OBJECTIVE To improve the quality standard for Jubei mixture . METHODS The chemical reaction of trinitrophenol and hydrocyanic acid was used to identify Armeniacae Amarum solution . Platycodon grandiflorus ，Fritillaria thunbergii，Scutellaria baicalensis ，the leaves of Eriobotrya japonica and Glycyrrhiza uralensis in Jubei mixture were identified by thin-layer chromatography （TLC）. High-performance liquid chromatography was used to simultaneously determine the contents of four active components ，such as amygdalin ，baicalin，wogonoside and monoammonium glycyrrhizinate in Jubei mixture . RESULTS Trinitrophenol test paper showed brick red . TLC spots of five medicinal materials were clear ，without interference from negative control . The linear ranges of amygdalin ，baicalin，wogonoside and monoammonium glycyrrhizinate were 0.066 8-1.335 5 μg（R2＝0.9994），0.189 8-3.796 9 μg（R2＝0.999 9），0.062 6-1.251 3 μg（R2＝0.999 9），0.041 8-0.835 5 μg（R2＝0.999 8）， respectively. RSDs of precision ，repeatability and stability tests were all lower than 2%. The average recoveries were 98.2%， 99.5%，98.3%，99.6%，and RSDs were 0.7%，1.6%，1.5%，1.1%（n＝6）. The contents of 15 batches of samples were different ， and the content of sample from company A was generally lower than those from companies B and C . CONCLUSIONS The standard established can reflect the inherent quality of Jubei mixture well .

Objective:To evaluate the biocompatibility of Ti-75 alloy(TA) as a substrate of composite implant (CI) and the role of the shear strength of TA-coating in the CI-bone interface. Methods:A transcortical implant model was used. A total of 32 implants of CI and TA were implanted into bilateral femur of 4 adult mongrel dogs. the animals were killed 3 and 6 months after surgery. The implant-bone interfaces were observed by morphological examination and the interface shear strength was measured by push-out test. After push-out test, the failure interfaces were observed by SEM. Results:Osseo-integration was confirmed in the both interfaces of CI and TA with bone. The interface strength(MPa) of CI in 3 and 6 month was 7. 84? 0.99 and 12. 76? 1. 45, that of TA 3. 71? 1. 10 and 6. 33? 0. 89 respectively (P