Comparative study of flexural strength of temporary restorative resin according to surface polishing and fabrication methods
10.14368/jdras.2021.37.1.16
- Author:
Jae-Hun LIM
1
;
Jae-In LEE
Author Information
1. Department of Prosthodontics, College of Dentistry, Wonkwang University, Iksan, Republic of Korea
- Publication Type:Original Article
- From:Journal of Dental Rehabilitation and Applied Science
2021;37(1):16-22
- CountryRepublic of Korea
- Language:English
-
Abstract:
The purpose of this study is to investigate the effect of surface polishing and fabrication method on the flexural strength of temporary restorative resin. Materials and Methods: Each of four fabrication methods was used to make 30 temporary restorative resin specimens and the specimens were divided into two groups depending on whether they were polished by mechanical polishing. Specimens were stored in 37°C thermostat for 24 hours. Flexural strength was measured using a universal testing machine (UTM). The data obtained through the experiment were analyzed with Two-way ANOVA, Tukey’s HSD test and Paired t-test. Results: CAD/CAM milling group showed the highest flexural strength regardless of surface polishing. In decreasing order, the flexural strength of the other fabrication method group was as follows SLA 3D printing, DLP 3D printing, and Conventional method group. Conclusion: Surface polishing did not affect flexural strength of the temporary restorative resin (P > 0.05). However, there were statistically significant differences in flexural strength depending on fabrication method (P < 0.05).