A comparative study on the mechanical properties of flexible denture materials containing different fluoride concentrations
10.3969/j.issn.2095-4344.2017.30.009
- VernacularTitle:不同含氟比例弹性义齿材料的力学性能比较
- Author:
yu Zhen TANG
1
;
Zhe ZHANG
;
yi Wei ZHANG
Author Information
1. 桂林医学院第二附属医院
- From:
Chinese Journal of Tissue Engineering Research
2017;21(30):4805-4810
- CountryChina
- Language:Chinese
-
Abstract:
BACKGROUND: Long-term use of flexible denture prosthesis will increase the incidence of caries and periodontal disease, and partial denture stomatitis. The addition of fluoride in the prosthesis material can prevent and reduce the incidence of these diseases. Currently, increasing research addresses the addition of fluoride into dental materials at home and abroad, but little is reported on the addition of sodium monofluorophosphate (Na2(PO3)F into flexible denture materials and on the relevant mechanical performance.OBJECTIVE: To evaluate the mechanical properties of flexible denture materials containing different fluoride concentrations.METHODS: Totally 180 elastic denture samples were made at the three different sizes of 80 mm×51 mm×1 mm (n=60), 20 mm×5 mm×5 mm (n=60), 25 mm×2 mm×2 mm (n=60). Then, elastic denture samples containing Na2(PO3)F 0 (control), 3%, 5%, 10%, 15%, 20% were prepared in each size groups. The tensile strength, flexural strength and Shore A hardness of the samples were tested.RESULTS AND CONCLUSION: When the mass ratio of fluoride was up to 10%, the tensile strength and flexural strength reduced a little (P > 0.05). When the mass ratio of fluoride was up to 15%, the tensile strength and flexural strength were significantly lower than those of non-fluoride samples (P < 0.05). When the mass ratio of fluoride was up to 20%, the tensile strength, flexural strength and Shore A hardness were significantly lower than those of non-fluoride samples (P < 0.05). To conclude, Na2(PO3)F content has a significant effect on the tensile strength, flexural strength and Shore A hardness, and 10% is the best proportion of Na2(PO3)F. The mechanical properties of fluoride-containing flexible denture materials will be changed if the mass ratio of fluoride is higher than 10%.