Comparison of capsule type resin modified glass ionomer porosity according to mixing methods
10.14368/jdras.2021.37.4.217
- Author:
Jung-min KIM
1
;
Jin-Woo KIM
;
Kyung-Mo CHO
;
Yoon LEE
;
Eung-Hyun KIM
;
Se-Hee PARK
Author Information
1. Department of Conservative Dentistry, College of Dentistry, Gangneung-Wonju National University, Gangneung, Republic of Korea
- Publication Type:Original Article
- From:Journal of Dental Rehabilitation and Applied Science
2021;37(4):217-224
- CountryRepublic of Korea
- Language:English
-
Abstract:
Purpose:The purpose of this study was to evaluate the porosity of resin modified glass ionomer (RMGI) by different mixing methods.
Materials and Methods:Five specimens were prepared for each groups according to capsules and mixing methods. Two RMGI capsule and two mixing machines were used for this study. One resin-modified glass ionomer cement is Fuji II LC (F2LC) and the other is Photac Fil Quick Aplicap (PFQ). For Mixing of RMGI capsule, Rotomix using rotating motion and CM-II using shaking motion were used. After measuring height, radius and mass of specimens, Density was calculated. And porosity was measured using micro-computed tomography (micro-CT). All data were statistically analyzed using T-test, two-way ANOVA to compare between groups at 95% significance level to evaluate the affect of capsule and mixing method on the porosity.
Results:The porosity was observed in all specimens generally. And there is significant differece between porosities according to RMGI capsule and Mixing method. The porosity of PFQ was lower than that of F2LC and the porosity of Rotomix was lower than that of CM-II. Conclusion: There was a difference of porosity according to kind of capsules and mixing methods. When using same capsule, less porosity was observed on PFQ than F2LC. When using same mixing mehod, less porosity was observed on Rotomix than CM-II. Using mixing machine of same coporation as that of RMGI capsule did not lead to lower porosity. Therefore, Selecting optimal mixing machine is important.