An in vitro study of the biocompatibility of Ti-Nb-Zr Bate titanium alloy
- VernacularTitle:钛铌锆?钛合金生物相容性的体外实验研究
- Author:
Qingwei JIA
;
Congqin NING
;
Dongyan DING
- Publication Type:Journal Article
- Keywords:
titanium-niobium-zirconium;
biocompatible materials;
in vitro
- From:
Orthopedic Journal of China
2006;0(06):-
- CountryChina
- Language:Chinese
-
Abstract:
[Objective]To evaluate the biocompatibility of a new bate titanium alloys made of titanium, niobium and zirconium (Ti-Nb-Zr) which have higher strength and lower elastic modulus by in vitro study.[Method](1)the cell toxicity of Ti-Nb-Zr was evaluated using L-929 cell line's relative growth rate (RGR) which was transformed into 6 toxicity ranks in according with the national standard;(2)the J774A.1macrophages cultured with Ti-Nb-Zr particles whose diameter was about 1 ?m for 24-48 hours were observed using inverted phase contrast microscopy and transmission electron microscopy. Expression of IL-6 and TNF-? mRNA in these cells were measured using RT-PCR technique. The TNF-? in the supernatant was also measured using ELISA method. All the results were compared with the traditional orthopedic implants metal materials such as Ti-6Al-4V and Co-Gr-Mo.[Result]The cell toxicity of Ti-Nb-Zr was ranked zero degree. The particles could be seen in the macrophages under the light microscopy. Ti-Nb-Zr particles made the J774.A1 macrophages less configurative changes than Ti-6Al-4V and Co-Gr-Mo did.Expressions of IL-6 and TNF-? mRNA in J774.A1 cell were increased after stimulation for 48 hours by all kinds of metallic materials. The TNF-? in the supernatants of Ti-Nb-Zr group were less than that of the Ti-6Al-4V and Co-Gr-Mo groups (P