Orthodontic bracket shear bond strength to ND:YAG laser and ER:YAG laser irradiated enamel.
- Author:
Seung Hoon CHOI
1
;
Won Sik YANG
Author Information
1. Department of Orthodontics, College of Dentistry, Seoul National University, Korea.
- Publication Type:Original Article
- Keywords:
Nd:YAG LASER;
Er:YAG LASER;
SHEAR BOND STRENGTH
- MeSH:
Bicuspid;
Dental Enamel*;
Humans;
Orthodontic Brackets*;
Tooth
- From:Korean Journal of Orthodontics
1997;27(1):141-155
- CountryRepublic of Korea
- Language:Korean
-
Abstract:
The purpose of thisstudy was to evaluate the effectiveness of the Nd:YAG laser and the Er:YAAG laser on etching enamel for direct bonding of orthodontic bracket. The advantages of laser etching rather than conventional acid etching are to reduce the subsurface demineralization rate, to inhibit the spillage of acid onto uninvolved ""its of enamel, and to save the clinical manipulation time involving drying, trashing and drying again. 189 freshly extracted human premolars were prepared for this research. 165 out of them were divided into 11 groups of 15 teeth. One group was acid etching and the rest groups were irradiated with Nd:YAG laser by four different energy levels(1100mj 10pps, 100mj 20pps, 150mj 20pps, 200mj 20pps) and with Er:YAG laser by six different energy levels(60mj 5pps, 60mj 10pps, 100mj 10pps. 200mj 10pps, 200mj l5pps, 400mj 10pps). Shear bond strength was tested with Instron after 24 hours, one week, and three weeks. Twenty-four out of 189 teeth were divided into twelve groups untreated control, acid etching, and ten laser irradiation subgroups. And the ultrastructural enamel surfaces of each group were observed with scanning electron microscope. The results were as follows; 1. The means and the standard deviations of shear bond strength of Nd:YAG and Er:YAU laser irradiation by different energy levels were obtained. 2. Shear bond strengths of Er:YAG laser irradiation groups were higher than those of Nd:YAG laser irradiation groups at the identical energy level. 3. Maximum bond strengths was achieved at the energy of I50mj, 2Opps in Nd:YAG laser irradiation groups or 6Omj, 10pps in Er:YAG laser irradiation groups. 4. It was acceptible for direct bonding to irradiate lb0mj 20pps with Nd:YAG laser or to irradiate 60mj 10pps with Er:YAG laser considering the results of shear bond strength tests and SEM obsesvation.