Effect of two kinds of materials on the prevention of early erosive enamel wear
10.3760/cma.j.issn.1002-0098.2019.07.004
- VernacularTitle: 渗透树脂与树脂粘接剂预防牙釉质早期酸蚀性磨损的效果评价
- Author:
Yunbing WU
1
;
Hui GU
;
Lijuan HUANG
;
Xiaoping LUO
;
Jie YANG
Author Information
1. Department of Prosthodontics, Nanjing Stomatological Hospital, Medical School of Nanjing University, Nanjing 210008, China
- Publication Type:Journal Article
- Keywords:
Tooth wear;
Acid etching, dental;
Composite resins
- From:
Chinese Journal of Stomatology
2019;54(7):450-455
- CountryChina
- Language:Chinese
-
Abstract:
Objective:To investigate the preventive effect of resin infiltration and adhesive on early erosive enamel wear.
Methods:Orthodontic reduction premolars collected from Central Laboratory of Nanjing Stomatological Hospital, Medical School of Nanjing University were used to prepare 70 specimens. Forty samples were divided into eight groups (n=5) and treated with different conditions (pH=1.6, 2.4, 3.2 or 4.0 hydrochloric acid solution, etching time was 30 or 60 s), and the conditions for obtaining early erosive enamel samples were selected. Based on this procedure, thirty early erosive enamel samples were made and divided into three groups: control group, resin infiltration group, and adhesive group. And the treatment of 30 days acid abrasion cycle was carried out. Confocal microscopy was used to measure the thickness changes of enamel or material before and after cycle.
Results:Early erosive enamel samples was obtained when pH was 4.0 and etching time was 60 s. After 30 days cycle, the wear of enamel was (29.71±6.72) μm in control group, (5.60±2.24) μm in resin infiltration group and (2.89±1.03) μm in adhesive group. In infiltration group and adhesive group, lower enamel was not affected by the cycle, and the material loss ratios of the infiltration resin group and adhesive group were 0.41±0.14 and 0.29±0.13, respectively. The ratio of material loss was not significantly different (P>0.05). But infiltration group lost (12.95±2.22) μm of enamel during the application of the material.
Conclusions:Resin infiltration and adhesive have the same short-term protective effect against early erosive enamel wear. Adhesive has less damage to enamel and better effect.