Bonding values of two contemporary ceramic inlay materials to dentin following simulated aging.
- Author:
Ashraf Abdelfattah KHALIL
1
;
Khalid Mohamed ABDELAZIZ
Author Information
- Publication Type:Original Article
- Keywords: Inlays; Bonding; Ceramics; Resin cement; Dentin
- MeSH: Adhesives; Aging*; Ceramics*; Dentin*; Inlays*; Molar; Resin Cements; Tooth
- From:The Journal of Advanced Prosthodontics 2015;7(6):446-453
- CountryRepublic of Korea
- Language:English
- Abstract: PURPOSE: To compare the push-out bond strength of feldspar and zirconia-based ceramic inlays bonded to dentin with different resin cements following simulated aging. MATERIALS AND METHODS: Occlusal cavities in 80 extracted molars were restored in 2 groups (n=40) with CAD/CAM feldspar (Vitablocs Trilux forte) (FP) and zirconia-based (Ceramill Zi) (ZR) ceramic inlays. The fabricated inlays were luted in 2 subgroups (n=20) with either etch-and-bond (RelyX Ultimate Clicker) (EB) or self-adhesive (RelyX Unicem Aplicap) (SA) resin cement. Ten inlays in each subgroup were subjected to 3,500 thermal cycles and 24,000 loading cycles, while the other 10 served as control. Horizontal 3 mm thick specimens were cut out of the restored teeth for push out bond strength testing. Bond strength data were statistically analyzed using 1-way ANOVA and Tukey's comparisons at alpha=.05. The mode of ceramic-cement-dentin bond failure for each specimen was also assessed. RESULTS: No statistically significant differences were noticed between FP and ZR bond strength to dentin in all subgroups (ANOVA, P=.05113). No differences were noticed between EB and SA (Tukey's, P>.05) bonded to either type of ceramics. Both adhesive and mixed modes of bond failure were dominant for non-aged inlays. Simulated aging had no significant effect on bond strength values (Tukey's, P>.05) of all ceramic-cement combinations although the adhesive mode of bond failure became more common (60-80%) in aged inlays. CONCLUSION: The suggested cement-ceramic combinations offer comparable bonding performance to dentin substrate either before or after simulated aging that seems to have no adverse effect on the achieved bond.