Effects of cooling rate on the bonding strength of cast titanium to porcelain
- VernacularTitle:降温速率对Noritake瓷与铸钛结合强度的影响
- Author:
Ruobing ZHANG
;
Yumei ZHANG
;
Shaopeng QI
- Publication Type:Journal Article
- Keywords:
Cooling rate;
Cast titanium;
Porcelain;
Bonding strength
- From:
Journal of Practical Stomatology
2001;0(03):-
- CountryChina
- Language:Chinese
-
Abstract:
Objective:To study effects of the cooling rate on the bonding characteristics of titanium porcelain bonded to cast titanium.Methods:According to ISO 9693,24 cast titanium plates(25 mm?3 mm?0.5 mm)were prepared.The middle of the samples(8 mm?3 mm) were bonded with bonding porcelain,opaque porcelain and dentin porcelain.The specimens from each porcelain-metal combination group were randomly assigned into four experimental cooling rate conditions,namely cooling rate of 15,40,50 and 100 ℃/min.A three-point-flexure-test was used to evaluate the bonding strength of titanium porcelain bonded to cast pure titanium.SEM/EDS were taken to characterize the failed surface of the titanium-porcelain interface.Statistical analyses were made by one-way analysis of variance(ANOVA).Results:The bonding strength of 15 ℃/min group was significantly higher than other groups.There were no significant differences in bond strength between 40 ℃/min and 50 ℃/min groups.SEM/EDS revealed that with an increase cooling rate,the remained porcelains on the titanium side were decreased.Conclusion:The 15 ℃/min cooling rate might be an effective method to improve the titanium-porcelain bonding strength.