Sealing effects of pinus massoniana bark extract on dentin tubule and its wear resistance in vitro
10.7652/jdyxb201804025
- VernacularTitle:马尾松树皮提取物对牙本质小管的封闭效果及其耐磨损性能的体外研究
- Author:
Cheng-Fang TANG
1
;
Li-Yan YANG
;
Hui ZENG
;
Xin-Yang MA
;
Meng WANG
;
Jing-Wei LI
Author Information
1. 西安医学院口腔医学系
- Keywords:
dentin hypersensitivity;
pinus massoniana bark extract(PMBE);
dentin tubule;
wear resistance;
sealing
- From:
Journal of Xi'an Jiaotong University(Medical Sciences)
2018;39(4):573-577,588
- CountryChina
- Language:Chinese
-
Abstract:
Objective To observe the sealing effect of transient pinus massoniana bark extract (PMBE)pre-coating on dentin tubules and its wear resistance so as to provide an experimental basis for PMBE to be used to prevent and treat dentin hypersensitivity.Methods The model of dentin hypersensitivity was established by acid etching method.The samples were transient pre-coating with 80 g/L of PMBE ethanol solution,and then some of them experienced brushing wear treatment with ethanol group and fluorine vanish group as negative and positive controls.The surface and profile morphologies of the samples were observed using field emission scanning electron microscope (FESEM)in each group.The area of dentin tubular openings (ADTO)and percentage area of dentin tubular openings (PADTO)were also measured.Results The dentin tubules were opened completely and the lumen of dentin tubules was empty in ethanol group.The dentin tubules were completely or basically closed and some films or plugging could be seen in the lumen of dentin tubules in fluorine vanish/immediate group and PMBE/immediate group.The dentin tubules were partly opened and some wear marks could be seen on the dentin surface in fluorine vanish/wear groups,PMBE/wear groups.ADTO and PADTO in ethanol group were significantly higher than those in fluorine vanish groups and PMBE groups (P＜0.05).ADTO and PADTO did not significantly differ between fluorine vanish/wear groups and PMBE/wear groups (P＞0.05),which were all significantly higher than those in fluorine vanish/immediate group and PMBE/immediate group (P＜0.05).Conclusion Local transient pre-coating of PMBE ethanol solution can achieve fine immediate sealing effect of dentin tubules and some degree of wear resistance.