Study of adhesive characteristics of two kinds of orthodontical light-curing adhesive agents
- VernacularTitle:两种光固化正畸黏结剂的黏结性能评价
- Author:
Weiwei LIN
;
Jinwu CHEN
;
Xinyi ZHAO
- Publication Type:Journal Article
- Keywords:
Orthodontic bonding;
Shear bond strength;
Adhesive remnant index
- From:
Journal of Practical Stomatology
1995;0(04):-
- CountryChina
- Language:Chinese
-
Abstract:
Objective: To investigate the adhesive characteristics of two kinds of light-curing resin that was used to bond teeth and orthodontics brackets. Methods: A total of 60 premolar teeth were randomly divided into six groups, and brackets were bonded according to the manufacturers' instructions. In group A1, A2 and A3, the teeth were prepared using 100 ml/L polyacrylic acid, and the brackets were bonded using Fuji Ortho LC. In group B1, B2 and B3, the teeth were using self-etching primer, and the brackets were bonded using Transbond Plus Self Etching Primer (TPSEP). After 30 min and 24 h under room temperature and received cold-heat cycle treatment respectively, bond strength was measured using a testing instrument (2000S, Lloyds Instruments, Fareham, England) at a speed of 1 mm/min, and the residual adhesive was quantified using a stereomicroscope. The adhesive interface was observed by scanning electron microscope. Results: The bond shear strength of TPSEP and Ortho Glass LC are more than 5 MPa. The bond shear strength of TPSEP is stronger than that of Ortho Glass LC after 24 h. However,The adhesive remnant index (ARI)of TPSEP is higher than that of Ortho Glass LC. Conclusion: Transbond Plus Self Etching Primer and Ortho Glass LC can satisfy the clinic need of orthodontics.