PURPOSE: The purpose of this study was to investigate the effect of size and shape of retention element on the bond strength of indirect composite resin and metal. MATERIAL AND METHOD: The metal disk specimens, each 6mm in diameter, were cast from Cr-Co alloy. They were divided into 8 groups by applied retention element: retention bead group B2 (phi 0.2mm), B4 (phi 0.4mm), B6 (phi 0.6mm), B8 (phi 0.8mm), retention crystal group C2 (0.2mm), C5 (0.5mm), C8 (0.8mm), and sandblasting group SB (110micrometer Al2O3 blasting) as control. Eighty-eight metal specimens were veneered with TESCERA(R) Indirect resin system. One specimen of each group was sectioned and the resin-metal bonding pattern at the interface was observed under measuring microscope. Other specimens were then tested for tensile bond strength on an Instron universal testing machine at a crosshead speed of 2mm/min. RESULTS: 1. Compared to sandblasting, beads or crystals increased the resin-metal bond strength (P<.05). 2. 0.2mm retention crystals were most effective in improving the resin-metal bond strength (P<.05). 3. 0.2mm beads showed the highest bond strength among retention bead groups, but there was no statistically significant difference (P>.05). 4. Retention crystals tend to be higher in bond strength than retention beads due to wider surface area. 5. The larger retention element, the larger the undercut for the mechanical retention, but the gap at resin-metal interface was also increased. CONCLUSION: Within the limitations of this study, 0.2mm retention crystals were most effective in improving the resin-metal bond strength.
Alloys

PURPOSE: The object of this study was to determine if the low-priced alloy and metal UCLA abutment could be available for manufacturing bar-retained framework of implant prosthesis. MATERIALS AND METHODS: Bar structure was classified into 4 groups, The specimen of group 1 and 2 were based on casting high noble metal alloys and noble metal alloys with gold UCLA abutment. The specimen of group 3 and 4 were based on casting noble metal alloys and base metal alloys with metal UCLA abutment. Cast bar structure was installed in an acrylic resin model and only the screw on the hexed abutment side was tightened to 20 Ncm. On the opposite side, vertical discrepancy was measured with stereo microscope from front, back, and lateral side of the implant-abutment interface. One-way ANOVA was performed to analyze the marginal fit discrepancy. RESULTS: One-way ANOVA test showed significant differences among all groups (P<.05) except for Group 1 and 3. Among them, difference between Group 1 and 2 was noticeable. Measured vertical discrepancies were all below 70 microm except to Group 2. CONCLUSION: Base metal alloy and metal UCLA abutment could be used as an alternative to high-priced gold alloy for implant bar-retained framework.
Alloys

It was the purpose of this study to analyze and compare the mechanical properties of orthodontic open coil springs. Four variable factors were presented - wire diameter (.008", .009", .010"), lumen size (.030", .032", .036"), arch wire size and shape (.016" round, .016" x .022" rect.) and alloy type (HiT II, Elgiloy, Sentalloy). The total 104 specimens were divided into 13 groups, and compression test was performed on an Instron test machine. The load-deflection curve of each open coil spring was obtained, from which, the load-deflection relations, stiffnesses, percent recoveries were computed statistically. The results were obtained as follows: 1. When the lumen size of the coil spring remained constant, stiffness and percent recovery increased as the wire diameter increased. 2. When the wire diameter of the coil spring remained constant, stiffness and percent recovery decreased as the lumen size increased. 3. The effect of size and shape of arch wire on the coil spring was not statistically significant. 4. In alloy types, stiffness was the greatest in HiT II (55.21), Elgiloy (42.61) and Sentalloy (7.74) in that order. Sentalloy exhibited superior percent recovery and long range of action.
Alloys

PURPOSE: The aim of this study was to evaluate the effect of metal primers on the bonding of dental alloys and veneer resin. Polyvinylpyrrolidone solution's tarnish effect on bonding strength was also investigated. MATERIALS AND METHODS: Disk-shape metal specimens (diameter 8 mm, thickness 1.5 mm) were made from 3 kinds of alloy (Co-Cr, Ti and Au-Ag-Pd alloy) and divided into 4 groups per each alloy. Half specimens (n=12 per group) in tarnished group were immersed into polyvinylpyrrolidone solution for 24 hours. In Co-Cr and Ti-alloy, Alloy Primer (MDP + VBATDT) and MAC-Bond II (MAC-10) were applied, while Alloy Primer and V-Primer (VBATDT) were applied to Au-Ag-Pd alloys. After surface treatment, veneering composite resin were applied and shear bond strength test were conducted. RESULTS: Alloy Primer showed higher shear bond strength than MAC-Bond II in Co-Cr alloys and Au-Ag-Pd alloy (P<.05). However, in Ti alloy, there was no significant difference between Alloy Primer and MAC-Bond II. Tarnished Co-Cr and Au-Ag-Pd alloy surfaces presented significantly decreased shear bond strength. CONCLUSION: Combined use of MDP and VBATDT were effective in bonding of the resin to Co-Cr and Au-Ag-Pd alloy. Tarnish using polyvinylpyrrolidone solution negatively affected on the bonding of veneer resin to Co-Cr and Au-Ag-Pd alloys.
Alloys ; Dental Alloys* ; Povidone

The purpose of this study was to compare the casting problem and corrosion behavior in two types of HL Hexed abutments of the Steri-Oss system : gold/plastic coping and gold coping. The anodic Polarization behavior, the galvanic corrosion between abutments and Type III gold alloys, before and after casting were analyzed, and the crevice corrosion of casting samples was analyzed with the CPPT test and the SEM. The results are as follows ; 1. Anodic polarization behavior of samples ; Before casting, gold/plastic coping and gold coping was shown to have a similar corrosion patterns. TypeIII casting gold alloy was shown to have a lower corrosion potential and passivation film. Corrosion potential of the case of gold/plastic coping after casting was higher than that of gold coping, but the region of passivation film for gold/plastic coping was smaller than that of gold coping. 2. Galvanic corrosion behavior of samples ; Contact current density between casting gold alloys and gold/plastic before casting was higher than that between gold coping and casting gold alloy. Galvanic corrosion of samples after casting was shown to have similar contact current density. 3. Crevice corrosion behavior of samples ; Crevice corrosion resistance of casting sample using gold coping was lower than that of casting sample using gold/plastic coping, and a severe corrosion pattern was observed at the abutment-casting gold alloy interface by the SEM.
Alloys* ; Corrosion* ; Gold Alloys

This study was conducted to evaluate the tensile bond strength by bonding the dental bracket with Super-bond after treating the surface of dental Nickel-Chromium alloy with sandblasting, sandblasting & tin-plating, respectively, and tin-plating. 10 pieces of Nickel-Chromium alloys with brackets bonded with Super-bond without their surface treatment were sampled as a control group, 20 pieces of Nickel-Chromium alloy brackets bonded with Super-bond after treating them with sandblasting as group I, 20 pieces of Nickel-Chromium alloys tin-plated and bonded with Super-bond after sandblasting as group II, and then 20 pieces of alloys with brackets bonded with Super-bond after tin-plating as group III. The result of those examination and comparison is summarized as follows: 1. Group I showed the mean tensile bond strength of 14.41+/-2.24MPa which was highest among 4 groups, followed by group III( 13.59+/-L51MPa ), group II( 12.27+/-1.45MPa ), and control group( 10.50+/-1.57MPa ), respectively. However, it was shown that them was no statistically significant difference between group I and III, group III and II, and group II and control group( P>005 ). 2. The main failure pattern of those brackets showed that 70% of the control group had an adhesive failure at the bracket Superbond interface, and 30% at the Nickel-Chromium alloy-Superbond interface, while other groups did the adhesive failure at the bracket-Superbond interface. 3. When examined under SEM, it was shown that adhesives were mostly attached to the surface of the Nickel-Chromium alloy for all groups while a considerable quantity of adhesives were attached to the bracket base. Then, those samples treated only with sandblasting showed the most even and remarkable roughness of their surface.
Adhesives ; Alloys* ; Chromium Alloys

OBJECTIVES: The purpose of this study was to compare the maximum screw-in forces generated during the movement of various Nickel-Titanium (NiTi) file systems. MATERIALS AND METHODS: Forty simulated canals in resin blocks were randomly divided into 4 groups for the following instruments: Mtwo size 25/0.07 (MTW, VDW GmbH), Reciproc R25 (RPR, VDW GmbH), ProTaper Universal F2 (PTU, Dentsply Maillefer), and ProTaper Next X2 (PTN, Dentsply Maillefer, n = 10). All the artificial canals were prepared to obtain a standardized lumen by using ProTaper Universal F1. Screw-in forces were measured using a custom-made experimental device (AEndoS-k, DMJ system) during instrumentation with each NiTi file system using the designated movement. The rotation speed was set at 350 rpm with an automatic 4 mm pecking motion at a speed of 1 mm/sec. The pecking depth was increased by 1 mm for each pecking motion until the file reach the working length. Forces were recorded during file movement, and the maximum force was extracted from the data. Maximum screw-in forces were analyzed by one-way ANOVA and Tukey's post hoc comparison at a significance level of 95%. RESULTS: Reciproc and ProTaper Universal files generated the highest maximum screw-in forces among all the instruments while M-two and ProTaper Next showed the lowest (p < 0.05). CONCLUSIONS: Geometrical differences rather than shaping motion and alloys may affect the screw-in force during canal instrumentation. To reduce screw-in forces, the use of NiTi files with smaller cross-sectional area for higher flexibility is recommended.
Alloys ; Pliability

No abstract available.
Alloys* ; Joints*

The effects of pretreatment of Co-Cr alloy, including two adhesive primers that contain either MDP or MAC-10, and silicoating on the bond. The results obtained as follows : Strength of 4-META/MMA-TBB resin were investigated using FT-IR SEM, and EDAX. in the SEM observation of surface morphologies, the sandblasted specimen exibited a very rough surface, whereas the surfaces of the two groups primed with either MDR or MAC-10 were covered with a layer of primer, and the surface morphology of the silicoated specimen remained almost the same after sandblasting. Before the thermocycling tests, the group treated with MDP demonstrated the highest mean tensile bond strength and the sandblasted group showed the lowest bond strength. After 20,000 themocyling, the mean tensile bond strength of the sandblasted group exhibited a 50% reduction in bond strength, while the other showed a 20~30% reduction. Observation of the metal-resin interface revealed that in all groups the resin permeated the rough surface formed by sandblasting thereby producing a mechnical bond between the metal and the resin, It was also found that thermocycling resulted in a gap formation at the metal-resin interface of the specimens, and the sandblasted group exhibited a larger gap width than the other groups. in fracture mode, all specimens indicated a cohesive fracture within the resin before thermocycling. However, thermocyling produced adhesive failure at the edge of the resin-metal interface in most specimens, The sandblasted group, which exhibited the lowest bond strength after thermocycling, also demonstrated the largest area of adhexive failure.
Adhesives ; Alloys*

The quasi-conformation therapy was performed to get a homogeneous dose distributions for irregeular shaped tumor lesion by using the arc moving beam and beam modifying filer which was made by cerrobend alloy (p=9.4g/cc) metal. In our dose calcuation programme, it was fundmentally based on Clarkson's method to calcuate the irregular multi-step block field in rotation therapy. In this study, the expected relative depth doses under multipartial attenuator agree well with measured data at same plane. The results of comparison the dose computation with that of TLD measurement are very closed within +/-5% uncertainties in the irradiation to phantom with quasi-comformation method. And it has shown that irregular typed multi-step filter can be applied to quasi-conformation therapy in high energy radiation plannings.
Alloys ; Radiotherapy*