PURPOSE: This study investigated the effect of laser parameters and air-abrasion on the peel strength of silicon-based soft denture liner to different denture resins. MATERIALS AND METHODS: Specimens (N=180) were prepared out of three different denture base resins (Rodex, cross-linked denture base acrylic resin; Paladent, heat-cured acrylic resin; Deflex, Polyamide resin) (75 mm x 25 mm x 3 mm). A silicon-based soft denture liner (Molloplast B) was applied to the denture resins after the following conditioning methods: a) Air-abrasion (50 microm), b) Er,Cr:YSGG laser (Waterlase MD Turbo, Biolase Technology) at 2 W-20 Hz, c) Er,Cr:YSGG laser at 2 W-30 Hz, d) Er,Cr:YSGG laser at 3 W-20 Hz, e) Er,Cr:YSGG laser at 3 W-30 Hz. Non-conditioned group acted as the control group. Peel test was performed in a universal testing machine. Failure modes were evaluated visually. Data were analyzed using two-way ANOVA and Tukey's test (alpha=.05). RESULTS: Denture liner tested showed increased peel strength after laser treatment with different parameters (3.9+/-0.4 - 5.58+/-0.6 MPa) compared to the control (3.64+/-0.5 - 4.58+/-0.5 MPa) and air-abraded groups (3.1+/-0.6 - 4.46+/-0.3 MPa), but the results were not statistically significant except for Paladent, with the pretreatment of Er,Cr:YSGG laser at 3 W-20 Hz. Polyamide resin after air-abrasion showed significantly lower peel strength than those of other groups (3.1+/-0.6 MPa). CONCLUSION: Heat-cured acrylic resin, PMMA, may benefit from Er,Cr:YSGG laser treatment at 3 W-20 Hz irradiation. Air-abrasion of polyamide resins should be avoided not to impair their peel bond strengths to silicon-based soft denture liners.
Collodion ; Denture Bases ; Denture Liners ; Dentures ; Nylons ; Polymethyl Methacrylate

PURPOSE: The purpose of this study was to evaluate whether surface treatments affect the translucency of laminate veneers with different shades and thicknesses. MATERIALS AND METHODS: A total of 224 disc-shaped ceramic veneers were prepared from A1, A3, HT (High Translucent) and HO (High Opaque) shades of IPS e.max Press (Ivoclar Vivadent) with 0.5 mm and 1.0 mm thicknesses. The ceramics were divided into four groups for surface treatments. Group C: no surface treatments; Group HF: etched with hydrofluoric acid; Group SB: sandblasted with 50-microm Al2O3; and Group L; irradiated with an Er;YAG laser. A translucent shade of resin cement (Rely X Veneer, 3M ESPE) was chosen for cementation. The color values of the veneers were measured with a colorimeter and translucency parameter (TP) values were calculated. A three-way ANOVA with interactions for TP values was performed and Bonferroni tests were used when appropriate (alpha=0.05). RESULTS: There were significant interactions between the surface treatments, ceramic shades and thicknesses (P=.001). For the 0.5-mm-thick specimens there were significant differences after the SB and L treatments. There was no significant difference between the HF and C treatments for any shades or thicknesses (P>.05). For the 1-mm-thick ceramics, there was only a significant difference between the L and C treatments for the HT shade ceramics (P=.01). There were also significant differences between the SB and C treatments except not for the HO shades (P=.768). CONCLUSION: The SB and L treatments caused laminate veneers to become more opaque; however, HF treatment did not affect the TP values. When the laminate veneers were thinner, both the shade of the ceramic and the SB and laser treatments had a greater effect on the TP values.
Cementation ; Ceramics ; Dental Porcelain* ; Hydrofluoric Acid ; Resin Cements

There are some corrections in the body of the article.

Objective:To determine the effect of Lentinula edodes extract on ultraviolet (UV) A and UVB-induced changes in matrix metalloproteinase (MMP) and typeⅠprocollagen expression using human immortalized HaCaT keratinocytes. Methods:Lentinula edodes ethanol extract (LEE) was obtained by extraction with 80％ ethanol for 4 h at 80 ℃. Effect of LEE on UV-induced alteration on the expression and production of MMPs and typeⅠprocollagen in keratinocytes was investigated using ELISA, RT-PCR, and Western blotting assay. To determine the underlying mechanism of LEE-mediated effects, mitogen-activated protein kinase (MAPK) and activator protein 1 signaling pathways were analysed by Western blotting assay. Results:LEE significantly inhibited the expression of MMP-1 and MMP-9 and increased the expression of typeⅠprocollagen in UVA and UVB-irradiated HaCaT keratinocytes. The phosphorylation levels of p38 were significantly inhibited by LEE whereas it did not affect c-Jun N-terminal kinase and extracellular signal-regulated kinase phosphorylation. Suppression of p38 phosphorylation was also accompanied by downregulation of UVA and UVB-induced increase in c-Fos. Conclusions:LEE effectively inhibits the expression of MMP-1 and MMP-9 and increases typeⅠprocollagen production through the p38 MAPK/c-Fos signaling pathway in UVA and UVB-irradiated HaCaT keratinocytes. This findings suggest that Lentinula edodes may be developed as a cosmetic material to suppress UV exposure-mediated skin aging.

Objective: To investigate matrix metalloproteinases (MMP)-2 and MMP-9 inhibitory effect of Salsola komarovii Iljin, an edible halophyte with health beneficial effects. Methods: Salsola komarovii crude extracts (SKI), and solvent (n-hexane, 85% aq. MeOH, n-BuOH, and H