OBJECTIVES: This study assessed the effect of water storage on the flexural strength (FS) of low shrinkage composites. MATERIALS AND METHODS: A total of 165 bar-shaped specimens (2 × 2 × 25 mm) were fabricated of 2 low shrinkage composites (Filtek P90 [3M ESPE], GC Kalore [GC International]) and a conventional methacrylate-based composite (Filtek Z250 [3M ESPE]). The specimens were subjected to 3-point bending test at 6 time intervals, namely: immediately after curing, at 24 hours, 1 week, 1 month, 6 months, and 1 year following storage in wet and dry conditions. The FS of the specimens were measured by applying compressive load at a crosshead speed of 1.0 mm/min. Data was analyzed using 3-way analysis of variance (ANOVA) and Tukey's test. RESULTS: Three-way ANOVA revealed significant interactions between time, type of composite, and storage condition (p = 0.001). Tukey's multiple comparison test revealed significant reductions in FS of all composites after 6 months and 1 year of storage in distilled water compared to dry condition. CONCLUSIONS: Filtek P90 showed the highest and GC Kalore showed the lowest FS after 1 year storage in distilled water. The immediate high strength of Filtek Z250 significantly decreased at 1 year and its final value was lower than that of Filtek P90.
Composite Resins* ; Polymers ; Silorane Resins* ; Water*

OBJECTIVES: The aim of this study was to evaluate the effect of pre-etching on the bond strength of silorane-based composite specific adhesive system to dentin. MATERIALS AND METHODS: Thirty human molars were randomly divided into 5 groups according to the different bonding strategies. For teeth restored with silorane-based composite (Filtek Silorane, 3M ESPE), the specific self-etching adhesive system (Adhesive System P90, 3M ESPE) was used with and without pre-etching (Pre-etching/Silorane and Silorane groups). Teeth restored with methacrylate based-composite (Filtek Z250, 3M ESPE) were hybridized with the two-step self-etching system (Clearfil SE Bond, Kuraray), with and without pre-etching (Pre-etching/Methacrylate and Methacrylate groups), or three-step adhesive system (Adper Scotchbond Multi-Purpose, 3M ESPE) (Three-step/Methacrylate group) (n = 6). The restored teeth were sectioned into stick-shaped test specimens (1.0 x 1.0 mm), and coupled to a universal test machine (0.5 mm/min) to perform microtensile testing. RESULTS: Pre-etching/Methacrylate group presented the highest bond strength values, with significant difference from Silorane and Three-step/Methacrylate groups (p < 0.05). However, it was not significantly different from Preetching/Silorane and Methacrylate groups. CONCLUSIONS: Pre-etching increased bond strength of silorane-based composite specific adhesive system to dentin.
Adhesives* ; Dentin ; Humans ; Molar ; Silorane Resins ; Tooth

Dental composites have improved significantly in physical properties over the past few decades. However, polymerization shrinkage and stress is still the major drawback of composites, limiting its use to selected cases. Much effort has been made to make low shrinking composites to overcome this issue and silorane-based composites have recently been introduced into the market. The aim of this study was to measure the volumetric polymerization shrinkage kinetics of a silorane-based composite and compare it with conventional methacrylate-based composites in order to evaluate its effectiveness in reducing polymerization shrinkage. Five commercial methacrylate-based (Beautifil, Z100, Z250, Z350 and Gradia X) and a silorane-based (P90) composites were investigated. The volumetric change of the composites during light polymerization was detected continuously as buoyancy change in distilled water by means of Archemedes'principle, using a newly made volume shrinkage measurement instrument. The null hypothesis was that there were no differences in polymerization shrinkage, peak polymerization shrinkage rate and peak shrinkage time between the silorane-based composite and methacrylate-based composites. The results were as follows: 1. The shrinkage of silorane-based (P90) composites was the lowest (1.48%), and that of Beautifil composite was the highest (2.80%). There were also significant differences between brands among the methacrylate-based composites. 2. Peak polymerization shrinkage rate was the lowest in P90 (0.13%/s) and the highest in Z100 (0.34%/s). 3. The time to reach peak shrinkage rate of the silorane-based composite (P90) was longer (6.7 s) than those of the methacrylate-based composites (2.4-3.1 s). 4. Peak shrinkage rate showed a strong positive correlation with the product of polymerization shrinkage and the inverse of peak shrinkage time (R = 0.95).
Composite Resins ; Kinetics ; Light ; Polymerization ; Polymers ; Silorane Resins ; Water

OBJECTIVES: The aim of this study was to evaluate the effect of three different drinks on the color parameters of four different restorative materials. MATERIALS AND METHODS: Three different composites (Filtek Ultimate Universal Restorative, Filtek Ultimate Flowable, and Filtek Silorane, 3M ESPE) and a polyacid-modified composite resin material (Dyract XP, Dentsply DeTrey GmbH) were evaluated. Eighty-four disc-shaped specimens of 8 mm in diameter and 2 mm in thickness were prepared (n = 21 each). Color coordinates (L*a*b*, DeltaL*, Deltaa*, Deltab*, and DeltaE*) were measured using a VITA Easyshade Compact (VITA Zahnfabrik) after 24 hr of storage (baseline) and after 30 day of storage in three different beverages of black tea, Coca cola, or water (control) (n = 7). In each beverage, the specimens were stored three times a day, one hr each, for 30 day. The color changes (DeltaE) were calculated and were analyzed by Kruskal-Wallis and Dunn multiple comparison test. RESULTS: The color difference (DeltaE*) of the resin materials ranged between 1.31 and 15.28 after 30 day of immersion in the staining solutions. Dyract XP in Coca cola (15.28 +/- 2.61) and black tea (12.22 +/- 2.73) showed the highest mean DeltaE* value after 30 day, followed by Filtek Ultimate Universal Restorative (5.99 +/- 1.25) and Filtek Ultimate Flowable (4.71 +/- 1.40) in black tea (p < 0.05). CONCLUSIONS: The compomers displayed unacceptable color changes at the end of 30 day in all beverages. Among resin composites, the silorane based composite exhibited relatively good color stability than the others. Filtek Ultimate Universal Restorative and Filtek Flowable showed similar color changes in all beverages.
Beverages ; Coca ; Cola ; Compomers ; Immersion ; Nanocomposites ; Silorane Resins ; Tea ; Water

Since the introduction of restorative dental composites, their physical properties have been significantly improved. However, polymerization shrinkage is still a major drawback. Many efforts have been made to develop a low shrinking composite, and silorane-based composites have recently been introduced into the market. In addition, many different methods have been developed to measure the polymerization shrinkage. In this study, we developed a new method to measure the linear polymerization shrinkage of composites without direct contact to a specimen using a particle tracking method with computer vision. The shrinkage kinetics of a commercial silorane-based composite (P90) and two conventional methacrylate-based composites (Z250 and Z350) were investigated and compared. The results were as follows: 1. The linear shrinkage of composites was 0.33-1.41%. Shrinkage was lowest for the silorane-based (P90) composite, and highest for the flowable Z350 composite. 2. The new instrument was able to measure the true linear shrinkage of composites in real time without sensitivity to the specimen preparation and geometry.
Kinetics ; Polymerization ; Polymers ; Silorane Resins ; Track and Field ; Vision, Ocular

PURPOSE: This in vitro study investigated the fracture resistance of endodontically treated premolars restored using silorane- or methacrylate-based composite along with or without fiber or nano-ionomer base. MATERIALS AND METHODS: Ninety-six intact maxillary premolars were randomly divided into eight groups (n = 12). G1 (negative control) was the intact teeth. In Groups 2-8, root canal treatment with mesio-occlusodistal preparation was performed. G2 (positive control) was kept unrestored. The other groups were restored using composite resin as follows: G3, methacrylate-based composite (Z250); G4, methacrylate composite (Z250) with polyethylene fiber; G5 and G6, silorane-based composite (Filtek P90) without and with the fiber, respectively; G7 and G8, methacrylate- and silorane-based composite with nano-ionomer base, respectively. After aging period and thermocycling for 1000 cycles, fracture strength was tested and fracture patterns were inspected. The results were analyzed using ANOVA and Tukey HSD tests (alpha=0.05). RESULTS: Mean fracture resistance for the eight groups (in Newton) were G1: 1200 +/- 169a, G2: 360 +/- 93b, G3: 632 +/- 196c, G4: 692 +/- 195c, G5: 917 +/- 159d, G6: 1013 +/- 125ad, G7: 959 +/- 148d, G8: 947 +/- 105d (different superscript letters revealed significant difference among groups). Most of the fractures in all the groups were restorable, except Group 3. CONCLUSION: Silorane-based composite revealed significantly higher strength of the restored premolars compared to that of methacrylate one. Fiber insertion demonstrated no additional effect on the strength of both composite restorations; however, it increased the prevalence of restorable fracture of methacrylate-based composite restored teeth. Using nano-ionomer base under methacrylate-based composite had a positive effect on fracture resistance and pattern. Only fiber-reinforced silorane composite restoration resulted in a strength similar to that of the intact teeth.
Aging ; Bicuspid* ; Dental Pulp Cavity ; Polyethylene ; Prevalence ; Silorane Resins ; Tooth

OBJECTIVETo evaluate the color stability and translucency of silorane-based low shrinkage composite after in vitro aging procedures of thermal cycling and water storage respectively, and to compare with those of conventional methacrylate-based posterior composite.

METHODSThree light-cured composite resins, dimethacrylate-based composite A (Filtek™ Z350), B (Filtek™ P60) and silorane-based composite C (Filtek™ P90), were tested in this study. Ten specimens (10 mm in diameter, 1 mm in height) of each composite were prepared. The ten specimens in each group were then divided into two subgroups (n = 5). One subgroup underwent thermal cycling [(5.0 ± 0.5)~(55.0 ± 1.0) °C, 10 000 cycles] and the other was stored in 37 C° distilled water for 180 days. With a spectrophotometer, the CIE L * a * b * parameters of the specimens were tested before and after artificial aging against white, medium grey and black backgrounds, respectively. △E, TP and △TP were calculated and data were analyzed using independent-samples t test and partial analysis (P < 0.05).

RESULTSWith regard to color stability, silorane-based composite showed color alteration above the clinically acceptable levels (△E > 3.3), and also showed higher △E with a statistically significant difference in comparison with the other composites (B and C) (P < 0.05) after artificial aging. With regard to translucency, composite C showed more alteration compared with composite B (P < 0.05) after thermal cycling.

CONCLUSIONSIt may be concluded that the silorane-based composite underwent greater alteration with regard to color stability and translucency.

Aging ; Color ; Composite Resins ; Light ; Materials Testing ; Methacrylates ; Silorane Resins ; Spectrophotometry ; Surface Properties ; Water

The purpose of this study was to evaluate the color stability of light cured composite resins according to the resin matrices. Three kinds of resin matrices such as Bis-GMA (Venus® Diamond; VD), Silorane (FiltekTM P90; P90), and Ormocer (Admira; Ad) were selected. Each of them were used to prepare 30 specimens. The initial CIE L*a*b* values were measured by means of a Spectrophotometer (NF999, Nippon Denshoku, Japan). For accelerated aging process, the specimens were immersed in a circulating water bath with distilled water at 60℃. Spectrophotometric analyses were made after immersion of 8, 16, 24, 41 days and the color difference (ΔE*) was calculated. The L* value increased compared with initial L* value. VD had the greatest L* value change and Ad had the smallest L* value change (p<0.05). Ad had the greatest a* value change and VD had the smallest a* value change (p<0.05). The b* value of P90 increased steadily in positive value (+)(p<0.05). ΔE* of Ad had the smallest value and that of P90 had the greatest change with time. According to this study, the value of light cured composite resins was increased with water sorption and color of those changed into greenish and yellowish. And according to the evaluation of color stability, Ad with Ormocer as resin matrices had the best color stability with time in oral environment and P90 with Silorane as resin matrices had the lowest color stability with time. And VD had the greatest initial ΔE*.
Aging ; Baths ; Bisphenol A-Glycidyl Methacrylate ; Composite Resins ; Diamond ; Immersion ; Organically Modified Ceramics ; Silorane Resins ; Water

OBJECTIVE: To evaluate the shear bond strength (SBS), fracture mode, wire pull out (WPO) resistance and microleakage between low-shrinking and conventional composites used as a lingual retainer adhesive. METHODS: A total of 120 human mandibular incisor teeth, extracted for periodontal reasons, were collected. Sixty of them were separated into two groups. To determine the SBS, either Transbond-LR (3M-Unitek) or Silorane (3M-Espe) was applied to the lingual surface of the teeth by packing the material into standard cylindrical plastic matrices (Ultradent) to simulate the lingual retainer bonding area. To test WPO resistance, 20 samples were prepared for each composite where the wire was embedded in the composite materialand cured. Then tensile stress was applied until failure of the composite occurred. The remaining 60 teeth were divided into two groups and multi-stranded 0.0215-inch diameter wire was bonded with the same composites. Microleakage was evaluated by the dye penetration method. Statistical analyses were performed by Wilcoxon, Pearson chi-square, and Mann-Whitney-U tests at p < 0.05 level. RESULTS: The SBS and WPO results were not statistically significant between the two groups. Significant differences were found between the groups in terms of fracture mode (p < 0.001). Greater percentages of the fractures showed mix type failure (85%) for Silorane and adhesive (60%) for Transbond-LR. Microleakage values were lower in low-shrinking composite than the control and this difference was found to be statistically significant (p < 0.001). CONCLUSIONS: Low-shrinking composite produced sufficient SBS, WPO and microleakage values on the etched enamel surfaces, when used as a lingual retainer composite.
Adhesives ; Dental Enamel ; Humans ; Incisor ; Orthodontic Retainers ; Plastics ; Resin Cements ; Shear Strength ; Silorane Resins ; Tooth

OBJECTIVES: The purpose of this study was to evaluate microTBS (microtensile bond strength) of current dentin bonding adhesives which have different hydrophobicity with low-shrinkage silorane resin. MATERIALS AND METHODS: Thirty-six human third molars were used. Middle dentin was exposed. The teeth were randomly assigned to nine experimental groups: Silorane self-etch adhesives (SS), SS + phosphoric acid etching (SS + pa), Adper easy bond (AE), AE + Silorane system bonding (AE + SSb), Clearfil SE bond (CSE), CSE + SSb, All-Bond 2 (AB2), AB2 + SSb, All-Bond 3 (AB3). After adhesive's were applied, the clinical crowns were restored with Filtek LS (3M ESPE). The 0.8 mm x 0.8 mm sticks were submitted to a tensile load using a Micro Tensile Tester (Bisco Inc.). Water sorption was measured to estimate hydrophobicity adhesives. RESULTS: microTBS of silorane resin to 5 adhesives: SS, 23.2 MPa; CSE, 19.4 MPa; AB3, 30.3 MPa; AB2 and AE, no bond. Additional layering of SSb: CSE + SSb, 26.2 MPa; AB2 + SSb, 33.9 MPa; AE + SSb, no bond. High value of microTBS was related to cohesive failure. SS showed the lowest water sorption. AE showed the highest solubility. CONCLUSIONS: The hydrophobicity of adhesive increased, and silorane resin bond-strength was also increased. Additional hydrophobic adhesive layer did not increase the bond-strength to silorane resin except AB2 + SSb. All-Bond 3 showed similar microTBS & water sorption with SS. By these facts, we could reach a conclusion that All-Bond 3 is a competitive adhesive which can replace the Silorane adhesive system.
Adhesives ; Crowns ; Dentin ; Humans ; Hydrophobic and Hydrophilic Interactions ; Methacrylates ; Molar, Third ; Phosphoric Acids ; Resin Cements ; Silorane Resins ; Tooth ; Water