OBJECTIVES: The aim of the study was to evaluate the 5-year clinical performance of occlusal carious restorations using nanofill and microhybrid composites, in combination with 3-step etch-and-rinse adhesives, in patients who were going to commence orthodontic treatment. MATERIALS AND METHODS: A total of 118 restorations for occlusal caries were conducted prior to orthodontic treatment. Occlusal restorations were performed both with Filtek Supreme XT (3M ESPE) and Filtek Z250 (3M ESPE) before beginning orthodontic treatment with fixed orthodontic bands. Restorations were clinically evaluated at baseline and at 1, 2, 3, 4, and 5-year recalls. RESULTS: None of the microhybrid (Filtek Z250) and nanofill (Filtek Supreme XT) composite restorations was clinically unacceptable with respect to color match, marginal discoloration, wear or loss of anatomical form, recurrent caries, marginal adaptation, or surface texture. A 100% success rate was recorded for both composite materials. There were no statistically significant differences in any of the clinical evaluation criteria between Filtek Z250 and Filtek Supreme XT restorations for each evaluation period. CONCLUSIONS: The composite restorations showed promising clinical results relating to color matching, marginal discoloration, wear or loss of anatomical form, recurrent caries, marginal adaptation, and surface texture at the end of the 5-year evaluation period.
Adhesives* ; Humans ; Orthodontics

PURPOSE: To evaluate the effect of prolonged sandblasting on the bond durability of dual-cure adhesive resin cement to computer-aided design and computer-aided manufacturing (CAD/CAM) restoratives. MATERIALS AND METHODS: Nano-ceramic LAVA Ultimate and hybrid-ceramic VITA Enamic CAD/CAM blocks were used for this study. Each CAD/CAM block was sectioned into slabs of 4-mm thickness for the microtensile test (µTBS) test and 2-mm thickness for the surface roughness test. Three groups were created according to the sandblasting protocols; group 1: specimens were sandblasted for 15 seconds, group 2: specimens were sandblasted for 30 seconds, and group 3: specimens were sandblasted for 60 seconds. After sandblasting, all specimens were luted using RelyX Ultimate Clicker. Half the specimens were subjected to µTBS tests at 24 hours, and the other half were subjected to tests after 5000 thermocycles. Additionally, a total of 96 CAD/CAM block sections were prepared for surface roughness tests and scanning electron microscopy (SEM) evaluations. The Mann-Whitney U test, Kruskal-Wallis one-way analysis of variance, and Dunn's post hoc test were used to compare continuous variables among the groups. RESULTS: At baseline, group 1, group 2, and group 3 exhibited statistically similar µTBS results for LAVA. However, group 3 had significantly lower µTBS values than groups 1 and 2 for VITA. After 5000 thermocycles, µTBS values significantly decreased for each block (P < .05). CONCLUSION: It is important to perform controlled sandblasting because it may affect bond strength results. Sixty seconds of sandblasting disturbs the initial µTBS values and the stability of adhesion of CAD/CAM restoratives to dual-cure adhesive resin cement for VITA Enamic.
Adhesives ; Computer-Aided Design ; Microscopy, Electron, Scanning ; Resin Cements

PURPOSE: To investigate the effect of accelerated aging on surface properties of glazed CAD/CAM resin blocks using a 2D surface profilometer and a 3D non-contact optical profilometer. MATERIALS AND METHODS: Three types of CAD/CAM resin restorative materials, LAVA Ultimate (3M ESPE, St Paul, MN, USA), VITA Enamic (Vita Zahnfabrik H. Rauter, Bad Säckingen, Germany), and Cerasmart (GC Corparation, Tokyo, Japan) were used for this study. CAD/CAM blocks were cut in 3-mm thickness slabs and divided into three groups; Group 1: control group (specimens polished with 600 grit SCI paper); Group 2: specimens sandblasted, silanized, and glazed with Optiglaze Color (GC); Group 3: glazed specimens subjected to 5000 thermocycles (n=15). The surface roughness (Ra and Rz) was evaluated using a profilometer and a 3D scanning instrument. Data were analyzed using two-way ANOVA and Tukey's post-hoc test (P < .05). RESULTS: LAVA, VITA, and Cerasmart exhibited statistically similar Ra and Rz values for each group (P>.05). For VITA and Cerasmart, the specimens in Group 1 exhibited significantly higher Ra values than Group 2 (P < .05). Group 1 (0.502 Ra), Group 2 (0.384 Ra), and Group 3 (0.431 Ra) exhibited statistically similar Ra values for LAVA (P=.062). After 5000 thermocycles, surface roughness values did not change significantly for glazed LAVA, VITA, and Cerasmart (P>.05). CONCLUSION: Glaze material Optiglaze Color makes CAD/CAM resin surfaces smooth and glazed CAD/CAM surfaces seem resistant to deterioration under 5000 thermocycles.
Aging ; Surface Properties