Bonding between nickel-based alloys and resin-veneers: strength and mechanism
- VernacularTitle:镍基合金与饰面树脂的粘结强度及其粘结机制
- Author:
Xiaoqian QIU
;
Dalin WANG
;
Qingfu ZHANG
- Publication Type:Journal Article
- Keywords:
nickel;
alloy;
resin-veneer;
shear strengths
- From:
Academic Journal of Second Military Medical University
2000;0(11):-
- CountryChina
- Language:Chinese
-
Abstract:
Objective:To determine the shear bond strength and analyze the bonding mechanism of home-made and imported nickel-based alloys to resin-veneers.Methods: Home-made and imported alloy disks were cast by lost-wax technique and embedded in acrylic resin fabricating cylinders.Sixteen specimens of each alloy were divided into 2 subgroups: thermocycling group and non-thermocycling group.Specimens in thermocycling groups were submitted to thermocycling(300 cycles) and those in non-thermocycling groups were just stored in water at 37?C for 24 h(0 cycles).Then the shear bond strength values were determined by universal testing machine.The highest shear bond strength values were recorded and metallurgical analysis was performed on the interface between alloys and resin-veneers.Results: The shear bond strength values of both alloys to resin-veneers were relatively high either before or after thermocycling.The shear bond strength values of home-made alloy+thermocycling group,imported alloy+thermocycling group,home-made alloy+non-thermocycling group and imported alloy + non-thermocycling group were(10.50?2.72),(13.12?2.82),(15.51?3.04) and(18.44?3.15) MPa,respectively.The bond strength was significantly different before and after thermocycling for both alloys(P