FRACTURE TOUGHNESS AND FRACTURE MODE OF CEMENT-RETAINED VERSUS SCREW-RETRIEVABLE CEMENT-RETAINED IMPLANT-SUPPORTED CROWNS: A PILOT STUDY
- Author:
Ammar Yaseer Abdul Hakim @Abdul Khakin
1
;
Rohana Ahmad
2
;
Nur Hafizah Kamar Affendi
2
Author Information
- Publication Type:Journal Article
- Keywords: Dental Implant; Implant Abutment; Cement Retained; Screw-Retrievable Cement-Retained; Zirconia Crown
- From: Journal of University of Malaya Medical Centre 2024;27(Special Issue):341-348
- CountryMalaysia
- Language:English
- Abstract: FRACTURE TOUGHNESS AND FRACTURE MODE OF CEMENT-RETAINED VERSUS SCREW-RETRIEVABLE CEMENT-RETAINED IMPLANT-SUPPORTED CROWNS: A PILOT STUDY:The aim of this pilot study was to compare the fracture toughness and fracture mode of cement-retained versus screw-retrievable cement-retained implant-supported monolithic zirconia crowns. Ten implant-supported crowns were made from monolithic CAD/CAM zirconia and equally divided into control and test groups. The control group received cement-retained monolithic zirconia crowns (CR), while the test group received screw-retrievable cement-retained monolithic zirconia crowns (SRCR). The crowns were then bonded to prefabricated Variobase titanium-based abutments with resin luting cement. To simulate the aging process in the oral cavity, all samples were undergone thermal cycling machine. After ageing, each group underwent a single load fracture test to analyze the fracture load, and the fracture mode was evaluated using scanning electron microscopy (SEM). The Mann-Whitney U test was used to compare fracture toughness, and statistical significance was set at p<0.05. The mean fracture toughness of CR crowns was 2945.49 ± 511.426 N, while that of SRCR crowns was 2897.82 ± 510.837 N, but the difference was not significant (U=10, p= 0.917). SEM examination revealed that all failures originated from the fitting surface of the crowns. The titanium-based abutment remained intact in all specimens. Within the limitations of this pilot study, the CR showed higher fracture toughness than SRCR implant crown, but both specimen fracture at six times more than the average maximum bite force of posterior tooth. The presence of screw access in SRCR has affected the fracture mode.