The effects of different surface treatments on the shear bond strengths of two dual-cure resincements to CAD/CAM restorative materials
10.4047/jap.2020.12.4.189
- Author:
Nurullah TURKER
1
;
Ulviye Şebnem BUYUKKAPLAN
;
Ebru Kaya BAŞAR
;
Mehmet Mustafa ÖZARSLAN
Author Information
1. Akdeniz University Faculty of Dentistry, Department of Prosthodontics, Antalya, Turkey
- Publication Type:Original Article
- From:The Journal of Advanced Prosthodontics
2020;12(4):189-196
- CountryRepublic of Korea
-
Abstract:
. The aim of the present study was to investigate the effects of surface treatments on the bond strengths between polymer-containing restorative materials and two dual-cure resin cements. MATERIALS AND METHODS.In the present study, rectangular samples prepared from Lava Ultimate (LU) and Vita Enamic (VE) blocks were used. The specimen surfaces were treated using CoJet sandblasting, 50 μm Al2O3 sandblasting, % 9 HF (hydrofluoric) acid, ER,Cr:YSGG laser treatment, and Z-Prime. Dual-cure resin cements (TheraCem and 3M RelyX U 200) were applied on each specimen’s treated surface. A micro-tensile device was used to evaluate shear bond strength. Statistical analysis was performed using the SAS 9.4v3. RESULTS. While the bond strengthusing TheraCem with LU or VE was not statistically significant (P=.164), the bond strength using U200 with VE was statistically significant (P=.006). In the TheraCem applied VE groups, Z-Prime and HF acid were statistically different from CoJet, Laser, and Sandblast groups. In comparison of TheraCem used LU group, there was a statistically significant difference between HF acid and other surface treatments. CONCLUSION. The bondingperformance between the restorative materials and cements were material type-dependent and surface treatment had a large effect on the bond strength. Within the limitations of the study, the use of both U200 and TheraCem may be suggested if Z-prime was applied to intaglio surfaces of VE. The cementation of LU using TheraCem is suitable after HF acid conditioning of the restoration surfaces.