Preparation of chitosan/polyvinyl alcohol composite scaffold at different mass ratios:Comparison of structure and characteristics
- VernacularTitle:不同质量配比壳聚糖/聚乙烯醇复合材料组织工程支架的制备:结构及性能比较
- Author:
Qinhua LI
;
Lei HUANG
;
Hui LI
;
Sihan FANG
- Publication Type:Journal Article
- From:
Chinese Journal of Tissue Engineering Research
2007;0(03):-
- CountryChina
- Language:Chinese
-
Abstract:
BACKGROUND:Polyvinyl alcohol(PVA)has similar water content as human tissues,good biocompatibility and high mechanical strength,thereby being utilized as tissue-engineered matrix material.However,the modification in cellular affinity benefits the function as tissue regeneration scaffold materials.OBJECTIVE:To prepare chitosan(CS)/PVA composite scaffold and explore the feasibility of serving as a scaffold for tissue engineering.METHODS:Scaffolds of CS/PVA was fabricated by blending PVA-124 with various amounts of CS using film forming,particle forming,and free-drying methods.Water content,light transmittance,and swelling ratio were tested.Scanning electron microscope was used to observe the configuration of the cross section.RESULTS AND CONCLUSION:A total of 7 different proportional scaffolds were obtained with different PVA and CS dosage.The composite film showed light transmittance between 70%-80%,high water content between 121.2%-162.5% and swelling ratio between 60.3%-133.7%.Composite particle and sponge obtained water content between 82.0%-461.2% and 280.8%-1 939.0%.Composite scaffold with the amount ratio of PVA 0.75 g/CS 0.15 g exhibited the best performance.Scanning electron microscope showed that at a mass ratio of PVA 0.75 g/CS 0.15 g,the scaffold prepared by freeze-drying method had regular,fluffy inner structure,with good mechanics and high water content.