Study of bond strength of one-piece glass fiber posts-and-cores with flared root canals in vitro.
- Author:
Yuan ZHANG
1
;
Jian Min HAN
2
;
Lin LIU
1
;
Xu Liang DENG
3
Author Information
1. Department of Stomatology, Beijing Anzhen Hospital, Capital Medical University, Beijing 100029, China.
2. Department of Dental Materials, Peking University School and Hospital of Stomatology & National Clinical Research Center for Oral Diseases & National Engineering Laboratory for Digital and Material Technology of Stomatology & Beijing Key Laboratory of Digital Stomatology, Beijing 100081, China.
3. Department of Geriatric Dentistry, Peking University School and Hospital of Stomatology & National Clinical Research Center for Oral Diseases & National Engineering Laboratory for Digital and Material Technology of Stomatology & Beijing Key Laboratory of Digital Stomatology, Beijing 100081, China.
- Publication Type:Journal Article
- MeSH:
Composite Resins;
Dental Bonding;
Dental Pulp Cavity;
Dental Stress Analysis;
Dentin;
Glass;
Humans;
Materials Testing;
Post and Core Technique;
Resin Cements
- From:
Journal of Peking University(Health Sciences)
2019;51(2):327-334
- CountryChina
- Language:Chinese
-
Abstract:
OBJECTIVE:To compare the effects of three kinds of fiber posts (CAD/CAM one-piece glass fiber posts-and-cores, prefabricated glass fiber post and light curing plastic fiber post) on the bond strength of flared root canals and the effect of thermal cycling on their bond strength.
METHODS:Extracted human single teeth (n=90) were endodontically treated and randomly divided into three groups (n = 30 each). The teeth were restored by three kinds of fiber post: CAD/CAM one-piece glass fiber posts-and-cores, prefabricated posts and light curing plastic fiber post. Following post cementation, the specimens were stored in distilled water at 37 °C for 7 days. Half bonded specimens of each group were submitted to thermal cycling (6 000 times, 5 to 55 °C) prior to micro-push-out bond strength test. Fabrication of micro-push-out bond strength test specimens was conducted by precision slicing machine. The micro-push-out bond strength was tested using a universal testing machine, and the failure modes were examined with a stereomicroscope.
RESULTS:In CAD/CAM one-piece glass fiber posts-and-cores group, the bond strength of cervical, middle and apical was (9.58±2.67) MPa,(8.62±2.62) MPa,(8.21±2.48) MPa respectively before thermal cycling, and after thermal cycling the bond strength of cervical, middle and apical was (8.14±3.19) MPa,(6.43±2.47) MPa,(6.45±3.20) MPa respectively. In prefabricated posts group, the bonding strength of cervical, middle and apical was (3.89±2.04) MPa,(4.83±1.23) MPa,(4.67±1.86) MPa respectively before thermal cycling, and after thermal cycling the bond strength of cervical, middle and apical was (6.18±1.61) MPa,(5.15±1.94) MPa,(6.39±2.87) MPa respectively. In light curing plastic fiber post group, the bond strength of cervical, middle and apical before thermal cycling was (4.05±2.41) MPa,(1.75±1.70) MPa,(2.60±2.34) MPa respectively, and after thermal cycling the bond strength of cervical, middle and apical was (5.04±2.72) MPa,(1.96±1.70) MPa,(1.34±0.92) MPa respectively. Postal types and root canal regions were found to significantly affect the push-out bond strength. Compared with the other two groups, the one-piece glass fiber posts-and-cores had the highest bonding strength in the cervical, middle and apical. Temperature cycling has no significant effect on the micro push-out bond strength of three kinds of fiber posts.
CONCLUSION:One-piece glass fiber posts-and-cores has better bonding strength and excellent bonding performance.