Effect of speed sintering and aging on the translucency of high-translucent zirconia
10.7518/hxkq.2024.2023249
- VernacularTitle:快速烧结和低温老化对高透氧化锆半透性的影响
- Author:
Yan LI
1
;
Mengyi ZHONG
;
Ying YANG
Author Information
1. 南昌大学附属口腔医院,南昌 330006;江西省口腔生物医学重点实验室,南昌 330006;江西省口腔疾病临床医学研究中心,南昌 330006
- Keywords:
high-translucent zirconia;
speed sintering;
low-temperature degradation;
translucency
- From:
West China Journal of Stomatology
2024;42(1):62-66
- CountryChina
- Language:Chinese
-
Abstract:
Objective This work aimed to evaluate the effect of speed sintering and low-temperature degradation on the translucency of high-translucent zirconia.Methods The ST and TT specimens were randomly divided into two groups depending on the sintering process:conventional sintering and speed sintering.The sintered specimens were divided into three subgroups according to the aging time:aged for 0,5,and 20 h.Chromatic parameters(L*,a*,and b*values)were measured by Shade Eye NCC computer colorimeter in a dark environment under black and white back-ground,and the translucency parameter(TP)was used to evaluate the translucency of zirconia.Results Speed sintering may decrease the TP of ST and increase the TP of TT.As for the effect of low-temperature degradation on the translucen-cy of zirconia,the TP of ST decreased with the extension of aging time,and no significant difference was found in rapid sintering ST.Although the TP of TT decreased,no statistical difference was observed.Conclusion Speed sintering may decrease the translucency of high-strength zirconia and increase the translucency of high-translucent zirconia.Low-tem-perature degradation had no effect on the translucency of high-translucent zirconia.Speed sintering can be recommended for high-translucent zirconia in terms of translucency.