A change of shear bond strength of orthodontic resin adhesives under water immersion.
- Author:
Je Jun LEE
1
;
Jong Chul KIM
Author Information
1. Department of Orthodontics, College of Dentistry, Chonnam National University, Korea.
- Publication Type:Original Article
- Keywords:
water immersion;
resin adhesive;
shear bond strength;
ARI
- MeSH:
Adhesives*;
Bicuspid;
Immersion*;
Incidence;
Water*
- From:Korean Journal of Orthodontics
1998;28(5):783-789
- CountryRepublic of Korea
- Language:Korean
-
Abstract:
The purpose of this study was to evaluate the changes of shear bond strengths and failure patterns in orthodontic resin adhesives according to the water immersion time. Metal brackets were bonded to the specimens involving the premolars with chemical-cured(Concise(R)) and light-cured(Transbond(R)) adhesives. The shear bond strength was measured on universal testing machine and the failure patterns were assessed with the adhesive remnant index(ARI) after storage in distilled water at 37degrees C for 1 day, 1 week and 1, 3, and 6 months, respectively. The results were as follows: 1. The shear bond strengths at the 6 month in both Concise and Transbond were significantly higher than those at the 1 day, 1 week and 1 month(P<0.05). There were positive correlations between shear bond strength and water immersion time in both Concise and Transbond(P<0.01). 2. There were no significant differences in shear bond strength between Concise and Transbond. 3. The brackets were failed primarily at the bracket base-adhesive interface and there was no significant difference in the incidence of ARI scores according to the water immersion time.