OBJECTIVE: To compare the cyclic fatigue resistance of nickel-titanium files made by 3 new heat treatment in simulated S-shaped root canals at different temperatures. METHODS: Gold heat-treated nickel-titanium files TruNatomy (25 mm, tip size 26#/0.04) and ProTaper Gold (25 mm, tip size 25#/0.08) were selected as the experimental group, M wire technique nickel-titanium file ProTaper Next (25 mm, tip size 25#/0.06) was selected as the control group. It was speculated that the Gold technique used in TruNatomy nickel-titanium file was R phase separation technique, which included a complete intermediate R-phase, increasing its flexibility. ProTaper Gold was a CM wire nickel-titanium file and the increased phase transformation temperature by heat treatment introduced martensite at room temperature, while it underwent gold heat treatment on the surface, generating an intermediate R phase during phase transformation, providing hyperelastic. ProTaper Next used M wire technique, M wire included austenite at room temperature, where heat mechanical processing introduced hardened martensite, which was incapable of participating phase transformation. Because of the lower elastic modulus of hardened martensite than austenite, the flexibility of the file was increased. Twenty instruments of each nickel-titanium file were submitted to the cyclic fatigue test by using a simulated canal with double curvatures at room tem-perature (24 ℃) and 65 ℃, 10 instruments of each nickel-titanium file were selected at each temperature (n=10). At the same temperature, the number of cyclic fatigue (NCF) and fragment length were analyzed by using One-Way analysis of variance at a significance level of P < 0.05. NCF and fragment length of the same nickel-titanium file at room temperature and 65 ℃ were compared by paired sample t test and the significance level was α=0.05. Fractured surfaces were analyzed by using scanning electron microscope. RESULTS: In double-curved canals, all the failure of the files due to cyclic fatigue was first seen in the apical curvature before the coronal curvature. At room temperature, in the apical curvature, NCF of TruNatomy was 344.4±96.6, ProTaper Gold was 175.0±56.1, ProTaper Next was 133.3±39.7, NCF of Tru Natomy was the highest (P < 0.05). In the coronal curvature, NCF of TruNatomy was 618.3± 75.3, ProTaper Gold was 327.5±111.8, ProTaper Next was 376.6±67.9, NCF of TruNatomy was also the highest (P < 0.05). There was no significant difference among the apical and coronal fragment length of the 3 nickel-titanium files (P>0.05). At 65 ℃, in the apical curvature, NCF of TruNatomy was 289.6±65.8, ProTaper Gold was 187.5±75.4, ProTaper Next was 103.0±38.5, NCF of TruNatomy was the highest (P < 0.05). In the coronal curvature, NCF of TruNatomy was 454.2±45.4, ProTaper Gold was 268.3±31.4, ProTaper Next was 283.8±31.7, NCF of TruNatomy was also the highest (P < 0.05). The apical fragment length of ProTaper Next was the highest (P < 0.05), and there was no significant difference among coronal fragment length of the 3 nickel-titanium files (P>0.05). Compared with room temperature, at 65 ℃, in the coronal curvature, NCF of TruNatomy decreased significantly (P < 0.05). The fractured surfaces of the three nickel-titanium files demonstrated typical cyclic fatigue. CONCLUSION Gold heat-treated nickel-titanium file had better cyclic fatigue resistance than M wire nickel-titanium file in S-shaped root canals.
Nickel/chemistry* ; Titanium/chemistry* ; Hot Temperature ; Root Canal Preparation/methods* ; Humans ; Materials Testing ; Gold/chemistry* ; Dental Alloys/chemistry* ; Stress, Mechanical

Znic (Zn) alloys with good cytocompatibility and suitable degradation rate have been a kind of biodegradable metal with great potential for clinical applications. This paper summarizes the biological role of degradable Zn alloy as bone implant materials, discusses the mechanical properties of different Zn alloys and their advantages and disadvantages as bone implant materials, and analyzes the influence of different processing strategies (such as alloying and additive manufacturing) on the mechanical properties of Zn alloys. This paper provides systematic design approaches for biodegradable Zn alloys as bone implant materials in terms of the material selection, product processing, structural topology optimization, and assesses their application prospects with a view to better serve the clinic.
Orthopedics ; Zinc ; Alloys ; Dental Materials ; Prostheses and Implants

OBJECTIVE: To compare the retentions of different designs of cobalt-chromium (Co-Cr), pure titanium (CP Ti), and titanium alloy (Ti-6Al-4V) removable partial denture (RPD) circumferential clasps manufactured by selective laser melting (SLM) and to analyze the stress distribution of these clasps during the removal from abutment teeth. METHODS: Clasps with clasp arm size A (1.9 mm width/1.1 mm thickness at the body and 0.8-taper) or B (1.2 times A) and 0.25 mm or 0.50 mm undercut engagement were modeled on a prepared first premolar die, named as designs A1, A2, A3, and A4, respectively. The density and elastic modulus of SLM-built Co-Cr, CP Ti, and Ti-6Al-4V were measured and given to different groups of clasps. The density, elastic modulus, and Poisson ' s ratio of enamel were given to the die. The control group was the cast Co-Cr clasp with design A1, to which the density and elastic modulus of cast Co-Cr alloy were given. The Poisson's ratio of all metals was 0.33. The initial 5 N dislodging force was applied, and the maximum displacement of the clasp along the insertion path was computed. The load was reapplied with an increment of 5 N than in the last simulation until the clasp was completely dislodged. The retentive force range of different groups of clasps was obtained. The retentive forces of the SLM-built Co-Cr, CP Ti, and Ti-6Al-4V clasps with equivalent computed retentive force range to the control group were validated through the insertion/removal experiment. The von Mises stress distributions of these three groups of SLM-built clasps under 15 N loads were analyzed. RESULTS: SLM-built Co-Cr, CP Ti, and Ti-6Al-4V clasps with designs B1 or B2, and Co-Cr clasps with design A2 had higher retentive forces than those of the control group. SLM-built CP Ti and Ti-6Al-4V clasps with design A1 had lower retentive forces than those of the control group. SLM-built Co-Cr clasp with design A1 and SLM-built CP Ti and Ti-6Al-4V clasps with design A2 had equivalent retentive forces to those of the control group. The insertion/removal experiment showed that the measured retentive forces of these three groups of SLM-built clasps were (21.57±5.41) N, (19.75±4.47) N, and (19.32±2.04) N, respectively. No statistically significant measured retentive force difference was found among these three groups of SLM-built clasps (P>0.05). The maximum von Mises stress of these three groups of SLM-built clasps exceeded their responding yield strength except for the Ti-6Al-4V one. CONCLUSION SLM-built Co-Cr circumferential clasps had higher retention than CP Ti and Ti-6Al-4V ones with the same clasp arm size and undercut engagement. The retention of SLM-built circumferential clasps could be adjusted by changing the undercut engagement and clasp arm size. If SLM-built circumferential clasps are used in clinical practice, the Ti-6Al-4V clasp with clasp arm size A and 0.50 mm undercut engagement is recommended considering the long-term use of RPD in the patient's mouth.
Chromium Alloys ; Dental Clasps ; Denture Retention ; Denture, Partial, Removable ; Finite Element Analysis ; Humans ; Lasers ; Titanium

Various engine-driven NiTi endodontic files have been indispensable and efficient tools in cleaning and shaping of root canals for practitioners. In this review, we introduce the relative terms and conceptions of NiTi file, including crystal phase composition, the design of the cutting part, types of separation. This review also analysis the main improvement and evolution of different generations of engine-driven nickel-titanium instruments in the past 20 years in the geometric design, manufacturing surface treatment such as electropolishing, thermal treatment, metallurgy. And the variety of motion modes of NiTi files to improve resistance to torsional failure were also discussed. Continuous advancements by the designers, provide better balance between shaping efficiency and resistance to of NiTi systems. In clinical practice an appropriate system should be selected based on the anatomy of the root canal, instrument characteristics, and operators' experience.
Dental Alloys/chemistry* ; Dental Instruments ; Equipment Design ; Nickel/chemistry* ; Root Canal Preparation ; Titanium/chemistry*

OBJECTIVES: At present, removable partial denture is still one of the main restoration methods for dentition defects. However, the trend for digital partial denture is becoming more and more obvious in the field of oral repair. However, there are relatively few studies on digital removable partial denture. The aim of this study is to investigate the effects of 3 processing technologies (precision casting, digital cutting, and 3D printing) on the fitness for the clasps of cobalt chromium alloy and pure titanium removable partial denture, and to provide a theoretical basis for the clinical application of digital removable partial denture. METHODS: Clasps of Co-Cr alloy and pure titanium were produced by 3 different processing technologies (precision casting, digital cutting, and 3D printing). There are 6 groups, including a casting pure titanium group, a casting cobalt chromium group, a cutting pure titanium group, a cutting cobalt chromium group, a printing pure titanium group, and a printing cobalt chromium group ( RESULTS: There was no statistical difference in fitness between the casting pure titanium group and the casting cobalt chromium group ( CONCLUSIONS The cobalt chromium alloy and pure titanium clasps made by precision casting, digital cutting, and 3D printing have good fitness. Under the same process, there is no significant difference between cobalt chromium alloy and pure titanium clasps. The 3D printing pure titanium clasps have better fitness than casting pure titanium and cutting pure titanium clasps, which meet the needs of clinical application.
Chromium Alloys ; Cobalt ; Denture, Partial, Removable ; Titanium

PURPOSE: The aim of this study is to evaluate the effectiveness of MnO₂-diatom microbubbler (DM) on the surface of prosthetic materials as a mouthwash by comparing the biofilm removal effect with those previously used as a mouthwash in dental clinic.MATERIALS AND METHODS: DM was fabricated by doping manganese dioxide nanosheets to the diatom cylinder surface. Scanning electron microscopy (SEM) was used to observe the morphology of DM and to analyze the composition of doped MnO₂. Stereomicroscope was used to observe the reaction of DM in 3% hydrogen peroxide. Non-precious metal alloys, zirconia and resin specimens were prepared to evaluate the effect of biofilm removal on the surface of prosthetic materials. And then Streptococcus mutans and Porphyromonas gingivalis biofilms were formed on the specimens. When 3% hydrogen peroxide solution and DM were treated on the biofilms, the decontamination effect was compared with chlorhexidine gluconate and 3% hydrogen peroxide solution by crystal violet staining.RESULTS: Manganese dioxide was found on the surface of the diatom cylinder, and it was found to produce bubble of oxygen gas when added to 3% hydrogen peroxide. For all materials used in the experiments, biofilms of the DM-treated groups got effectively removed compared to the groups used with chlorhexidine gluconate or 3% hydrogen peroxide alone.CONCLUSION: MnO₂-diatom microbubbler can remove bacterial membranes on the surface of prosthetic materials more effectively than conventional mouthwashes.
Alloys ; Biofilms ; Chlorhexidine ; Decontamination ; Dental Clinics ; Dental Plaque ; Diatoms ; Gentian Violet ; Hydrogen Peroxide ; In Vitro Techniques ; Manganese ; Membranes ; Microscopy, Electron, Scanning ; Mouthwashes ; Oral Hygiene ; Oxygen ; Porphyromonas gingivalis ; Streptococcus mutans

PURPOSE: The present study was designed to examine the clinical fit of fixed dental prosthesis fabricated by the milling-sintering method using a presintered cobalt-chromium alloy. MATERIALS AND METHODS: Two single metal-ceramic crowns were fabricated via milling-sintering method and casting method in each of the twelve consecutive patients who required an implant-supported fixed prosthesis. In the milling-sintering method, the prosthetic coping was designed in computer software, and the design was converted to a non-precious alloy coping using milling and post-sintering process. In the casting method, the conventional manual fabrication process was applied. The absolute marginal discrepancy of the prostheses was evaluated intraorally using the triple-scan technique. Statistical analysis was conducted using Mann-Whitney U test (α=.05). RESULTS: Eight patients (66.7%) showed a lower marginal discrepancy of the prostheses made using the milling-sintering method than that of the prosthesis made by the casting method. Statistically, the misfit of the prosthesis fabricated using the milling-sintering method was not significantly different from that fabricated using the casting method (P=.782). There was no tendency between the amount of marginal discrepancy and the measurement point. CONCLUSION: The overall marginal fit of prosthesis fabricated by milling-sintering using a presintered alloy was comparable to that of the prosthesis fabricated by the conventional casting method in clinical use.
Alloys ; Clinical Study ; Crowns ; Dental Prosthesis ; Humans ; Methods ; Prostheses and Implants

OBJECTIVE: To assess the effects of two surface treatments (sandblasting, SB; microarc-oxidation, MAO) and resin luting on shear bond strength and durability of titanium alloy and composite-resin. METHODS: Eighty cylindrical titanium alloy specimens with a diameter of 10 mm and a height of 8 mm were fabricated by CAD/CAM technique. It was divided into two groups according to the surface treatment methods: sandblasting with Al2O3 particles on the surface of SB specimens; porous ceramic film structure could be formed on the surface of MAO specimens after surface treatment. Each group was classified into SB-resin luting-N group (not used), SB-resin luting-Y group (used), MAO-resin luting-N group (not used), MAO-resin luting-Y group (used) depending on whether or not resin luting was applied. Each specimen was bonded and cured with the Cemerage resin, and the shear bond strength after 0 and 5 000 thermocycling was tested. The results were statistically analyzed. The surface morphology of titanium alloy specimens before and after the shear bond strength test was observed by scanning electron microscopy (SEM). RESULTS: The shear bond strength between titanium alloy and composite-resin was the highest in the SB combined with resin luting group after 0 thermocycling (16.2±1.8) MPa; was the lowest in MAO group after 5 000 thermocycling (8.9±1.5) MPa. The shear bond strength of SB and MAO surface treatment methods combined without resin luting group after 5 000 thermocycling were (10.7±2.2) MPa and (8.9±1.5) MPa, which were statistically lower than those in the thermocycling 0 (P=0.000 and P=0.001). The shear bond strength of SB and MAO surface treatment methods combined with resin luting group after 5 000 thermocycling were (15.5±2.1) MPa and (11.7±1.3) MPa, respectively, which were lower than those in the thermocycling 0 group, but there was no statistical significance (P=0.087 and P=0.234). CONCLUSION Both the surface treatment methods of SB and MAO combined with resin luting can improve the shear bond strength and durability of titanium alloy and composite-resin. The SB combined with resin luting is more significant. At present, the effect of SB is better than that of MAO due to the limitation of technical parameters of micro-arc oxidation.
Alloys ; Composite Resins ; Dental Bonding ; Materials Testing ; Resin Cements ; Shear Strength ; Surface Properties ; Titanium

OBJECTIVE: To construct a model for a controlled memory (CM) nickel-titanium (NiTi) file and another M-wire NiTi file with the same geometry by using finite element analysis. To evaluate the flexibility of a CM NiTi file by using three dimensional finite element method and to compare its mechanical responses with that M-wire NiTi. METHODS: Based on the reverse engineering, the 21 mm long, 25#/08 taper Hyflex NT NiTi file and Hyflex CM NiTi file were fixed by the cantilever bending model at a distance of 9.5 mm from the tip of the file. The mechanical tester's indenter was loaded/unloaded at a distance of 3 mm from the tip of the file. The maximum displacement was 3 mm, the load displacement curve was obtained. Subsequently, by using a micro-CT to scan (layer spacing of 8 μm) NiTi files, and ABAQUS (6.10) was introduced to construct a geometric model. Hyflex NT was considered as a shapememory alloy constitutive model, Hyflex CM was considered as a power-hardening plastic constitutive model, respectively. Comparing the load-displacement curve of cantilever bending in the three-dimensional finite element model with the load-displacement curve in the experiment. RESULTS: Two tetrahedral element models were constructed, the total number of nodes was 99 353 and the total number of cells was 63 744. When the loading displacement was 1 mm, the stress distribution of the cross section at 6.1 mm from the tip of the file was observed. The upper and lower surfaces were subjected to the maximum bending stress and entered the phase transformation yield stage. The finite element simulation could clearly show the deformation of the file. Various information such as deformation characteristics and stress distribution in the process were well fitted to the actual experimental curve. CONCLUSION The constitutive behavior of the material has a significant effect on the mechanical behavior of NiTi file. The finite element model established for the NiTi file of the CM wire can accurately capture the characteristics of various deformation processes of the NiTi root canal file, and it has a good fit with the actual experimental curve. The finite element model can be used for study on bending properties of CM wire.
Dental Alloys ; Equipment Design ; Finite Element Analysis ; Materials Testing ; Nickel ; Root Canal Preparation ; Stress, Mechanical ; Titanium

PURPOSE: The aim of the present study was to record the metal-ceramic bond strength of a feldspathic dental porcelain and a Co-Cr alloy, using the Direct Metal Laser Sintering technique (DMLS) for the fabrication of metal substrates. MATERIALS AND METHODS: Ten metal substrates were fabricated with powder of a dental Co-Cr alloy using DMLS technique (test group) in dimensions according to ISO 9693. Another ten substrates were fabricated with a casing dental Co-Cr alloy using classic casting technique (control group) for comparison. Another three substrates were fabricated using each technique to record the Modulus of Elasticity (E) of the used alloys. All substrates were examined to record external and internal porosity. Feldspathic porcelain was applied on the substrates. Specimens were tested using the three-point bending test. The failure mode was determined using optical and scanning electron microscopy. The statistical analysis was performed using t-test. RESULTS: Substrates prepared using DMLS technique did not show internal porosity as compared to those produced using the casting technique. The E of control and test group was 222 ± 5.13 GPa and 227 ± 3 GPa, respectively. The bond strength was 51.87 ± 7.50 MPa for test group and 54.60 ± 6.20 MPa for control group. No statistically significant differences between the two groups were recorded. The mode of failure was mainly cohesive for all specimens. CONCLUSION: Specimens produced by the DMLS technique cover the lowest acceptable metal-ceramic bond strength of 25 MPa specified in ISO 9693 and present satisfactory bond strength for clinical use.
Alloys ; Dental Porcelain ; Elastic Modulus ; Microscopy, Electron, Scanning ; Porosity