Effect of hydrolytic resistance urushiol-modified monomer on comprehensive performance of light-curing resin composites
10.13481/j.1671-587X.20250328
- VernacularTitle:耐水解型漆酚改性单体对光固化复合树脂综合性能的影响
- Author:
Zhengyuan YANG
1
;
Yaqing WEN
;
Lingkang LIU
;
Qi LIN
;
Song ZHU
Author Information
1. 吉林大学口腔医院修复科,吉林 长春 130021
- Keywords:
Light-cured composite resin;
Water sorption value;
Double bond conversion rate;
Volume shrinkage rate;
Mechanical properties
- From:
Journal of Jilin University(Medicine Edition)
2025;51(3):814-821
- CountryChina
- Language:Chinese
-
Abstract:
Objective:To synthesize a hydrolysis-resistant urushiol-modified monomer(UMM)to improve the hydrolysis resistance of light-cured composite resin,while reducing the volume shrinkage rate(VS),increasing the double bond conversion rate(DC),and mitigating the potential biosafety concerns of bisphenol A glycidyl methacrylate(Bis-GMA)monomer.Methods:UMM was synthesized by modifying urushiol via an acyl chloride reaction,and its structure was analyzed and characterized using Fourier transform infrared spectroscopy(FT-IR).Control group was consisted of Bis-GMA/triethylene glycol dimethacrylate(TEGDMA)without UMM,while 10%UMM,15%UMM,and 20%UMM groups were prepared by partially replacing Bis-GMA with UMM at mass fractions of 10%,15%,and 20%,respectively.The viscosity of UMM was measured using a rheometer.The DC of light-cured composite resin in various groups was detected by FT-IR spectroscopy,and the VS was calculated.The contact angle of light-cured composite resin in various groups was measured using the sessile drop method,and the water sorption and solubility values were calculated.The mechanical properties of light-cured composite resin in various groups were tested.The in vitro cytotoxicity of light-cured composite resin in various groups was evaluated using the cell counting kit-8(CCK-8)assay.Results:The FT-IR spectra results showed that the absorption peak of the hydroxyl group at 3 402 cm-1 disappeared,while characteristic absorption peaks of-C=O and-C=C appeared at 1 745 and 1 637 cm-1,indicating that urushiol successfully reacted with acryloyl chloride to form UMM.The viscosity of UMM ranged from 25.14 to 29.43 Pa·s.Compared with control group,the DC of light-cured composite resin in 10%UMM,15%UMM,and 20%UMM groups was significantly increased(P<0.05),while the VS was significantly decreased(P<0.05),both in a dose-dependent manner.Compared with control group,the contact angle of light-cured composite resin in 10%UMM,15%UMM,and 20%UMM groups was significantly increased(P<0.05).Compared with 10%UMM group,the contact angle of light-cured composite resin in 15%UMM and 20%UMM groups was further increased(P<0.05).Compared with control group,the water sorption and solubility values of light-cured composite resin in 10%UMM,15%UMM,and 20%UMM groups were significantly decreased(P<0.05),showing a dose-dependent trend.After 24 h of water immersion,compared with control group,the flexural strength(FS)and elastic modulus(EM)of light-cured composite resin in 10%UMM,15%UMM,and 20%UMM groups were significantly decreased(P<0.05),also in a dose-dependent manner.After 7 d of water immersion,compared with control group,the FS of light-cured composite resin in 10%UMM group was significantly increased(P<0.05),while that in 20%UMM group was significantly decreased(P<0.05).Compared with 10%UMM group,the FS of light-cured composite resin in 15%UMM and 20%UMM groups was significantly decreased(P<0.05),exhibiting a dose-dependent trend.Compared with control group,the EM of light-cured composite resin in 15%UMM and 20%UMM groups was significantly decreased(P<0.05),also in a dose-dependent manner.The relative growth rate(RGR)of the L929 cells in control,10%UMM,15%UMM,and 20%UMM groups was above 90%,with no statistically significant differences among groups(P>0.05),and all cytotoxicity results were qualified.Conclusion:A novel low-viscosity monomer UMM is successfully synthesized in this study.All UMM-containing light-cured composite resin formulations exhibit higher DC,lower VS,reduced water sorption and solubility values,improved hydrolysis resistance,and low cytotoxicity.UMM can serve as a potential resin monomer to enhance the hydrolysis resistance of light-cured composite resin.