraction（XRD）， Fourier-transform infrared spectroscopy（FTIR） and thermogravimetric-differential thermal analysis（TG-DTA）， and to explore the spectral characteristics for rapid identification of Alumen and its potential adulterant， Ammonium alum. MethodsA total of 27 batches of Alumen samples from 8 production regions were collected for preliminary identification based on visual characteristics. The PDF standard cards of XRD were used to differentiate Alumen from A. alum， and the XRD characteristic profiles of Alumen were established， and then the common peaks were screened. Based on hierarchical clustering analysis（HCA） and orthogonal partial least squares-discriminant analysis（OPLS-DA）， the characteristic information that could be used for identification of Alumen was selected with variable importance in the projection（VIP） value>1. FTIR characteristic profiles of Alumen were established， and key wavenumbers for identification were screened by HCA and OPLS-DA with VIP value>1. Meanwhile， the thermogravimetric differences between Alumen and A. alum were analyzed by TG-DTA， and the thermogravimetric traits that could be used for identification were screened. ResultsAlumen and A. alum could not be effectively distinguished by traits alone. However， by comparing the PDF standard cards of XRD， 15 batches of Alumen and 12 batches of A. alum could be distinguished. In the XRD profiles， 10 characteristic peaks were confirmed， corresponding to diffraction angles of 14.560°， 24.316°， 12.620°， 32.122°， 17.898°， 34.642°， 27.496°， 46.048°， 40.697° and 21.973°. In the FTIR profiles， 4 wavenumber ranges（399.193-403.050， 1 186.010-1 471.420， 1 801.190-2 620.790， 3 612.020-3 997.710 cm^-1） and 12 characteristic wavenumbers（1 428.994， 1 430.922， 1 432.851， 1 434.779， 1 436.708， 1 438.636， 1 440.565， 1 442.493， 1 444.422， 1 446.350， 1 448.279， 1 450.207 cm^-1） were identified. In the TG-DTA profiles， there were characteristic decomposition peaks of ammonium ion and mass reduction features near 555.34 ℃ for A. alum. These characteristics could serve as important criteria for distinguishing the authenticity of Alumen. ConclusionXRD， FTIR and TG-DTA can be used to rapidly detect Alumen and A. alum， and combined with the discriminant features selected through chemometrics， the rapid and accurate identification of Alumen and A. alum can be achieved. The research findings provide new approaches for the rapid identification of Alumen.

ObjectiveTo investigate the processing technology of calcined Haematitum based on the concept of quality by design（QbD） and to assess its health risk. MethodsTaking whole iron content， Fe²⁺ dissolution content and looseness as critical quality attributes（CQAs）， and calcination temperature， calcination time， spreading thickness and particle size as critical process parameters（CPPs） determined by the failure mode and effect analysis（FMEA）， the processing technology of calcined Haematitum was optimized by orthogonal test combined with analytic hierarchy process-criteria importance through intercriteria correlation（AHP-CRITIC） hybrid weighting method. The contents of heavy metals and harmful elements were determined by inductively coupled plasma mass spectrometry， and the health risk assessment was carried out by daily exposure（EXP）， target hazard quotient（THQ） and lifetime cancer risk（LCR）， and the theoretical value of the maximum limit was deduced. ResultsThe optimal processing technology for calcined Haematitum was calcination at 650 ℃， calcination time of 1 h， particle size of 0.2-0.5 cm， spreading thickness of 1 cm， and vinegar quenching for 1 time［Haematitum-vinegar（10：3）］. The contents of 5 heavy metals and harmful elements in 13 batches of calcined Haematitum were all decreased with reductions of up to 5-fold. The cumulative THQ of 2 batches of samples was>1， while the cumulative THQ of all batches of Haematitum was>1. The LCR of As in 1 batches of Haematitum was 1×10^-6-1×10^-4， and the LCR of the rest was<1×10^-6， and the LCRs of calcined Haematitum were all<1×10^-6， indicating that the carcinogenic risk of calcined Haematitum was low， but special attention should still be paid to Haematitum medicinal materials. Preliminary theoretical values of the maximum limits of Cu， As， Cd， Pb and Hg were formulated as 1 014， 25， 17， 27， 7 mg·kg^-1. ConclusionThe optimized processing technology of calcined Haematitum is stable and feasible， and the contents of heavy metals and harmful elements are reduced after processing. Preliminary theoretical values of the maximum limits of Cu， As， Cd， Pb and Hg are formulated to provide a scientific basis for the formulation of standards for the limits of harmful elements in Haematitum.

ObjectiveBased on the concept of quality by design（QbD）， the processing process of calcined Pyritum was optimized， and its X-ray diffraction（XRD） fingerprint was established. MethodsThe safety， effectiveness and quality controllability of calcined Pyritum were taken as the quality profile（QTPP）， the color， hardness， metallic luster， phase composition， the contents of heavy metals and hazardous elements were taken as the critical quality attributes（CQAs）， and the calcination temperature， calcination time， paving thickness and particle size were determined as the critical process parameters（CPPs）. Differential thermal analysis， X-ray diffraction（XRD） and inductively coupled plasma mass spectrometry（ICP-MS） were used to analyze the correlation between the calcination temperature and CQAs of calcined Pyritum. Then， based on the criteria importance through intercriteria correlation（CRITIC）-entropy weight method， the optimal processing process of calcined Pyritum was optimized by orthogonal test. Powder XRD was used to analyze the phase of calcined Pyritum samples processed according to the best process， and the mean and median maps of calcined Pyritum were established by the superposition of geometric topological figures， and similarity evaluation and cluster analysis were carried out. ResultsThe results of single factor experiments showed that the physical phase of Pyritum changed from FeS₂ to Fe₇S₈ during the process of temperature increase， the color gradually deepened from dark yellow， and the contents of heavy metals and harmful elements decreased. The optimized processing process of calcined Pyritum was as follows：calcination temperature at 750 ℃， calcination time of 2.5 h， paving thickness of 3 cm， particle size of 0.8-1.2 cm， vinegar quenching 1 time［Pyritum-vinegar（10∶3）］. After calcination， the internal structure of Pyritum was honeycomb-shaped， which was conducive to the dissolution of active ingredients. XRD fingerprints of 13 batches of calcined Pyritum characterized by 10 common peaks were established. The similarities of the relative peak intensities of the XRD fingerprints of the analyzed samples were>0.96， and it could effectively distinguish the raw products and unqualified products. ConclusionTemperature is the main factor affecting the quality of calcined Pyritum. After processing， the dissolution of the effective components in Pyritum increases， and the contents of heavy metals and harmful substances decrease， reflecting the function of processing to increase efficiency and reduce toxicity. The optimized processing process is stable and feasible， and the established XRD fingerprint can be used as one of the quality control standards of calcined Pyritum.

ObjectiveTo explore the quantity-quality transfer process of medicinal materials， decoction pieces and standard decoction of Haliotidis Concha（Haliotis discus hannai） by analyzing the physical phase and compositional changes， so as to provide references for the effective control of its quality. MethodsA total of 20 batches of Haliotidis Concha（H. discus hannai） from different habitats were collected and prepared into corresponding calcined products and standard decoction， and the content of CaCO₃ of the three samples were determined and the extract yield and transfer rate of CaCO₃ were calculated. The changes in elemental composition and their relative contents were investigated by X-ray fluorescence spectrometry（XRF）， X-ray diffraction（XRD） was used to study the changes in the phase compositions of the three samples and to establish their respective XRD specific chromatogram. Fourier transform infrared spectrometry（FTIR） was used to study the changes in the chemical composition and content changes of the three samples and to establish their respective FTIR specific chromatogram， while combining hierarchical cluster analysis（HCA）， principal component analysis（PCA） and orthogonal partial least squares-discriminant analysis（OPLS-DA） to find the common and differential characteristics， in order to explore the quantity-quality transfer relationship in the preparation process of standard decoction of Haliotidis Concha（H. discus hannai）. ResultsThe CaCO₃ contents of the 20 batches of medicinal materials， decoction pieces and standard decoction of Haliotidis Concha（H. discus hannai） were 93.87%-98.95%， 96.02%-99.97% and 38.29%-51.96%， respectively， and the extract yield of standard decoction was 1.71%-2.37%， and the CaCO₃ transfer rate of decoction pieces-standard decoction was 0.68%-1.27%. XRF results showed that the elemental species and their relative contents contained in Haliotidis Concha and its calcined products had a high degree of similarity， and although there was no obvious difference in the elemental species contained in decoction pieces and standard decoction， the difference in the relative contents was obvious， which was mainly reflected in the decrease of the relative content of element Ca and the increase of the relative content of element Na. XRD results showed that Haliotidis Concha mainly contained CaCO₃ of aragonite and calcite， while calcined Haliotidis Concha only contained CaCO₃ of calcite， and standard decoction mainly contained CaCO₃ of calcite and Na₂CO₃ of natrite. FTIR results showed that there were internal vibrations of O-H， C-H， C=O， HCO₃^- and CO₃^2- groups in Haliotidis Concha， while O-H， HCO₃^- and CO₃^2- groups existed in the calcined products and standard decoction. ConclusionThe changes of Haliotidis Concha and calcined Haliotidis Concha are mainly the increase of CaCO₃ content， the transformation of CaCO₃ aragonite crystal form to calcite crystal form and the absence of organic components after calcination， and the changes of calcined products and standard decoction are mainly the decrease of CaCO₃ content and the increase of Na₂CO₃ relative content. The method established in the study is applicable to the quality control of the shellfish medicines-decoction pieces- standard decoction， which provides a new idea for the study of quality control of dispensing granules of shellfish medicines.

OBJECTIVES: Investigating the protective effect of naringenin (NAR) on the osteogenic potential of human periodontal ligament stem cells (hPDLSCs) under oxidative stress and its related mechanisms. METHODS: The oxidative damage model of hPDLSCs was established using hydrogen peroxide (H₂O₂) andthe hPDLSCs were treated with different concentrations of NAR and 0.5 μmol/L forkhead box protein O-1 (FOXO1) inhibitor AS1842856. After that, the cell counting kit-8 (CCK8) was used to determine the optimal concentrations of H₂O₂ and NAR. The alkaline phosphatase (ALP) staining and real time fluorescent quantitative reverse transcription polymerase chain reaction (qRT-PCR) were employed to assess the expression of ALP, runt-related transcription factor 2 (RUNX2) and osteocalcin (OCN) in hPDLSCs of each group. The enzyme-linked immunosorbent assay (ELISA) and 2',7'-dichlorofluorescin diacetate (DCFH-DA) staining were utilized to evaluate the expression of reactive oxygen species (ROS), malondialdehyde (MDA) and lactate dehydrogenase (LDH) in hPDLSCs. Meanwhile, qRT-PCR and western blot were used to detect the expression levels of FOXO1 and β-catenin, both are pathway related genes and proteins. RESULTS: H₂O₂ exposure led to an increase in oxidative damage in hPDLSCs, characterized by a rise in intracellular ROS levels and increased expression of MDA and LDH (P<0.05). At the same time, the osteogenic differentiation ability of hPDLSCs decreased, as evidenced by lighter ALP staining and reduced expression levels of osteogenic differentiation-related genes ALP, RUNX2 and OCN (P<0.05). Co-treatment with NAR alleviated the oxidative damage in hPDLSCs, enhanced their antioxidant capacity, and restored their osteogenic ability. The FOXO1 inhibitor AS1842856 downregulated the expression of β-catenin (P<0.05) and significantly diminished both the antioxidant effect of NAR and its ability to restore osteogenesis (P<0.05). CONCLUSIONS NAR can enhance the antioxidant capacity of hPDLSCs by activating the FOXO1/β-catenin signaling pathway within hPDLSCs, thereby mitigating oxidative stress damage and alleviating the loss of osteogenic capacity.
Humans ; Oxidative Stress/drug effects* ; Periodontal Ligament/cytology* ; Hydrogen Peroxide ; Forkhead Box Protein O1/metabolism* ; Stem Cells/cytology* ; Flavanones/pharmacology* ; beta Catenin/metabolism* ; Osteogenesis/drug effects* ; Signal Transduction ; Core Binding Factor Alpha 1 Subunit/metabolism* ; Alkaline Phosphatase/metabolism* ; Osteocalcin/metabolism* ; Cells, Cultured ; Cell Differentiation/drug effects*

ObjectiveTo observe the clinical effectiveness and safety of Xuandi Ziyin Mixture （玄地滋阴合剂） for central precocious puberty （CPP） in girls with syndrome of yin deficiency and fire exuberance， and to analyse the effect of body mass index （BMI） on the effectiveness. MethodsA total of 236 girls with CPP of yin deficiency and fire exuberance syndrome were included， and all of them were given Xuandi Ziyin Mixture， 30 ml each time， twice a day， for a total treatment period of 6 months. Before and after treatment， children's weight， height and bone age were measured， BMI and BMI Z-score （BMI Z） and the difference between bone age and actual age were calculated； ultrasound was used to detect uterine and ovarian sizes， and to calculate uterine volume （V_uterus）， bilateral ovarian volume （V_{left ovary}， V_{right ovary}）， and bilateral maximal follicle diameters （r_{left follicle} and r_{right follicle}）； and serum sex hormones were measured， including follicle-stimulating hormone （FSH）， luteinising hormone （LH）， prolactin （PRL）， estradiol （E₂）， and testosterone （T）， and were scored for traditional Chinese medicine （TCM） syndrome. Multiple linear regression was used to analyse the influence factors of the difference between bone age and actual age， and changes in uterine volume. The children were divided into the normal weight group and the overweight/obesity group according to baseline BMI， and the bone age， the difference between bone age and actual age， V_uterus and BMI Z scores before and after treatment were compared between the two groups. ResultsFinally， 199 children entered the statistical analysis. Compared with pre-treatment， the bone age， BMI and BMI Z scores of the children increased after treatment， and the difference between bone age and actual age， TCM syndrome scores， V_uterus， V_{left ovary}， V_{right ovary}， r_{left follicle} and r_{right follicle} decreased； and the levels of serum FSH， LH， E₂， and T significantly decreased （P＜0.05 or P＜0.01）. The difference between bone age and actual age was negatively correlated with LH and V_uterus （P＜0.05）， and changes in uterine volume were positively correlated with LH （P＜0.01）. Comparing between the groups before and after treatment， the bone age， difference between bone age and actual age， and BMI Z scores of children in the normal weight group （100 cases） were significantly smaller than those in the overweight/obesity group （99 cases） （P＜0.01）. Compared with pre-treatment， the bone age of the children in both groups increased， but the difference between bone age and actual age and V_uterus were significantly smaller （P＜0.01）. Further comparison of Δ bone age and actual age difference and ΔV_uterus （Δ = post-treatment value - pre-treatment value） between the two groups showed no statistically significant difference （P＞0.05）. ConclusionsXuandi Ziyin Mixture can reduce bone age， sex hormone level， ovary and uterus size， and improve clinical symptoms in girls with yin deficiency and fire exuberance syndrome of CPP. It is also effective in overweight/obese children， and the inhibitory effect on bone age in girls with CPP is not affected by BMI， with good safety.