PURPOSE: The study compared the color change, lightness, and translucency of hybrid resin ceramics exposed to toothbrush abrasion and surface treatment. MATERIALS AND METHODS: Four hybrid ceramics [Lava Ultimate (LU), Vita Enamic (EN), Shofu HC (SH), and Crystal Ultra (CU)] were compared with a glass-ceramic (Vita Mark II) control. One hundred and twenty specimen blocks were prepared using a precision saw machine. Specimens in each material were divided into four subgroups based on the surface treatment (polishing or staining) and a storage medium (water or citric acid). Simulated tooth brushing with a mixture of 100 RDA (radioactive abrasives) with 0.3 ml distilled water was used for 3650 cycles (7300 strokes) for each specimen. Measurements for the color change, lightness, and translucency were measured after toothbrushing using a spectrophotometer. Statistical analysis compared outcomes using paired t-test, ANOVA, and Tukey post hoc test. RESULTS: The maximum color change was identified in SH (stained acid) [1.44 (0.40)], whereas the lowest was identified in EN (polished water) [0.66 (0.16)] material. The maximum and minimum loss of surface translucency was observed in SH (polished water) [12.3 (0.52)] and EN (stained acid) [6.5 (0.55)] specimens, respectively. Lastly, loss of lightness was the highest in VM (polished acid) [69 (0.95)], whereas the lowest was observed in CU (stained water) [56.7 (0.86)]. CONCLUSION The comparison presented a significant effect of toothbrush abrasion on translucency and lightness of the hybrid resin ceramics. Color change was not significantly influenced irrespective of the storage medium employed. Surface staining demonstrated the preservation and stability of color and optical properties under the influence of toothbrush abrasion and chemical trauma.

Purpose: This in-vitro study evaluated and compared the color stability of 3D-printed and conventional heat-polymerized acrylic resins following aging, mechanical brushing, and immersion in staining medium. Materials and methods: Forty disc-shaped specimens (10 mm in diameter and 3 mm thick) were prepared from two 3D-printed [DentaBASE (DB) and Denture 3D+ (D3D)] and one conventional polymethylmethacrylate (PMMA) denture materials. The specimens were thermo-cycled, subjected to mechanical brushing, and were immersed in either coffee, lemon juice, coke, or artificial saliva (AS) to simulate one and two years of oral use. Color measurements of the specimens were recorded by a spectrophotometer at baseline (T0), and after one (T1) and two years (T2) of simulation. The color changes (ΔE) were determined and also quantified according to the National Bureau of Standards (NBS) units. Descriptive statistics, followed by factorial ANOVA and Bonferroni post-hoc test (α=.05), were applied for data analysis. Results: The independent factors, namely material, staining medium, and immersion time, and interaction among these factors significantly influenced ΔE (P <.009). Irrespective of the materials, treatments, and time, the highest and the lowest mean ∆Es were observed for PMMA in lemon juice (4.58 ± 1.30) and DB in AS (0.41 ± 0.18), respectively. Regarding the material type, PMMA demonstrated the highest mean ∆E (2.31 ± 1.37), followed by D3D (1.67 ± 0.66), and DB (0.85 ± 0.52), and the difference in ΔE between the materials were statistically significant (P <.001). All the specimens demonstrated a decreased color changes at T2 compared to T1, and this difference in mean ∆E was statistically significant (P <.001). Conclusion The color changes of 3D-printed denture resins were low compared to conventional heat polymerized PMMA. All the tested materials, irrespective of the staining medium used, demonstrated a significant decrease in ∆E values over time.

Purpose: This in-vitro study evaluated and compared the color stability of 3D-printed and conventional heat-polymerized acrylic resins following aging, mechanical brushing, and immersion in staining medium. Materials and methods: Forty disc-shaped specimens (10 mm in diameter and 3 mm thick) were prepared from two 3D-printed [DentaBASE (DB) and Denture 3D+ (D3D)] and one conventional polymethylmethacrylate (PMMA) denture materials. The specimens were thermo-cycled, subjected to mechanical brushing, and were immersed in either coffee, lemon juice, coke, or artificial saliva (AS) to simulate one and two years of oral use. Color measurements of the specimens were recorded by a spectrophotometer at baseline (T0), and after one (T1) and two years (T2) of simulation. The color changes (ΔE) were determined and also quantified according to the National Bureau of Standards (NBS) units. Descriptive statistics, followed by factorial ANOVA and Bonferroni post-hoc test (α=.05), were applied for data analysis. Results: The independent factors, namely material, staining medium, and immersion time, and interaction among these factors significantly influenced ΔE (P <.009). Irrespective of the materials, treatments, and time, the highest and the lowest mean ∆Es were observed for PMMA in lemon juice (4.58 ± 1.30) and DB in AS (0.41 ± 0.18), respectively. Regarding the material type, PMMA demonstrated the highest mean ∆E (2.31 ± 1.37), followed by D3D (1.67 ± 0.66), and DB (0.85 ± 0.52), and the difference in ΔE between the materials were statistically significant (P <.001). All the specimens demonstrated a decreased color changes at T2 compared to T1, and this difference in mean ∆E was statistically significant (P <.001). Conclusion The color changes of 3D-printed denture resins were low compared to conventional heat polymerized PMMA. All the tested materials, irrespective of the staining medium used, demonstrated a significant decrease in ∆E values over time.