Ormocer has organic-inorganic compound polymers. One of advantages of ormocer is reduced polymerization shrinkage. The purpose of this study was to compare the amount of contraction shrinkage of composite resins and ormocers. Additionally, the time of each material when there is no further change of contraction shrinkage was analysed. Four brands of composite resins (P-60, Surefil, Z-250 and Denfil) and two brands of ormocers (Definite and Admira) were used. 20 seconds, 40 seconds and 60 seconds of curing times were given. Contraction shrinkage of them were measured using a linometer for 80 seconds. The effect of material and curing time to contraction shrinkage at the time of 80 seconds was analysed by two-way ANOVA. The effect of time to contraction shrinkage was analysed by one-way ANOVA, and the time when there was no further change of the contraction shrinkage was analysed. The results are as follows : 1. P-60, Definite, Z-250 and Denfil had no further change of contraction shrinkage from the time of 20 seconds, and Surefil and Admira had no further change of contraction shrinkage from the time of 10 seconds. 2. Statistical analysis revealed volumetric shrinkage varied among material (p<0.05). No significant difference of contraction shrinkage among different curing times was found, and there was no effect of interaction between materials and curing times to contraction shrinkage. 3. Definite and Admira showed the statistically same contraction shrinkage with those of Z-250 and P-60, which is higher than that of Surefil and lower than that of Denfil (p<0.05).
Composite Resins* ; Organically Modified Ceramics* ; Polymerization ; Polymers

The purpose of this study was to evaluate the color stability of light cured composite resins according to the resin matrices. Three kinds of resin matrices such as Bis-GMA (Venus® Diamond; VD), Silorane (FiltekTM P90; P90), and Ormocer (Admira; Ad) were selected. Each of them were used to prepare 30 specimens. The initial CIE L*a*b* values were measured by means of a Spectrophotometer (NF999, Nippon Denshoku, Japan). For accelerated aging process, the specimens were immersed in a circulating water bath with distilled water at 60℃. Spectrophotometric analyses were made after immersion of 8, 16, 24, 41 days and the color difference (ΔE*) was calculated. The L* value increased compared with initial L* value. VD had the greatest L* value change and Ad had the smallest L* value change (p<0.05). Ad had the greatest a* value change and VD had the smallest a* value change (p<0.05). The b* value of P90 increased steadily in positive value (+)(p<0.05). ΔE* of Ad had the smallest value and that of P90 had the greatest change with time. According to this study, the value of light cured composite resins was increased with water sorption and color of those changed into greenish and yellowish. And according to the evaluation of color stability, Ad with Ormocer as resin matrices had the best color stability with time in oral environment and P90 with Silorane as resin matrices had the lowest color stability with time. And VD had the greatest initial ΔE*.
Aging ; Baths ; Bisphenol A-Glycidyl Methacrylate ; Composite Resins ; Diamond ; Immersion ; Organically Modified Ceramics ; Silorane Resins ; Water