BackgroundPaclitaxel (PTX) could inhibit the growth of fibroblasts, which occurs in proliferative cholangitis and leads to biliary stricture. However, its use has been limited due to poor bioavailability and local administration for short time. This study designed and synthesized a new PTX-conjugated chitosan film (N-succinyl-hydroxyethyl chitosan containing PTX [PTX-SHEC]) and evaluated its safety and efficiency using in vivo and in vitro experiments.

Methods:The SHEC conjugated with PTX was confirmed by nuclear magnetic resonance (NMR) and Fourier-transform infrared spectroscopy (FT-IR) measurements. Drug releases in vitro and in vivo were determined using high-performance liquid chromatography. Cell viability in vitro was measured using 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide. Rabbit biliary stricture model was constructed. All rabbits randomly divided into five groups (n = 8 in each group): the sham-operated rabbits were used as control (Group A), Groups B received laparotomies and suture, Group C received laparotomies and covered SHEC suture without the PTX coating, Group D received laparotomies and covered PTX-SHEC suture, and Group E received laparotomies and 1000 μmol/L PTX administration. Liver function tests and residual dosage of PTX from each group were measured by enzyme-linked immunosorbent assay. Histological data and α-smooth muscle actin (SMA) immunohistochemical staining of common bile duct were examined.

Results:NMR and FT-IR indicated that PTX was successfully introduced, based on the appearance of signals at 7.41-7.99 ppm, 1.50 ppm, and 1.03 ppm, due to the presence of aromatic protons, methylene protons, and methyl protons of PTX, respectively. No bile leak was observed. The PTX-conjugated film could slowly release PTX for 4 weeks (8.89 ± 0.03 μg at day 30). The in vitro cell viability test revealed significantly different levels of toxicity between films with and without PTX (111.7 ± 4.0% vs. 68.1 ± 6.0%, P < 0.001), whereas no statistically significant difference was observed among the three sets of PTX-contained films (67.7 ± 5.4%, 67.2 ± 3.4%, and 59.1 ± 6.0%, P > 0.05). Histological examinations revealed that after 28 days of implantment, Groups D and E (but not Group C) had less granulation tissue and glandular hyperplasia in the site of biliary duct injury than Group B. The pattern was more obvious in Group D than Group E. Less α-SMA-positive cells were found in tissue from Groups D and E. Comparing with Group E, the liver function was improved significantly in Group D, including total bilirubin (2.69 ± 1.03 μmol/L vs. 0.81 ± 0.54 μmol/L, P = 0.014), alanine aminotransferase (87.13 ± 17.51 U/L vs. 42.12 ± 15.76 U/L, P = 0.012), and alkaline phosphatase (60.61 ± 12.31 U/L vs. 40.59 ± 8.78 U/L, P < 0.001).

ConclusionsPTX-SHEC film effectively inhibites the myofibroblast proliferation and extracellular matrix over-deposition during the healing process of biliary reconstruction. This original film might offer a new way for reducing the occurrence of the benign biliary stricture.