OBJECTIVE: To compare the retentions of different designs of cobalt-chromium (Co-Cr), pure titanium (CP Ti), and titanium alloy (Ti-6Al-4V) removable partial denture (RPD) circumferential clasps manufactured by selective laser melting (SLM) and to analyze the stress distribution of these clasps during the removal from abutment teeth. METHODS: Clasps with clasp arm size A (1.9 mm width/1.1 mm thickness at the body and 0.8-taper) or B (1.2 times A) and 0.25 mm or 0.50 mm undercut engagement were modeled on a prepared first premolar die, named as designs A1, A2, A3, and A4, respectively. The density and elastic modulus of SLM-built Co-Cr, CP Ti, and Ti-6Al-4V were measured and given to different groups of clasps. The density, elastic modulus, and Poisson ' s ratio of enamel were given to the die. The control group was the cast Co-Cr clasp with design A1, to which the density and elastic modulus of cast Co-Cr alloy were given. The Poisson's ratio of all metals was 0.33. The initial 5 N dislodging force was applied, and the maximum displacement of the clasp along the insertion path was computed. The load was reapplied with an increment of 5 N than in the last simulation until the clasp was completely dislodged. The retentive force range of different groups of clasps was obtained. The retentive forces of the SLM-built Co-Cr, CP Ti, and Ti-6Al-4V clasps with equivalent computed retentive force range to the control group were validated through the insertion/removal experiment. The von Mises stress distributions of these three groups of SLM-built clasps under 15 N loads were analyzed. RESULTS: SLM-built Co-Cr, CP Ti, and Ti-6Al-4V clasps with designs B1 or B2, and Co-Cr clasps with design A2 had higher retentive forces than those of the control group. SLM-built CP Ti and Ti-6Al-4V clasps with design A1 had lower retentive forces than those of the control group. SLM-built Co-Cr clasp with design A1 and SLM-built CP Ti and Ti-6Al-4V clasps with design A2 had equivalent retentive forces to those of the control group. The insertion/removal experiment showed that the measured retentive forces of these three groups of SLM-built clasps were (21.57±5.41) N, (19.75±4.47) N, and (19.32±2.04) N, respectively. No statistically significant measured retentive force difference was found among these three groups of SLM-built clasps (P>0.05). The maximum von Mises stress of these three groups of SLM-built clasps exceeded their responding yield strength except for the Ti-6Al-4V one. CONCLUSION SLM-built Co-Cr circumferential clasps had higher retention than CP Ti and Ti-6Al-4V ones with the same clasp arm size and undercut engagement. The retention of SLM-built circumferential clasps could be adjusted by changing the undercut engagement and clasp arm size. If SLM-built circumferential clasps are used in clinical practice, the Ti-6Al-4V clasp with clasp arm size A and 0.50 mm undercut engagement is recommended considering the long-term use of RPD in the patient's mouth.
Chromium Alloys ; Dental Clasps ; Denture Retention ; Denture, Partial, Removable ; Finite Element Analysis ; Humans ; Lasers ; Titanium

OBJECTIVES: At present, removable partial denture is still one of the main restoration methods for dentition defects. However, the trend for digital partial denture is becoming more and more obvious in the field of oral repair. However, there are relatively few studies on digital removable partial denture. The aim of this study is to investigate the effects of 3 processing technologies (precision casting, digital cutting, and 3D printing) on the fitness for the clasps of cobalt chromium alloy and pure titanium removable partial denture, and to provide a theoretical basis for the clinical application of digital removable partial denture. METHODS: Clasps of Co-Cr alloy and pure titanium were produced by 3 different processing technologies (precision casting, digital cutting, and 3D printing). There are 6 groups, including a casting pure titanium group, a casting cobalt chromium group, a cutting pure titanium group, a cutting cobalt chromium group, a printing pure titanium group, and a printing cobalt chromium group ( RESULTS: There was no statistical difference in fitness between the casting pure titanium group and the casting cobalt chromium group ( CONCLUSIONS The cobalt chromium alloy and pure titanium clasps made by precision casting, digital cutting, and 3D printing have good fitness. Under the same process, there is no significant difference between cobalt chromium alloy and pure titanium clasps. The 3D printing pure titanium clasps have better fitness than casting pure titanium and cutting pure titanium clasps, which meet the needs of clinical application.
Chromium Alloys ; Cobalt ; Denture, Partial, Removable ; Titanium

OBJECTIVE: To explore the effects of low-level long-term occupational exposure to chromate on the health of workers, and the potential biomarkers of early health effects in terms of lung function, immune toxicity and genetic damage. METHODS: A total of 22 chromate contact workers and 44 non-chromate contact workers from an electroplating enterprise with long-term occupational environment monitoring in line with the national standards in Inner Mongolia were investigated. The questionnaire survey was conducted to collect the basic situation, the history of smoking, drinking, diseases and so on. The portable lung function instrument, inductively coupled plasma mass spectrometry and cytokinesis-blocked micronucleus test were performed to measure the chromate contact workers'lung function, whole blood Cr (WB-Cr) and micronuclei frequency (MNF) of peripheral blood lymphocytes respectively. The cytometric bead array was used to detect the levels of IL-1β, IL-6, IL-8, IL-10, IL-12P70 and TNFα in the serum among the two groups. The effects of chromate exposure on the above-mentioned indexes involved biological exposure, lung function, immune response and genetic damage, and their correlation were analyzed with different statistical methods. RESULTS: (1) the average length of service for chromate contact workers was 31 years, and their concentration of WB-Cr was 1.11-4.19 μg/L. They were divided into high and low exposure groups according to the median of 1.72 μg/L. The WB-Cr in the high exposure group (2.17 μg/L) was higher than that in the low exposure group (1.58 μg/L) as well as the reference value of the healthy population (1.74 μg/L, P<0.05); (2) the lung function test showed 10 (45.45%) chromate exposure workers had single or multiple abnormal lung function indexes, among which large airway injury index PEF, and small airway injury indexes MVV and FEF25%-75% were all negatively correlated with WB-Cr (r=-0.53, P<0.05; r=-0.52, P<0.05; r=-0.44, P<0.05); (3) IL-1β, IL-6, IL-8 and TNFα in the serum of chromate contact workers were higher than those in the control group (P<0.05), and there was a positive correlation between TNFα and WB-Cr, and among these cytokines (P<0.05); (4) the average lymphocyte MNF in chromate contact workers was 1.341%, higher than the reference value of the general population (0.436%, P<0.01). Poisson regression analysis showed MNF in thehigh exposure group was higher than that in the low exposure group, OR (95%CI) =1.323 (1.049, 1.669); (5) multiple linear regression analysis showed that the lung function index FEF25%-75% decreased with the increase of TNFα (P<0.05), no significant correlation was found between other cytokines, MNF and lung function indexes. CONCLUSION Long-term low-level occupational exposure to chromate can cause the decline of lung function, immune inflammatory reaction and genetic damage in workers, in which local or systemic inflammatory response is associated with decreased lung function. Lung function indexes PEF, FEF25%-75% and MVV, serum cytokines IL-1β, IL-6, IL-8, and TNFα, and peripheral blood lymphocyte MNF may be used as early health effects biomarkers of chromate exposure.
Biomarkers ; China ; Chromates ; Humans ; Occupational Exposure ; Smoking

OBJECTIVEThis research estimated shear bond durability of zirconia and different substrates cemented by two self-adhesive resin cements (Clearfil SA Luting and RelyX U100) before and after aging conditioning.

METHODSMachined zirconia ceramic discs were cemented with four kinds of core material (cobalt-chromium alloy, flowable composite resin core material, packable composite resin, and dentin) with two self-adhesive resin cements (Clearfil SA Luting and RelyX U100). All specimens were divided into eight test groups, and each test group was divided into two subgroups. Each subgroup was subjected to shear test before and after 10 000 thermal cycles.

RESULTSAll factors (core materials, cements, and thermal cycle) significantly influenced bond durability of zirconia ceramic (P<0.00 1). After 10 000 thermal cycles, significant decrease was not observed in shear bond strength of cobalt-chromium alloy luted with Clearfil SA Luting (P>0.05); observed shear bond strength was significantly higher than those of other substrates (P<0.05). Significantly higher shear bond strength was noted in Clearfil SA Luting luted with cobalt-chromium alloy, flowable composite resin core material, and packable composite resin than that of RelyX U100 (P<0.05). However, significant difference was not observed in shear bond strength of dentin luted with Clearfil SA Luting and RelyX U100 (P>0.05).

CONCLUSIONSDifferent core materials and self-adhesive resin cements can significantly affect bond durability of zirconia ceramic. 
.

Adhesives ; Ceramics ; Chromium Alloys ; Composite Resins ; Dental Bonding ; Dental Cementum ; Dentin ; Humans ; Materials Testing ; Resin Cements ; Zirconium

PURPOSE: The purpose of this study was to evaluate the efficacy of two different metal conditioners for non-precious metal alloys for the bonding of porcelain to a cobalt-chromium (Co-Cr) alloy. MATERIALS AND METHODS: Disk-shaped specimens (2.5x10.0 mm) were cast with Co-Cr alloy and used as adherend materials. The bonding surfaces were polished with a 600-grid silicon carbide paper and airborne-particle abraded using 110 microm alumina particles. Bonding specimens were fabricated by applying and firing either of the metal conditioners on the airborne-particle abraded surface, followed by firing porcelain into 5 mm in diameter and 3 mm in height. Specimens without metal conditioner were also fabricated. Shear bond strength for each group (n=8) were measured and compared (alpha=.05). Sectional view of bonding interface was observed by SEM. EDS analysis was performed to determine the chemical elements of metal conditioners and to determine the failure modes after shear test. RESULTS: There were significant differences among three groups, and two metal conditioner-applied groups showed significantly higher values compared to the non-metal conditioner group. The SEM observation of the sectional view at bonding interface revealed loose contact at porcelain-alloy surface for non-metal conditioner group, however, close contact at both alloy-metal conditioner and metal conditioner-porcelain interfaces for both metal conditioner-applied groups. All the specimens showed mixed failures. EDS analysis showed that one metal conditioner was Si-based material, and another was Ti-based material. Si-based metal conditioner showed higher bond strengths compared to the Ti-based metal conditioner, but exhibited more porous failure surface failure. CONCLUSION: Based on the results of this study, it can be stated that the application of metal conditioner is recommended for the bonding of porcelain to cobalt-chromium alloys.
Alloys* ; Aluminum Oxide ; Chromium Alloys ; Dental Porcelain* ; Fires ; Shear Strength ; Silicon

BACKGROUND: Chromium is one of the most common metal allergens that cause allergic contact dermatitis. European regulation of chromium (VI) content in cement was first implemented in 2005, and regulation of chromium in leather in 2015. OBJECTIVE: This clinical study was performed to obtain basic data on subjects with allergic contact dermatitis due to chromium in Korea. We investigated the clinical characteristics of patients with chromium allergy among subjects with contact dermatitis who underwent patch tests. METHODS: Patch test data from June 1998 to January 2014 were retrospectively analyzed (n=975; men=290, women=685). Patients who showed positive reactions to potassium dichromate (chromium [+] group; n=58) and who showed positive reactions to other allergens except potassium dichromate (others [+] group; n=497) were identified and the characteristics of both groups were compared. Patients who only reacted to chromium (only chromium group; n=17) were identified, and their clinical characteristics were investigated. The prevalence of chromium allergy was analyzed in each 4-year period to study the changes over time. RESULTS: The sensitization rate of potassium dichromate was 5.9% (n=58) and women comprised 72.4% (n=42) of the chromium (+) group. Hands and feet were more frequently affected in the chromium (+) group (p=0.002 and 0.019, respectively). Occupational dermatitis was significantly less common in the chromium (+) group. Chromium allergy was the most prevalent in patients in their 50s (8.4%). The only chromium group had significantly more number of patients aged 40 years or older (p=0.004). The prevalence of chromium allergy was 13.5% during 1998~2002, but decreased to 5.4% during 2010~2014. CONCLUSION: The characteristics of patients with chromium allergy suggests that chromium exposure in daily activities, including leather exposure, is more relevant than occupational exposure for most patients. The prevalence of chromium allergy has been decreasing in Korea, which may be an effect of voluntary regulation of chromium content in cement by manufacturers.
Allergens ; Chromium* ; Dermatitis, Allergic Contact ; Dermatitis, Contact ; Dermatitis, Occupational ; Female ; Foot ; Hand ; Humans ; Hypersensitivity* ; Korea* ; Occupational Exposure ; Patch Tests ; Potassium Dichromate ; Prevalence ; Retrospective Studies

OBJECTIVEThis study aims to determine the effect of fluoride concentration on the corrosion behavior of cobalt-chromium alloy fabricated by two different technology processes in a simulated oral environment.

METHODSA total of 15 specimens were employed with selective laser melting (SLM) and another 15 for traditional casting (Cast) in cobalt-chromium alloy powders and blocks with the same material composition. The corrosion behavior of the specimens was studied by potentiodynamic polarization test under different oral environments with varying solubilities of fluorine (0, 0.05%, and 0.20% for each) in acid artificial saliva (pH = 5.0). The specimens were soaked in fluorine for 24 h, and the surface microstructure was observed under a field emission scanning electron microscope after immersing the specimens in the test solution at constant temperature.

RESULTSThe corrosion potential (Ecorr) value of the cobalt-chromium alloy cast decreased with increasing fluoride concentration in acidic artificial saliva. The Ecorr, Icorr, and Rp values of the cobalt-chromium alloy fabricated by two different technology processes changed significantly when the fluoride concentration was 0.20% (P < 0.05). The Ecorr, Icorr, and Rp values of the cobalt-chromium alloy fabricated by two different technology processes exhibited a statistically significant difference. The Icorr value of the cobalt-chromium alloy cast was higher than that in the SLM group cobalt-chromium alloy when the fluoride concentration was 0.20% (P < 0.05). The Ecorr, tRp alues of the cobalt-chromium alloy cast were lower htan those of the SLM group cobalt-chromium alloy when the fluoride concentration was 0.20% (P< 0 .05).

CONCLUSIONFluoride ions adversely affected the corrosion resistance of the cobalt-chromium alloy fabricated by two different technology processes. The corrosion resistance of the cobalt-chromium alloy cast was worse than that of the SLM group cobalt-chromium alloy when the fluoride concentration was 0.20%.

Chromium Alloys ; Corrosion ; Fluorides ; Lasers ; Phosphates ; Saliva, Artificial ; Sodium Fluoride

OBJECTIVETo investigate the changes in lung injury and oxidative stress of sprague-Dawleyy (SD) rats at different times after single intratracheal instillation of potassium dichromate.

METHODSA total of 50 healthy male SD rats were randomly divided into control group and potassium dichromate group. The potassium dichromate group and the control group received 3 ml/kg intratracheal instillation of K2Cr2O7 (1.5 mg/kg) and normal saline, respectively. Rats in these two groups were sacrificed in batches at 1, 3, 7, 14, and 28 days after exposure. The changes in the following indices were observed and analyzed: body weight, lung coefficient, alkaline phosphatase (AKP) in bronchoalveolar lavage fluid, glutathione peroxidase (GSH-Px) in lung homogenate, and reduced glutathione (GSH) in serum.

RESULTSThe rats in the potassium dichromate group had significantly decreased body weight on day 1 and day 3 after exposure than the control group (P<0.05). Lung coefficient increased significantly on day 7 (P<0.05) and kept increasing until the end of the experiment. The potassium dichromate group had a significantly higher activity of AKP than the control group on day 1 and day 7 after exposure (P<0.05). However, the potassium dichromate group had a significantly lower activity of GSH-Px than the control group on day 1 and day 3 after exposure (P<0.05). And the potassium dichromate group had a lower activity of reduced GSH than the control group on day 3 and day 7 after exposure.

CONCLUSIONSingle intratracheal instillation of 1.5 mg/kg potassium dichromate could result in lung inflammatory injury. of SD rats, and the injury is more severe on day 7 after exposure. Body injury is related to antioxidant activity, and the antioxidant.activity cannot recover completely on day 28 after exposure.

Alkaline Phosphatase ; metabolism ; Animals ; Bronchoalveolar Lavage Fluid ; Disease Models, Animal ; Glutathione ; blood ; Glutathione Peroxidase ; metabolism ; Lung ; physiopathology ; Lung Injury ; chemically induced ; physiopathology ; Male ; Oxidative Stress ; Potassium Dichromate ; toxicity ; Rats ; Rats, Sprague-Dawley

OBJECTIVETo compare five materials commonly used in dentistry, including three types of metals and two types of ceramics, by using different sequences of three magnetic resonance imaging (MRI) field strengths (0.35, 1.5, and 3.0 T).

METHODSThree types of metals and two types of ceramics that were fabricated into the same size and thickness as an incisor crown were placed in a plastic tank filled with saline. The crowns were scanned using an magnetic resonance (MR) machine at 0.35, 1.5, and 3.0 T field strengths. The TlWI and T2WI images were obtained. The differences of various materials in different artifacts of field MR scans were determined.

RESULTSThe zirconia crown presented no significant artifacts when scanned under the three types of MRI field strengths. The artifacts of casting ceramic were minimal. All dental precious metal alloys, nickel-chromium alloy dental porcelain, and cobalt-chromium ceramic alloy showed varying degrees of artifacts under the three MRI field strengths.

CONCLUSIONZirconia and casting ceramics present almost no or faint artifacts. By contrast, precious metal alloys, nickel-chromium alloy dental porcelain and cobalt-chromium ceramic alloy display MRI artifacts. The artifact area increase with increasing magnetic field.

Artifacts ; Ceramics ; Chromium Alloys ; Crowns ; Dental Alloys ; Dental Materials ; Dental Porcelain ; Magnetic Fields ; Magnetic Resonance Imaging ; Zirconium

OBJECTIVEThis study aims to evaluate the optical data of the different sites of the cobalt-chrome (Co-Cr) alloy abutments covered by four different all-ceramic crowns and the color difference between the crowns and target tab using a digital dental spectrophotometer.

METHODSTen Co-Cr alloy abutments were made and tried in four different groups of all-ceramic crowns, namely, Procera aluminia, Procera zirconia, Lava zirconia (Lava-Zir), and IPS E.max glass-ceramic lithium disilicate-reinforced monolithic. The color data of the cervical, body, and incisal sites of the samples were recorded and analyzed by dental spectrophotometer. The CIE L*, a*, b* values were again measured after veneering. The color difference between the abutments covered by all-ceramic crowns and A2 dentine shade tab was evaluated.

RESULTSThe L* and b* values of the abutments can be increased by all of the four groups of all-ceramic copings, but a* values were decreased in most groups. A statistical difference was observed among four groups. After being veneered, the L* values of all the copings declined slightly, and the values of a*, b* increased significantly. When compared with A2 dentine shade tab, the ΔE of the crowns was below 4.

CONCLUSIONFour ceramic copings were demonstrated to promote the lightness and hue of the alloy abutments effecttively. Though the colorimetric baseline of these copings was uneven, veneer porcelain can efficiently decrease the color difference between the samples and thee target.

Ceramics ; Chromium Alloys ; Cobalt ; Color ; Colorimetry ; Crowns ; Dental Materials ; Dental Porcelain ; Dental Prosthesis Design ; Humans ; Metal Ceramic Alloys ; Titanium ; Zirconium