The Effects of Citric Acid on HA coated Implant Surface.
10.5051/jkape.2007.37.3.575
- Author:
Joong Cheon KIM
1
;
Young Hyuk KWON
;
Joon Bong PARK
;
Yeek HERR
;
Jong Hyuk CHUNG
;
Seung Il SHIN
Author Information
1. Department of Periodontology and Institute of Oral Biology, School of Dentistry, Kyung Hee University, Korea. kyhyuk@khu.ac.kr
- Publication Type:Original Article
- Keywords:
citric acid;
HA coated implant surface;
peri-implantitis
- MeSH:
Citric Acid*;
Hydrogen-Ion Concentration;
Peri-Implantitis;
Titanium
- From:The Journal of the Korean Academy of Periodontology
2007;37(3):575-584
- CountryRepublic of Korea
- Language:Korean
-
Abstract:
The present study was performed to evaluate the effect of citric acid on the change of implant surface microstructure according to application time. Implants with pure titanium machined surface, and HA coated surface were utilized. Pure titanium machined surface and HA coated surface were rubbed with pH 1 citric acid for 30s., 45s., 60s., 90s., and 120s. respectively. Then, the specimens were processed for scanning electron microscopic observation. The following results were obtained. 1. The specimens showed a few shallow grooves and ridges in pure titanium machined surface implants. The roughness of surfaces conditioned with pH 1 citric acid was slightly increased. 2. In HA-coated surfaces, round particles were deposited irregularly. The specimens were not significant differences within 45s. But, began to be changed from 60s. The roughness of surfaces was lessened and the surface dissolution was increased relative to the application time. In conclusion, pure titanium machined surface implants and HA coated surface implants can be treated with pH 1 citric acid for peri-implantitis treatment if the detoxification of these surfaces could be evaluated.