Objective To explore the clinical effectiveness and safety of percutaneous vertebral augmentation with the Vessel-X bone void filling container system (Vesselplasty). Methods Three cases of fresh osteoporotic vertebral compression fracture were treated with Vesselplasty. After procedure, the pain relief, the fracture reduction, and the cement distribution in the vertebra were observed. Results All the 3 cases were treated with the unipediclar injection technique. The operative time was 45, 32 and 30 min, respectively. The hemorrhage volume was

Objective To evaluate a fast-hardening strontium-calcium phosphate scaffold using a two-step reaction in room temperature.Methods The original powder phase consisted of tetracalcium phosphate (TTCP),dicalcium phosphate anhydrous (DCPA) and strontium hydrogen phosphate (DSPA).The liquid phase consisted of 20wt％ citric acid and 12wt％ polyvinylpyrrolidone K-30.Groups were designed as Sr-0,Sr-5,Sr-10,and Sr-20,according to the molar ratios of Sr/(Sr + Ca) being 0,5％,10％,and 20％ in the powder phase,respectively.The ratio 0.5 mL/g in the liquid to solid phase was used for mixing.After the scaffold was prepared,its setting time,compression strength,phase composition and structural morphology,ions release and pH value of the substrates were analyzed.Results Addition of citric acid accelerated the setting reaction.Acceptable setting time was achieved by optimizing composition of the original powder and liquid phases.On the other hand,the compression strength,phase composition and structural morphology were not affected by addition of strontium.In addition,calcium and strontium ions were detected in the substrates,without any significant change in the pH value.Conclusion This two-step reaction can be used to prepare a fast hardening strontium-calcium phosphate scaffold in room temperature.