OBJECTIVES: Through the investigation of the microhardness and microstructure of permanent tooth enamel at various eruption stages during childhood, this research offers references for the early prevention of childhood dental caries. METHODS: Forty-five premolars extracted due to orthodontic reasons were collected and screened. These premolars were divided into three experimental groups according to the time since eruption: Group A (erupted for 0-1 year), Group B (erupted for 1-3 years), and Group C (erupted for 3-5 years). Additionally, the third molars that were extracted due to impaction and had not erupted were selected as the control group, with 15 teeth in each group. Samples were prepared, and the surface microhardness, microstructure, and elemental composition of the enamel were measured using Vickers microhardness tester, scanning electron microscope, and electron probe, respectively. RESULTS: Compared with that in the control group, the microhardness of enamel in groups A, B, and C increased with prolonged eruption time, the surface porosity structure decreased considerably, the contents of Na and Mg on the surface decreased, and that of F increased (P<0.05). CONCLUSIONS The microhardness and microstructure of enamel in permanent teeth at different stages vary. Permanent teeth are at a substantially higher risk of caries within one year after eruption, and early prevention should be emphasized.
Dental Enamel/ultrastructure* ; Humans ; Hardness ; Dental Caries/prevention & control* ; Microscopy, Electron, Scanning ; Tooth Eruption ; Bicuspid/chemistry* ; Dentition, Permanent ; Child ; Child, Preschool

Objective: To investigate the effect of permeable resin on the surface structure, microhardness and color of tooth enamel after bleaching. Methods: Premolars extracted for orthodontic needs were selected (provided by the Department of Oral and Maxillofacial surgery of the first affiliated Hospital of Zhengzhou University) and randomly divided into A, B and C 3 groups. Each group was randomly divided into control subgroup, resin subgroup, bleaching subgroup and combined subgroup. Samples in the control subgroup did not receive any treatment. Those in the bleaching subgroup and combined subgroup were treated with cold light whitening. Those in the resin group and combined group were treated with permeable resin. Samples in the group A were observed by scanning electron microscope immediately after treatment and 2 weeks after treatment, and the microhardness of samples in the group B was measured before treatment, immediately after treatment and 2 weeks after treatment (the sample size of each time point was 8 in each subgroup). In group C, chromaticity was measured and chromatic aberration (ΔE value) was calculated before treatment, immediately after treatment and 1 and 2 weeks after treatment (10 samples in each subgroup). Results: Scanning electron microscope showed that the enamel surface of the resin subgroup and the combined group was smooth immediately after treatment, which was basically the same as that of the control subgroup, but covered with resin, and microporous defects and mineral deposits could be seen on the surface of the bleaching subgroup. Two weeks after treatment, the enamel surface of each subgroup was smooth, there was no obvious difference. Immediately after treatment, the microhardness of the control subgroup, resin subgroup, bleaching subgroup and combined subgroup were (354±33), (364±21), (411±30) and (350±17) HV, respectively (F=9.39,P<0.05). The microhardness of the bleaching subgroup was significantly higher than that of the other subgroups (P<0.05). There was no significant difference in microhardness among the four subgroups before treatment and 2 weeks after treatment (F=0.34, 2.75, P>0.05). Immediately after treatment, the ΔE values of the control subgroup, resin subgroup, bleaching subgroup and combined subgroup were 0.00±0.00, 2.29±1.86, 7.20±1.94 and 8.00±0.88, respectively (F=74.21,P<0.05); except that there was no significant difference between bleaching subgroup and combined subgroup (P>0.05), there were significant differences among the other subgroups (P<0.05). There was no significant difference in ΔE value among control subgroup, resin subgroup and bleaching subgroup at each time point (F=1.66, 0.30, 0.96, P>0.05). The difference in the combined subgroup immediately after treatment was significantly higher than that at 1 and 2 weeks after treatment (t=4.73, 4.23,P<0.05), but there was no significant difference between 1 and 2 weeks after treatment (t=0.75, P>0.05), and the color tended to be stable. Conclusions: When whitening healthy enamel, simple cold light whitening or cold light whitening combined with permeation resin can achieve whitening effect.
Color ; Dental Enamel ; Hardness ; Humans ; Hydrogen Peroxide/pharmacology* ; Tooth Bleaching/adverse effects* ; Tooth Bleaching Agents/pharmacology*

hardness ratio. For baseline clinical factors, we examined the maternal body mass index, blood pressure, heart rate, uterine artery Doppler indices, and fetal presentation.RESULTS: We established a specific protocol for the measurement of cervical elastography using the E cervix program. For all elastographic parameters, the intra-observer intraclass correlation coefficient (ICC) ranged from 0.633 to 0.723 for single measures and from 0.838 to 0.887 for average measures, and the inter-observer ICC ranged from 0.814 to 0.977 for single measures and from 0.901 to 0.988 for average measures. Regression analysis showed that the measurement of the elastographic parameter was not affected by baseline clinical factors.CONCLUSION: We present a standardized protocol for the measurement of cervical elastography using intrinsic compression. According to this protocol, reproducibility was acceptable and the measurement of elastographic parameters was not affected by the baseline clinical factors studied.]]>
Blood Pressure ; Body Mass Index ; Cervix Uteri ; Elasticity ; Elasticity Imaging Techniques ; Female ; Hardness ; Heart Rate ; Humans ; Jupiter ; Labor Presentation ; Pregnancy ; Pregnant Women ; Premature Birth ; Reproducibility of Results ; Uterine Artery

OBJECTIVES: The aim of this in vitro study was to evaluate the microhardness and surface roughness of composite resins before and after tooth bleaching procedures.MATERIALS AND METHODS: Sixty specimens were prepared of each composite resin (Filtek Supreme XT and Opallis), and BisCover LV surface sealant was applied to half of the specimens. Thirty enamel samples were obtained from the buccal and lingual surfaces of human molars for use as the control group. The surface roughness and microhardness were measured before and after bleaching procedures with 35% hydrogen peroxide or 16% carbamide (n = 10). Data were analyzed using 1-way analysis of variance and the Fisher test (α = 0.05).RESULTS: Neither hydrogen peroxide nor carbamide peroxide treatment significantly altered the hardness of the composite resins, regardless of surface sealant application; however, both treatments significantly decreased the hardness of the tooth samples (p < 0.05). The bleaching did not cause any change in surface roughness, with the exception of the unsealed Opallis composite resin and dental enamel, both of which displayed an increase in surface roughness after bleaching with carbamide peroxide (p < 0.05).CONCLUSIONS: The microhardness and surface roughness of enamel and Opallis composite resin were influenced by bleaching procedures.
Composite Resins ; Dental Enamel ; Hardness ; Humans ; Hydrogen Peroxide ; In Vitro Techniques ; Molar ; Tooth ; Tooth Bleaching ; Urea

BACKGROUND/AIMS: Endoscopic ultrasound (EUS) has a limited ability to determine the nature of solid pancreatic lesions (SPLs). Most recent ultrasound processors are provided with elastography software, which allows quantification of the tissue hardness. The aim of this study is to evaluate the effectiveness of the elasticity score (ES) and strain ratio (SR) in the differentiation of benign pancreatic lesions from malignant pancreatic lesions. METHODS: The study had a retrospective design; it included 97 patients with SPLs and 19 patients with inflammatory lesions. The ES and SR were determined during the examination; finally, EUS-guided fine needle aspiration was performed. RESULTS: In this 2-year study, 116 patients were enrolled (97 with malignant lesions and 19 with benign lesions). There were 69 men and 47 women. Their median age was 55.9 years. A cut-off point was detected at SR of 7.75 with a specificity of 99.9%, sensitivity of 90.7%, positive predictive value (PPV) of 99.9%, negative predictive value (NPV) of 67.9%, and accuracy of 92.2%. After adding the ES to the SR, the cut-off point at 7.75 resulted in a specificity of 94.6%, sensitivity of 99%, PPV of 98%, NPV of 98.5%, and accuracy of 97%. CONCLUSIONS: The use of the ES combined with the SR increases the accuracy of differentiation between benign and malignant SPLs and is an effective method for the evaluation of pancreatic masses.
Biopsy, Fine-Needle ; Elasticity ; Elasticity Imaging Techniques ; Female ; Hardness ; Humans ; Male ; Methods ; Pancreas ; Retrospective Studies ; Sensitivity and Specificity ; Ultrasonography

BACKGROUND: In this study, four types of effervescent vitamins marketed in Korea were analyzed for their acidity and vitamin content. For this purpose, bovine teeth were immersed in vitamin, and surface microhardness and appearance were measured before and after immersion to evaluate tooth demineralization and erosion.METHODS: Bovine permanent incisors with sound surface enamel were cut to 5×5 mm size, embedded in acrylic resin, and polished using a polishing machine with Sic-paper. The prepared samples were analyzed for pH, vitamin content, and surface hardness before and after immersion using a surface microhardness meter. Demineralization of surface dental enamel was observed using a scanning electron microscope.RESULTS: The average pH of the four effervescent vitamins was less than 5.5; the pH of the positive control Oronamin C was the lowest at 2.76, while that of the negative control Samdasoo was the highest at 6.86. The vitamin content was highest in Berocca and lowest in the DM company Multivitamin. On surface microhardness analysis, surface hardness values of all enamel samples were found to be decreased significantly after 1 and 10 minutes of immersion (p<0.05). After 10 minutes of immersion, there was a significant difference in the decrease in hardness between the experimental groups (p<0.05). Scanning electron microscopy observation showed that dental enamel demineralization after 10 minutes of immersion was the most severe in Oronamin C except for Samdasoo, followed by DM company Multivitamin and VitaHEIM. Immersion in BeroNew and Berocca resulted in similar effects.CONCLUSION: There is a risk of tooth erosion due to decreased tooth surface microhardness when using the four types of effervescent vitamins and vitamin carbonated beverages with pH below 5.5. Therefore, high pH vitamin supplements are recommended to prevent tooth erosion.
Carbonated Beverages ; Dental Enamel ; Hardness ; Hydrogen-Ion Concentration ; Immersion ; Incisor ; Korea ; Microscopy, Electron, Scanning ; Tablets ; Tooth ; Tooth Demineralization ; Tooth Erosion ; Vitamins

OBJECTIVES: We investigated the effects of commercial plum beverage on the dentin surface that could be exposed to caries, gliopathy, and abrasion to investigate the inhibitory effects of dentin corrosion.METHODS: The experimental beverages were Jeju Samdasoo (Group 1, negative control), Coca-Cola (Group 2, positive control), Chorok Maesil (Group 3), and Chorok Maesil with 3% calcium lactate added (Group 4). The specimens were prepared and divided into 4 groups of 12 each. The pH of the experimental beverages was measured using a pH meter, and specimen surface hardness was assessed according to the Vickers hardness number (VHN). The specimens were immersed in the experimental beverage for 1, 3, 5, 10, and 15 minutes. Then, we obtained the average VHN by measuring surface microhardness. Measures of surface microhardness were compared using the paired t-test before and after 15 minutes of immersion in each of the four beverages. Between-group differences in surface microhardness were compared using one-way analysis of variance and the Tukey test after the analysis.RESULTS: After 15 minutes of immersion in the experimental beverages, there was no significant difference in surface microhardness in group 1 (P>0.05). There were significant differences in groups 2, 3, and 4 (P < 0.05). The difference in surface microhardness before and after immersion for 15 minutes was highest in group 3 (−18.1±2.55), followed by group 2 (−13.0±3.53) and group 4 (−7.79±4.47). In group 1, the difference was −1.52±4.30. Moreover, there was a significant difference in each group (P < 0.05). After 10 minutes of immersion, surface microhardness tended to rapidly decrease.CONCLUSIONS: Patients who regularly ingest a commercially available plum drink with low pH should be provided dietary guidance on the risk of dental erosion. Calcium additives should be considered when producing plum beverage products.
Beverages ; Calcium ; Corrosion ; Dentin ; Hardness ; Humans ; Hydrogen-Ion Concentration ; Immersion ; Lactic Acid ; Prunus domestica ; Tooth

The purpose of this study was to investigate the effect of adding a protective coating on the microhardness and wear resistance of glass ionomer cements (GICs).Specimens were prepared from GIC and resin-modified GIC (RMGI), and divided into 3 groups based on surface protection: (1) no coating (NC), (2) Equia coat coating (EC), and (3) un-filled adhesive coating (AD). All specimens were then placed in distilled water for 24 h. Surface hardness (n = 10) was evaluated on a Vickers hardness testing machine. Wear resistance (n = 10) was evaluated after subjecting the specimen to thermocycling for 10,000 cycles using a chewing simulator. Data were analyzed using a one-way ANOVA and the Kruskal-Wallis test.Surface hardness was highest in the NC groups, followed by the EC and AD groups. The wear depth of GI + NC was significantly higher than that of all RMGI groups. EC did not significantly lower the wear depth compared to AD.Based on these results, it was concluded that although EC does not increase the surface microhardness of GIC, it can increase the wear resistance.
Adhesives ; Glass Ionomer Cements ; Hardness ; Hardness Tests ; Mastication ; Water

The purpose of this study was to evaluate polymerization of TheraCal LC, one of the tricalcium silicate cements. To measure the Vickers hardness number (VHN), the specimens were cured at different light curing time and distance.As a result, the VHN of the upper surface was significantly higher than the lower surface's in all groups (p < 0.05). The VHN of the lower surface was increased significantly with the increase of the light curing time in all distance (p < 0.05). When the distance was more than 4.0 mm at all light curing time, the VHN of lower surface was significantly decreased (p < 0.05). When the specimen was light cured for 20 seconds, the VHN of the lower surface did not exceed 2, which corresponds to 10% of the upper surface's.These results suggested that the 20 second light curing time was not sufficient to polymerize the lower surface under specific conditions and that light-curing time should be increased.
Hardness ; Polymerization ; Polymers ; Silicates

BACKGROUND: Erosion is a gradual process that occurs fairly quickly, and the full extent of the erosive effects of acidic beverages is not yet clear. The present study aimed to determine the differences in the erosive potentials among four naturally acidic fruit nectars within the same range of titratable acidity and to determine the influence of the components of organic acids on tooth erosion. METHODS: Diluted fruit nectars (mandarin 1:1.1, orange 1:1.7, lemon 1:15, grapefruit 1:20) with the same range of titratable acidity (7.9 ml) and their corresponding organic acids (0.05%, 0.1%, 0.3%, and 0.5% citric acid, malic acid, and a citric and malic acid mixture [pH 2.8], respectively) were used. Specimens were placed in conical tubes with 50 ml of each of the test solutions for 1 hour. A microhardness test and scanning electron microscopy were used to measure enamel erosion. Acid separation was carried out using high-performance liquid chromatography to analyze the composition of each test solution. RESULTS: Similar decreases in the Vickers hardness number (VHN) were observed among the groups treated with the following diluted fruit nectars: diluted mandarin nectar (75.9 ΔVHN), diluted lemon nectar (89.1 ΔVHN), diluted grapefruit nectar (91.7 ΔVHN), and diluted orange nectar (92.5 ΔVHN). No statistically significant differences were found in the enamel surface hardness after erosion (p>0.05). Citric and malic acids were the major organic acids in the test fruits. The lemon and orange groups had the highest malic acid concentrations, and the mandarin group had the lowest malic acid concentration. CONCLUSION: The titratable acidity and the citric and malic acid contents of the fruits could be crucial factors responsible for enamel erosion. Therefore, fruit-based drinks should be regarded as potentially erosive.
Beverages ; Chromatography, Liquid ; Citric Acid ; Citrus paradisi ; Citrus sinensis ; Dental Enamel ; Fruit ; Hardness ; In Vitro Techniques ; Microscopy ; Microscopy, Electron, Scanning ; Plant Nectar ; Tooth Erosion