Comparison of Alginate/Cockle Shell Powder Nanobiocomposite and Alginate/ Calcium Carbonate Bone Scaffolds on Osteoblast Growth
- Author:
Hemabarathy Bharatham
;
Zariyantey Abdul Hamid
;
Muhammad Fikri Musa
;
Nurnadiah Ahmad
;
Enoch Kumar Perimal
- Publication Type:Original Articles
- Keywords:
Bone scaffold;
Nano cockle shell powder;
calcium carbonate;
biomaterial;
osteoblast
- From:Malaysian Journal of Health Sciences
2017;15(2):1-7
- CountryMalaysia
- Language:English
-
Abstract:
Calcium carbonate (CaCO3
) plays a crucial role in influencing the growth of osteoblast. This study was conducted
to compare the performance of alginate/cockle shell powder nanobiocomposite (nCP) bone scaffold developed from
naturally occurring CaCO3 with alginate/calcium carbonate (CC) bone scaffold developed using synthetic CaCO3. The
study compares the performance of the scaffold in supporting the growth of osteoblast through in vitro evaluations as
well as initial biocompatibility observations through in vivo methods. Both scaffolds were developed using the mixture
of 40% alginate solution with either 60% of nano cockle shell powder or synthetic CaCO3 to obtain a three dimensional
scaffold structure. In vitro evaluation on calcium release and ALP enzyme activity was conducted on both scaffolds seeded
with osteoblast on day’s three, five and seven using commercial kits. In vivo observations using histological methods
were further conducted by implanting osteoblast seeded scaffold subcutaneously at the dorsum of 8 albino mice for 21
days. Findings from in vitro studies showed a significant increase (p < 0.05) in the release of calcium and ALP enzyme
activity in nCP scaffolds on day seven compared to days three and five of CC scaffold. Histological observations using
H&E and von Kossa staining showed infiltration and proliferation of osteoblast on both scaffolds as well as early stage
bone tissue formation. Formation of new blood vessels within the scaffolds was also observed in nCP scaffold. Both the
developed scaffolds were noted to support osteoblast growth and new tissue formation with better potentials displayed by
nCP scaffolds comparatively. This study shows that naturally occurring CaCO3 obtained from cockle shells in the form
of nano powder has good potentials to be used as a biomaterial for bone tissue engineering applications.