OBJECTIVES: This study aimed to observe the color rebound and rebound rates of non-pulp discolored teeth within 1 year after routine internal bleaching to guide clinical practice and prompt prognosis. METHODS: In this work, the efficacy of bleaching was observed in 20 patients. The color of discolored teeth was measured by using a computerized colorimeter before bleaching; immediately after bleaching; and at the 1st, 3rd, 6th, 9th, and 12th months after bleaching. The L*, a*, and b* values of the color of cervical, mesial, and incisal parts of the teeth were obtained, and the color change amounts ΔE*, ΔL*, Δa*, and Δb* were calculated. The overall rebound rate (P*) and the color rebound velocity (V*) were also analyzed over time. RESULTS: In 20 patients following treatment, the average ΔE* of tooth color change was 14.99. After bleaching, the neck and middle of the teeth ΔE* and ΔL* decreased in the 1st, 3rd, 6th, 9th, and 12th months, and the differences were statistically significant. Meanwhile, from the 9th month after bleaching, the rebound speed was lower than that in the 1st month, and the difference was statistically significant. The incisal end of the tooth ΔE* and ΔL* decreased in the 6th, 9th, and 12th months after bleaching, and the differences were statistically significant. No significant difference was found in the rebound speed between time points. However, this rate settled after the 9th month, with an average color rebound rate of 30.11% in 20 patients. CONCLUSIONS The results indicated that internal bleaching could cause a noticeable color change on pulpless teeth. The color rebound after bleaching was mainly caused by lightness (L*), which gradually decreased with time, and it was slightly related to a* and b*. The color of the teeth after internal bleaching rebounded to a certain extent with time, but the color rebound speed became stable from the 9th month. Clinically, secondary internal bleaching can be considered at this time according to whether the colors of the affected tooth and the adjacent tooth are coordinated and depending on the patient's needs.
Humans ; Tooth Bleaching/methods* ; Tooth, Nonvital/drug therapy* ; Color ; Tooth Discoloration/drug therapy* ; Tooth ; Hydrogen Peroxide/therapeutic use* ; Tooth Bleaching Agents/therapeutic use*

Tooth bleaching agents may weaken the tooth structure. Therefore, it is important to minimize any risks of tooth hard tissue damage caused by bleaching agents. The aim of this study was to evaluate the effects of applying 45S5 bioglass (BG) before, after, and during 35% hydrogen peroxide (HP) bleaching on whitening efficacy, physicochemical properties and microstructures of bovine enamel. Seventy-two bovine enamel blocks were prepared and randomly divided into six groups: distilled deionized water (DDW), BG, HP, BG before HP, BG after HP and BG during HP. Colorimetric and microhardness tests were performed before and after the treatment procedure. Representative specimens from each group were selected for morphology investigation after the final tests. A significant color change was observed in group HP, BG before HP, BG after HP and BG during HP. The microhardness loss was in the following order: group HP>BG before HP, BG after HP>BG during HP>DDW, BG. The most obvious morphological alteration of was observed on enamel surfaces in group HP, and a slight morphological alteration was also detected in group BG before HP and BG after HP. Our findings suggest that the combination use of BG and HP could not impede the tooth whitening efficacy. Using BG during HP brought better protective effect than pre/post-bleaching use of BG, as it could more effectively reduce the mineral loss as well as retain the surface integrity of enamel. BG may serve as a promising biomimetic adjunct for bleaching therapy to prevent/restore the enamel damage induced by bleaching agents.
Animals ; Biomimetic Materials ; analysis ; therapeutic use ; Cattle ; Ceramics ; analysis ; chemistry ; Chemical Phenomena ; Color ; Colorimetry ; Dental Enamel ; drug effects ; ultrastructure ; Electron Probe Microanalysis ; Glass ; analysis ; chemistry ; Hardness ; Hydrogen Peroxide ; pharmacology ; Hydrogen-Ion Concentration ; Microscopy, Electron, Scanning ; Protective Agents ; analysis ; therapeutic use ; Random Allocation ; Solubility ; Spectroscopy, Fourier Transform Infrared ; Time Factors ; Tooth Bleaching ; methods ; Tooth Bleaching Agents ; pharmacology ; Water ; chemistry ; X-Ray Diffraction