The effect of three different investing materials on complete denture flasking deformation
10.3760/cma.j.issn.1008-6706.2013.17.007
- VernacularTitle:三种包埋材料对全口义齿蜡型形变大小的影响
- Author:
Yan XIA
;
Zhihong ZHANG
;
Chenchen HUANG
- Publication Type:Journal Article
- Keywords:
Denture,complete,lower;
Technology,dental;
Calcium sulfate;
Siloxanes
- From:
Chinese Journal of Primary Medicine and Pharmacy
2013;20(17):2576-2578,后插1
- CountryChina
- Language:Chinese
-
Abstract:
Objective To investigate the effect of different investing materials on the complete denture flasking deformation.Methods The denture wax casts were invested by plaster,dental stone,and dental stone together with silicone,respectively.8 trial dentures were randomly chosen from above each group,and 4 reference points were selected in the cast.The conventional water bath polymerization system was used for the process.The distance between reference points were measured before and after thermally processing the Acrylic base.F test and Kruskal-Wallis H test were applied for statistical analysis.Results The distance between A and B (F =3.768,P =0.040) and the mean of total distance among O,A,B and C(F =4.830,P =0.019) had statistically significant differences among the three groups.The deformation variance of Group 1 (a conventional plaster) between 175μm and 267μm was maximum.The deformation values of Group2 (a dental stone) was appropriate with Group3 (a dental stone + a silicone).Smoothness (x2 =17.575,P ＜ 0.01) was statistically different among the three groups.Conclusion The flaskingprocess with the plaster had the maximum movement.The process with dental stone showed the minimal toothmovement,the process with the dental stone along with with thesilicone caused a similar movement as from the single dental stone but resulted in a smoother denture surface.