The objective of this systematic review was to assess tooth wear against ceramic crowns in posterior region in vitro and in vivo. An electronic PubMed search was conducted to identify studies on tooth wear against ceramic crowns in posterior region. The selected studies were analyzed in regard to type of crowns, natural antagonist, measuring protocol and outcome. From a yield of 1 000 titles, 43 articles were selected for full-text analysis; finally, no in vitro and only five in vivo studies met the inclusion criteria. As there is heterogeneity in design, used measuring method, ceramics and analysis-form, a meta-analysis was not possible. Results of these studies are very controversial which makes a scientifically valid comparison impossible. This review indicated that some all-ceramic crowns are as wear friendly as metal-ceramic crowns. Up to now, it has been impossible to associate tooth wear with any specific causal agent. The role of ceramic surface treatment that might be responsible for the changing in rate of tooth wear seems undetermined as yet through clinical trials. The literature reveals that studies on this topic are subject to a substantial amount of bias. Therefore, additional clinical studies, properly designed to diminish bias, are warranted.
Crowns ; Dental Enamel ; pathology ; Dental Porcelain ; chemistry ; classification ; Humans ; Metal Ceramic Alloys ; chemistry ; Surface Properties ; Tooth Crown ; pathology ; Tooth Wear ; etiology

PURPOSE: The aim of the present randomized controlled study was to compare prefabricated all-ceramic, anatomically shaped healing abutments followed by all-ceramic abutments and all-ceramic crowns and prefabricated standard-shaped (round-diameter) titanium healing abutments followed by final titanium abutments restored with porcelain-fused-to-metal (PFM) implant crowns in the premolar and molar regions. MATERIALS AND METHODS: Forty-two patients received single implants restored either by all-ceramic restorations (test group, healing abutment, final abutment, and crown all made of zirconia) or conventional titanium-based restorations. Immediately after prosthetic incorporation and after 12 months of loading, implant survival, technical complications, bone loss, sulcus fluid flow rate (SFFR) as well as plaque index (PI) and implant stability (Periotest) were analyzed clinically and radiologically. RESULTS: After 12 months of loading, an implant and prosthetic survival rate of 100% was observed. Minor prosthetic complications such as chipping of ceramic veneering occurred in both groups. No statistical significant differences were observed between both groups with only a minimum of bone loss, SFFR, and PI. CONCLUSION: All-ceramic implant prostheses including a prefabricated anatomically shaped healing abutment achieved comparable results to titanium-based restorations in the posterior region. However, observational results indicate a benefit as shaping the peri-implant soft-tissue with successive provisional devices and subsequent compression of the soft tissue can be avoided.
Bicuspid ; Ceramics ; Crowns ; Humans ; Molar ; Prostheses and Implants ; Survival Rate ; Titanium

PURPOSE: The objective of the study was to analyze the impact of cement, bonding pretreatment, and ceramic abutment material on the overall color results of CAD-CAM ceramic crowns bonded to titanium-based hybrid abutments. MATERIALS AND METHODS: For single implant restoration of a maxillary lateral incisor a total of 51 CAD-CAM-fabricated monolithic lithium disilicate crowns were fabricated and subsequently bonded onto 24 lithium disilicate Ti-base abutments, 24 zirconia Ti-base abutments and 3 resin abutment replicas as a control group.The 48 copings were cemented with three definitive and one provisional cement on both grit-blasted and non-blasted Ti-bases. The color of each restoration and surrounding artificial gingiva was measured spectrophotometrically at predefined measuring points and the CIELAB (ΔE ab ) color scale values were recorded. RESULTS: The color outcome of ceramic crowns bonded to hybrid abutments and soft tissues was affected differently by cements of different brands. Grit-blasting of Ti-bases prior to cementing CAD-CAM copings affected the color results of allceramic crowns. There was a significant difference (P = .038) for the median ΔE value between blasted and non-blasted reconstructions at the cervical aspect of the crown. Full-ceramic crowns on zirconia Ti-base abutments exhibited significantly lower ΔE values below the threshold of visibility (ΔE 1.8). In all subcategories tested, the use of a highly opaque temporary cement demonstrated the lowest median ΔE for both the crown and the artificial gingiva. CONCLUSION Various cements, core ceramic materials and airborne particle abrasion prior to bonding can adversely affect the color of Ti-base supported ceramic crowns and peri-implant soft tissue. However, zirconia CAD-CAM copings and an opaque cement can effectively mask this darkening.

PURPOSE: The objective of the study was to analyze the impact of cement, bonding pretreatment, and ceramic abutment material on the overall color results of CAD-CAM ceramic crowns bonded to titanium-based hybrid abutments. MATERIALS AND METHODS: For single implant restoration of a maxillary lateral incisor a total of 51 CAD-CAM-fabricated monolithic lithium disilicate crowns were fabricated and subsequently bonded onto 24 lithium disilicate Ti-base abutments, 24 zirconia Ti-base abutments and 3 resin abutment replicas as a control group.The 48 copings were cemented with three definitive and one provisional cement on both grit-blasted and non-blasted Ti-bases. The color of each restoration and surrounding artificial gingiva was measured spectrophotometrically at predefined measuring points and the CIELAB (ΔE ab ) color scale values were recorded. RESULTS: The color outcome of ceramic crowns bonded to hybrid abutments and soft tissues was affected differently by cements of different brands. Grit-blasting of Ti-bases prior to cementing CAD-CAM copings affected the color results of allceramic crowns. There was a significant difference (P = .038) for the median ΔE value between blasted and non-blasted reconstructions at the cervical aspect of the crown. Full-ceramic crowns on zirconia Ti-base abutments exhibited significantly lower ΔE values below the threshold of visibility (ΔE 1.8). In all subcategories tested, the use of a highly opaque temporary cement demonstrated the lowest median ΔE for both the crown and the artificial gingiva. CONCLUSION Various cements, core ceramic materials and airborne particle abrasion prior to bonding can adversely affect the color of Ti-base supported ceramic crowns and peri-implant soft tissue. However, zirconia CAD-CAM copings and an opaque cement can effectively mask this darkening.

PURPOSE: The objective of the study was to analyze the impact of cement, bonding pretreatment, and ceramic abutment material on the overall color results of CAD-CAM ceramic crowns bonded to titanium-based hybrid abutments. MATERIALS AND METHODS: For single implant restoration of a maxillary lateral incisor a total of 51 CAD-CAM-fabricated monolithic lithium disilicate crowns were fabricated and subsequently bonded onto 24 lithium disilicate Ti-base abutments, 24 zirconia Ti-base abutments and 3 resin abutment replicas as a control group.The 48 copings were cemented with three definitive and one provisional cement on both grit-blasted and non-blasted Ti-bases. The color of each restoration and surrounding artificial gingiva was measured spectrophotometrically at predefined measuring points and the CIELAB (ΔE ab ) color scale values were recorded. RESULTS: The color outcome of ceramic crowns bonded to hybrid abutments and soft tissues was affected differently by cements of different brands. Grit-blasting of Ti-bases prior to cementing CAD-CAM copings affected the color results of allceramic crowns. There was a significant difference (P = .038) for the median ΔE value between blasted and non-blasted reconstructions at the cervical aspect of the crown. Full-ceramic crowns on zirconia Ti-base abutments exhibited significantly lower ΔE values below the threshold of visibility (ΔE 1.8). In all subcategories tested, the use of a highly opaque temporary cement demonstrated the lowest median ΔE for both the crown and the artificial gingiva. CONCLUSION Various cements, core ceramic materials and airborne particle abrasion prior to bonding can adversely affect the color of Ti-base supported ceramic crowns and peri-implant soft tissue. However, zirconia CAD-CAM copings and an opaque cement can effectively mask this darkening.

PURPOSE: All-ceramic restorations required extensive tooth preparation. The purpose of this in vitro study was to investigate a minimally invasive preparation and thickness of monolithic zirconia crowns, which would provide sufficient mechanical endurance and strength. MATERIALS AND METHODS: Crowns with thickness of 0.2 mm (group 0.2, n=32) or of 0.5 mm (group 0.5, n=32) were milled from zirconia and fixed with resin-based adhesives (groups 0.2A, 0.5A) or zinc phosphate cements (groups 0.2C, 0.5C). Half of the samples in each subgroup (n=8) underwent thermal cycling and mechanical loading (TCML)(TC: 5℃ and 55℃, 2×3,000 cycles, 2 min/cycle; ML: 50 N, 1.2×106 cycles), while the other samples were stored in water (37℃/24 h). Survival rates were compared (Kaplan-Maier). The specimens surviving TCML were loaded to fracture and the maximal fracture force was determined (ANOVA; Bonferroni; α=.05). The fracture mode was analyzed. RESULTS: In both 0.5 groups, all crowns survived TCML, and the comparison of fracture strength among crowns with and without TCML showed no significant difference (P=.628). Four crowns in group 0.2A and all of the crowns in group 0.2C failed during TCML. The fracture strength after 24 hours of the cemented 0.2 mm-thick crowns was significantly lower than that of adhesive bonded crowns. All cemented crowns provided fracture in the crown, while about 80% of the adhesively bonded crowns fractured through crown and die. CONCLUSION: 0.5 mm thick monolithic crowns possessed sufficient strength to endure physiologic performance, regardless of the type of cementation. Fracture strength of the 0.2 mm cemented crowns was too low for clinical application.
Adhesives ; Cementation ; Ceramics ; Crowns ; In Vitro Techniques ; Survival Rate ; Tooth Preparation ; Water ; Zinc

PURPOSE: . Computer-aided design and manufacturing (CAD-CAM) of implant abutments has been shown to result in surface contamination from site-specific milling and fabrication processes. If not removed, these contaminants can have a potentially adverse effect and may trigger inflammatory responses of the peri-implant tissues. The aim of the present study was to evaluate the bacterial disinfection and cleaning efficacy of ultrasonic reprocessing in approved disinfectants to reduce the microbial load of CAD-CAM abutments. MATERIALS AND METHODS. Four different types of custom implant abutments (total N = 32) with eight specimens in each test group (type I to IV) were CAD-CAM manufactured. In two separate contamination experiments, specimens were contaminated with heparinized sheep blood alone and with heparinized sheep blood and the test bacterium Enterococcus faecium. Abutments in the test group were processed according to a three-stage ultrasonic protocol and assessed qualitatively and quantitatively by determination of residual protein. Ultrasonicated specimens contaminated with sheep blood and E. faecium were additionally eluted and the dilutions were incubated on agar plates for seven days. The determined bacterial counts were expressed as colony-forming units (CFU). RESULTS: . Ultrasonic reprocessing resulted in a substantial decrease in residual bacterial protein to less than 80 µg and a reduction in microbiota of more than 7 log levels of CFU for all abutment types, exceeding the effect required for disinfection. CONCLUSION . A three-stage ultrasonic cleaning and disinfection protocol results in effective bacterial decontamination. The procedure is reproducible and complies with the standardized reprocessing and disinfection specifications for one- or two-piece CAD-CAM implant abutments.

PURPOSE: The objective of the study was to analyze the impact of cement, bonding pretreatment, and ceramic abutment material on the overall color results of CAD-CAM ceramic crowns bonded to titanium-based hybrid abutments. MATERIALS AND METHODS: For single implant restoration of a maxillary lateral incisor a total of 51 CAD-CAM-fabricated monolithic lithium disilicate crowns were fabricated and subsequently bonded onto 24 lithium disilicate Ti-base abutments, 24 zirconia Ti-base abutments and 3 resin abutment replicas as a control group.The 48 copings were cemented with three definitive and one provisional cement on both grit-blasted and non-blasted Ti-bases. The color of each restoration and surrounding artificial gingiva was measured spectrophotometrically at predefined measuring points and the CIELAB (ΔE ab ) color scale values were recorded. RESULTS: The color outcome of ceramic crowns bonded to hybrid abutments and soft tissues was affected differently by cements of different brands. Grit-blasting of Ti-bases prior to cementing CAD-CAM copings affected the color results of allceramic crowns. There was a significant difference (P = .038) for the median ΔE value between blasted and non-blasted reconstructions at the cervical aspect of the crown. Full-ceramic crowns on zirconia Ti-base abutments exhibited significantly lower ΔE values below the threshold of visibility (ΔE 1.8). In all subcategories tested, the use of a highly opaque temporary cement demonstrated the lowest median ΔE for both the crown and the artificial gingiva. CONCLUSION Various cements, core ceramic materials and airborne particle abrasion prior to bonding can adversely affect the color of Ti-base supported ceramic crowns and peri-implant soft tissue. However, zirconia CAD-CAM copings and an opaque cement can effectively mask this darkening.

The aim of this study was to evaluate the effect of controlled intraoral grinding and polishing on the roughness of full-contour zirconia compared to classical veneered zirconia. Thirty bar-shaped zirconia specimens were fabricated and divided into two groups (n=15). Fifteen specimens (group 1) were glazed and 15 specimens (group 2) were veneered with feldspathic ceramic and then glazed. Prior to grinding, maximum roughness depth (Rmax) values were measured using a profilometer, 5 times per specimen. Simulated clinical grinding and polishing were performed on the specimens under water coolant for 15 s and 2 N pressure. For grinding, NTI diamonds burs with grain sizes of 20 µm, 10 µm, and 7.5 µm were used sequentially. The ground surfaces were polished using NTI kits with coarse, medium and fine polishers. After each step, Rmax values were determined. Differences between groups were examined using one-way analysis of variance (ANOVA). The roughness of group 1 was significantly lower than that of group 2. The roughness increased significantly after coarse grinding in both groups. The results after glazing were similar to those obtained after fine grinding for non-veneered zirconia. However, fine-ground veneered zirconia had significantly higher roughness than venerred, glazed zirconia. No significant difference was found between fine-polished and glazed zirconia, but after the fine polishing of veneered zirconia, the roughness was significantly higher than after glazing. It can be concluded that for full-contour zirconia, fewer defects and lower roughness values resulted after grinding and polishing compared to veneered zirconia. After polishing zirconia, lower roughness values were achieved compared to glazing; more interesting was that the grinding of glazed zirconia using the NTI three-step system could deliver smooth surfaces comparable to untreated glazed zirconia surfaces.
Aluminum Silicates ; chemistry ; Ceramics ; chemistry ; Crowns ; Dental Materials ; chemistry ; Dental Polishing ; instrumentation ; methods ; Dental Prosthesis Design ; Dental Veneers ; Diamond ; chemistry ; Humans ; Materials Testing ; Microscopy, Electron, Scanning ; Particle Size ; Potassium Compounds ; chemistry ; Pressure ; Surface Properties ; Time Factors ; Water ; chemistry ; Yttrium ; chemistry ; Zirconium ; chemistry