Preparation and in vitro release study of ligustrazine pamoate sustained-release nanosuspension
10.7501/j.issn.0253-2670.2020.03.010
- Author:
Hong-Yi ZHUO
1
Author Information
1. College of Pharmacy, Chengdu University of Traditional Chinese Medicine
- Publication Type:Journal Article
- Keywords:
In vitro release characteristics;
Insoluble salt;
Ligustrazine;
Miniaturized medium grinding method;
Nanosuspension;
Orthogonal experiment;
Pamoate;
Sustained release
- From:
Chinese Traditional and Herbal Drugs
2020;51(3):616-624
- CountryChina
- Language:Chinese
-
Abstract:
Objective: To prepare ligustrazine pamoate (Lig-PAM) sustained-release nanosuspension (Lig-PAM-NSps) and determine its in vitro release characteristics. Methods: Lig-PAM was prepared by hydrophobic salt formation method and its physicochemical properties were characterized. Then, Lig-PAM-NSps was prepared by miniaturized medium grinding method. The prescription and preparation process of Lig-PAM-NSps were optimized by the single factor and orthogonal experiment with average particle size, polydispersity index (PDI) and stability coefficient (SI) as indicators. Lig-PAM-NSps was characterized, and its stability and in vitro release was also investigated. Results: The compound ratio of Lig-PAM prepared by Lig and PAM in the amount of 1:1 was (97.48 ± 0.04)%. Compared with Lig, the solubilities of Lig-PAM in water and simulated body fluids were decreased by 95.50% and 77.39%, respectively. Fourier transform infrared spectroscopy (FT-IR) and X-ray powder diffraction (XRD) showed that the Lig and PAM formed Lig-PAM. The optimum prescription size of Lig-PAM-NSps was (585 ± 5) nm, PDI was (0.328 ± 0.015) and SI was (0.928 ± 0.012). The scanning electron microscopy (SEM) showed that Lig-PAM-NSps was spherical with uniform size distribution, and the particle size was about 600 nm and its physical stability was good within 60 d. The results of in vitro release showed that Lig-PAM-NSps had obvious sustained-release effect compared with Lig solution within 48 h, and showed the first-order release characteristics [ln(1-Q) = 0.153 67 t + 80.458 14, r = 0.998 26]. Conclusion: The preparation progress of Lig-PAM-NSps is stable and can release Lig slowly in vitro.