Micromorphometric change of implant surface conditioned with Tetracycline-HCl: HA and Etched surface.
10.5051/jkape.2006.36.3.731
- Author:
Ju Young HAN
1
;
Joon Bong PARK
;
Young Hyuk KWON
;
Yeek HERR
;
Jong Hyuk CHUNG
Author Information
1. Department of Periodontology, School of Dentistry, Kyung Hee University, Seoul, Korea. jbpark@khu.ac.kr
- Publication Type:Original Article
- Keywords:
Micromorphometric change;
tetracycline-HCI;
HA-coated surface;
etched surface
- MeSH:
Animals;
Comb and Wattles;
Honey;
Titanium
- From:The Journal of the Korean Academy of Periodontology
2006;36(3):731-744
- CountryRepublic of Korea
- Language:Korean
-
Abstract:
The present study was performed to evaluate the effect of tetracycline-HCl on the change of implant surface microstructure according to application time. Implant with pure titanium machined surface, HA-coated surface and dual acid etched surface were utilized. Implant surface was rubbed with 50mg/ml tetracycline-HCL solution for 1/2min., 1min., 1 1/2min., 2min., and 2 1/2min. respectively in the test group. Then, specimens were processed for scanning electron microscopic observation. The results of this study were as follows. 1. Both test and control group showed a few shallow grooves and ridges in pure titanium machined surface implants. There were not significant differences between two groups. 2. In HA-coated surfaces, round particles were deposited irregularly. The roughness of surfaces conditioned with tetracycline-HCL was lessened and the cracks were increased relative to the application time. 3. The etched surfaces showed the honey comb structures. The surface conditioning with tetracycline-HCl didn't influence on its micro-morphology. In conclusion, the detoxification with 50mg/ml tetracycline-HCl must be applied respectively with different time according to various implant surfaces.