Optimizing concentration of bioactive glass that promotes early enamel caries remineralization
10.11958/j.issn.0253-9896.2015.10.027
- VernacularTitle:生物活性玻璃促进早期釉质龋再矿化最适浓度的研究
- Author:
Qian FANG
;
Xue ZHOU
;
Yu MU
;
Nailing CHEN
;
Yanping ZHAO
;
Qinghui LIU
;
Wei PENG
- Publication Type:Journal Article
- Keywords:
dental caries;
dental enamel;
tooth remineralization;
early enamel caries;
bioactive glass;
microhardness
- From:
Tianjin Medical Journal
2015;(10):1187-1189,1190
- CountryChina
- Language:Chinese
-
Abstract:
Objective To explore the optimum concentration of bioactive glass that promotes early enamel caries remineralization. Methods Fresh bovine incisors were selected and used for enamel specimen preparation. All specimens were randomly divided into two groups:micro hardness group and fluorescence group. Both groups were further divided into 3%, 6%and 9%groups. These specimens were placed in containers with demineralization liquid at 37℃for 72 hours. Then they were treat with 3%, 6%and 9%bioactive glass solution respectively twice a day for 5 minutes each. Samples in all three groups were dipped circularly into an artificial demineralization solution and an artificial saliva solution for 15 days. The mi?crohardness of enamel surface was measured before and after demineralization and remineralization. The different value of microhardness before and after remineralization was calculated. The thickness of fluorescence beneath the surface of early enamel caries was observed to evaluate the extend of remineralization effect. Results The difference in value of micro hard?ness in 6%group was the highest while that in 3%group was the lowest. The differences were significant. The difference in value of demineralization depth in 6%group was greater than those in 3%and 9%groups (P<0.05). There was no statistical?ly significance between those in 3%group and 9%group. Conclution The optimum concentration of bioactive glass solu?tion that promotes the remineralization of early enamel caries is 6%, which is ideal for remineralization of early enamel caries.