Color measurements of dental CAD/CAM alumina-galss-composites
- VernacularTitle:渗透玻璃对牙科CAD/CAM用氧化铝玻璃复合体颜色的影响
- Author:
Yuanfu YI
;
Ning WEN
;
Zhongyi WANG
- Publication Type:Journal Article
- Keywords:
CAD/CAM;
Dental ceramic;
Alumina;
Glass;
Color
- From:
Journal of Practical Stomatology
1996;0(02):-
- CountryChina
- Language:Chinese
-
Abstract:
Objective: To measure the color of dental CAD/CAM alumina-glass-composites(AGC). Methods: Dental CAD/CAM alumina block were infiltrated at 1 120 ℃ by laboratory made AG1,AG2,AG3 and AG4 color serials of infiltration glass powder and Vita In-Ceram Alumina AL1,AL2,AL3 and AL4 infiltration glass respectively. Specimens were made with the area of 10 mm?10 mm,thickness of 0.5,1 and 1.5 mm respectively. Color parameters were measured by Minolta CM-2600d spectrophotometer. Results:The specimen with the thickness of 1 mm was used as the standard for color measurement.After infiltration with AL1-AL4 glass powder,the color parameters of Vita alumina core ceramic were L*: 69.39-78.41,a*:1.82- 4.02,b*:18.35-24.42,when infiltrated with AG1-AG4 glass powder, the color parameters of CAD/CAM AGC were L*:68.80-78.44,a*:1.32- 4.75,b*:16.85- 21.86. b*value and chroma of the AG3 core ceramic were lower than that of AL3 core ceramic,while a* value was higher.b* value and chroma of the AG1 and AG2 core ceramic were lower than that of AL1 and AL2 core ceramic. The reflectance curve of CAD/CAM AGC infiltrated by AG1-AG4 glass powder demonstrated the similar trend as that of the core ceramic infiltrated by Vita In-Ceram glass powder. Conclusion: The color range and surface reflection rate of laboratory made AG1-AG4 AGC are similar with those of Vita AL1-AL4 In-Ceram Alumina core and may meet the need of color match with veneer ceramics.