Evaluation of Biodegradation and Osteosynthesis in CaO-SiO2-B2O3 Glass-ceramics by Posterolateral Fusion of Rabbit Lumbar vertebrae.
10.4055/jkoa.2003.38.6.612
- Author:
Jae Hyup LEE
1
;
Jeong Hyun HA
;
Dong Ho LEE
;
Bong Soon CHANG
;
Hyun Seung RYU
;
Jun Hyuk SEO
;
Kug Sun HONG
;
Hwan KIM
;
Choon Ki LEE
Author Information
1. Department of Orthopedic Surgery, Seoul National University College of Medicine, Seoul, Korea. choonki@plaza.snu.ac.kr
- Publication Type:Original Article
- Keywords:
Spine fusion;
CaO-SiO2-B2O3 glass-ceramics;
Hydroxyapatite;
Tricalcium phosphate;
Biodegradation;
Osteoconductivity;
Bone replacement
- MeSH:
Animals;
Bone Regeneration;
Bone Substitutes;
Durapatite;
Lumbar Vertebrae*;
Polymers;
Porifera;
Rabbits;
Spinal Fusion;
Tensile Strength;
Transplants
- From:The Journal of the Korean Orthopaedic Association
2003;38(6):612-618
- CountryRepublic of Korea
- Language:Korean
-
Abstract:
PURPOSE: To compare the biodegradation and osteoconduction properties of CaO-SiO2-B2O3 glass-ceramics (CS10B), hydroxyapatite(HA), and tricalcium phosphate (TCP). MATERIALS AND METHODS: Porous CS10B implants were prepared by the polymer sponge method. Single-level posterolateral spinal fusions were performed on thirty rabbits. The animals were divided into three groups by implant material: HA, TCP and CS10B. Radiographs were performed every two weeks. All animals were sacrificed 12 weeks after surgery. The proportion of the area occupied by the ceramicsin the final over the initial radiographs was calculated. Uniaxial tensile strength was determined from 7 cases in each group. RESULTS: The proportion of the area occupied by HA (88.7+/-16.1%) was significantly higher than the others (p<0.05), and the proportion of the area occupied by CS10B (28.2+/-9.3%) was significantly lower than those of HA and TCP (37+/-9.6%) (p<0.05). The mean values of the tensile strengths of HA (191.4+/-33.5 N) and CS10B (182.7+/-19.9 N) were significantly higher (p<0.05) than those of TCP (141.1+/-28.2 N). CONCLUSION: CS10B had similar tensile strengths of the fusion masses as HA, however, it degraded more rapidly than HA or TCP. These findings suggest CS10B grafts as possible bone replacement materials.