1.The effect of thickness and translucency of polymer-infiltrated ceramic-network material on degree of conversion of resin cements
Kubilay BARUTCIGIL ; Ulviye Şebnem BÜYÜKKAPLAN
The Journal of Advanced Prosthodontics 2020;12(2):61-66
PURPOSE:
. The aim of the present study was to determine the degree of conversion of light- and dual-cured resin cements used in the cementation of all-ceramic restorations under different thicknesses of translucent (T) and high-translucent (HT) polymer-infiltrated ceramic-network (PICN) material.
MATERIALS AND METHODS:
. T and HT PICN blocks were prepared at 0.5, 1.0, 1.5, and 2.0 mm thicknesses (n=80). Resin cement samples were prepared with a diameter of 6 mm and a thickness of 100 μm. Light-cured resin cement was polymerized for 30 seconds, and dual-cure resin cement was polymerized for 20 seconds (n=180). Fourier transform infrared spectroscopy (FTIR) was used for degree of conversion measurements. The obtained data were analyzed with ANOVA and Tukey HSD, and independent t-test.
RESULTS:
. As a result of FTIR analysis, the degree of conversion of the light-cured resin cement prepared under 1.5- and 2.0-mm-thick T and HT ceramics was found to be lower than that of the control group. Regarding the degree of conversion of the dual-cured resin cement group, there was no significant difference from the control group.
CONCLUSION
. Within the limitation of present study, it can be concluded that using of dual cure resin cement can be suggested for cementation of PICN material, especially for thicknesses of 1.5 mm and above.
2.Effects of staining liquids and finishing methods on translucency of a hybrid ceramic material having two different translucency levels.
Sebnem Ulviye BUYUKKAPLAN ; Mehmet Mustafa ÖZARSLAN ; Cağatay BARUTCIGIL ; Merve ARSLAN ; Kubilay BARUTCIGIL ; Elif Ece YOLDAN
The Journal of Advanced Prosthodontics 2017;9(5):387-393
PURPOSE: Beverages may affect the translucency of esthetic dental restorative materials. The aim of the present study was to investigate the effects of coffee and red wine on the translucency of a PICN material with two translucency levels, and finished with different methods. MATERIALS AND METHODS: 2M2 high translucent and translucent VITA Enamic hybrid ceramic blocks were investigated. Rectangular specimens with the dimensions of 12 mm × 14 mm × 2 mm were prepared. The specimens were finished and polished with different methods as suggested by the manufacturer. The translucency parameters of the specimens were evaluated before and after 24 hours, 7 days, and 28 days immersion in distilled water, coffee and red wine. Translucency parameters were measured using a portable spectrophotometer. RESULTS: At the end of 28 days, there was no statistically significant difference between the groups of specimens kept in coffee (P>.05). In the red wine groups, there was a statistically significant difference between the control group and all other groups (P<.05) at the end of 28 days. CONCLUSION: The translucency of hybrid ceramic for a restoration may not be important regarding the effects of coffee on translucency change because the specimens with different translucencies and finishing methods that were immersed to coffee had similar translucency parameters at the end of 28 days. The translucency of hybrid ceramic may be important in the case of red wine, however, since the results showed that highly translucent specimens exposed to red wine demonstrated better translucency parameters than specimens made from translucent blocks at the end of 28 days.
Beverages
;
Ceramics*
;
Coffee
;
Immersion
;
Methods*
;
Water
;
Wine
3.Effects of different surface finishing procedures on the change in surface roughness and color of a polymer infiltrated ceramic network material.
Mehmet Mustafa ÖZARSLAN ; Ulviye Sebnem BUYUKKAPLAN ; Cagatay BARUTCIGIL ; Merve ARSLAN ; Nurullah TURKER ; Kubilay BARUTCIGIL
The Journal of Advanced Prosthodontics 2016;8(1):16-20
PURPOSE: Polymer infiltrated ceramic network (PICN) materials, also called hybrid ceramics, are new materials in dental market. The manufacturer of the PICN material VITA Enamic suggests 3 different finishing procedures for this new material. In the present study, surface roughness and color differences caused from different finishing procedures of VITA Enamic were investigated. MATERIALS AND METHODS: 120 specimens were prepared in dimensions 2 x 10 x 12 mm from VITA Enamic hybrid ceramic blocks with 'high translucency' and 'translucency 2M2' shades. The specimens were divided into 8 groups. For each group, different finishing procedures suggested by the manufacturer were performed. Surface roughness values were determined by a tactile portable profilometer. Color changes were evaluated using a clinical spectrophotometer. The data were analyzed using one-way ANOVA and Tukey's post-hoc comparison. The significance level was set at alpha=0.05. RESULTS: The roughest surfaces were observed in Glaze Groups. Their surface roughness values were similar to that of the control group. Clinical Kit and Technical Kit groups did not show a statistically significant difference regarding surface roughness (P>.05). The largest color difference regarding DeltaE00 was observed in Clinical Kit finishing groups. There were also statistically significant color changes between the groups (P<.05). However, all the groups showed clinically acceptable color change (DeltaE(00)<2.25) except Clinical Kit Groups (DeltaE(00)>2.25). CONCLUSION: Within the limitations of the present study, it may be suggested that finishing the VITA Enamic restorations by Technical Kit instead of Glaze and Clinical Kit gives better clinical performance in regard to surface roughness and shade matching.
Ceramics*
;
Polymers*