The effects of two MMPs inhibitors on the bonding performance in moderate fluorosis dentin
10.3760/cma.j.cn231583-20250321-00102
- VernacularTitle:两种MMPs抑制剂对中度氟斑牙牙本质粘接性能的影响
- Author:
Jiyan JIANG
1
;
Mengjie CHU
;
Ye TANG
;
Wanzhi HE
;
Hua YANG
;
Liming CHEN
Author Information
1. 贵阳市口腔医院牙体牙髓病科，贵阳 550000
- Publication Type:Journal Article
- Keywords:
Dental fluorosis;
Dentin bonding;
Ethylene diamine tetraacetic acid;
Chlorhexidine
- From:
Chinese Journal of Endemiology
2025;44(11):868-871
- CountryChina
- Language:Chinese
-
Abstract:
Objective:To study the effects of chlorhexidine (CHX) and ethylene diamine tetraacetic acid (EDTA) on adhesive properties of moderate fluorosis dentin.Methods:From August to September 2024, a total of 30 freshly extracted, non-carious and non-defective mandibular molars with moderate dental fluorosis, extracted for impaction or orthodontic reasons, were collected from the patients at the Department of Oral and Maxillofacial Surgery at Guiyang Stomatological Hospital and randomly divided into three groups (Groups A, B, and C, n = 10) using a simple randomization method, and pretreated for 60 s with normal saline (Group A), 17%EDTA gel (Group B), and 2%CHX solution (Group C), respectively. Subsequently, microtensile bonding strength testing and microleakage evaluation were performed. Results:The immediate bonding strengths of Groups A, B, and C were (14.23 ± 4.75), (20.94 ± 7.46), and (28.76 ± 14.61) MPa, respectively, and the bonding strengths after aging were (9.89 ± 3.81), (19.05 ± 7.85), and (22.15 ± 8.67) MPa, respectively. There were statistically significant differences in both immediate and aged bonding strengths among the three groups ( F = 6.08, 8.07, P = 0.010, 0.002). The immediate bonding strength of Group C was significantly higher than that of Group A ( P < 0.05), and the post aging bonding strength of both Group B and Group C was significantly higher than that of Group A ( P < 0.05). The proportion of silver staining area with microleakage in Groups A, B, and C were 21.87% (14.65%, 40.15%), 2.34% (1.87%, 5.29%), and 17.54% (4.59%, 20.47%), respectively, with statistically significant differences among the three groups ( H = 27.36, P = 0.001). The proportion of silver stained area with microleakage in Group B was significantly lower than that in Group A and Group C, and the difference was statistically significant ( P < 0.05). Conclusions:Pretreatment of moderate fluorosis dentin with 2%CHX or 17%EDTA can improve resin bongding performance, with EDTA being superior in reducing microleakage and CHX being better in enhancing adhesion strength.