Biocompatibility of nano-hydroxyapatite/polyamide 66 composite with human bone mesenchymal stem cells
10.3760/cma.j.issn.1671-7600.2016.03.012
- VernacularTitle:人骨髓基质干细胞与支架材料纳米羟基磷灰石/聚酰胺66的生物相容性研究
- Author:
Ang LI
;
Xiaoyu WANG
;
Zecheng LI
;
Qiannan XU
;
Zhenggang BI
- Publication Type:Journal Article
- Keywords:
Bone marrow cells;
Hydroxyapatite;
Polyamides;
Biocompatible materials
- From:
Chinese Journal of Orthopaedic Trauma
2016;18(3):241-246
- CountryChina
- Language:Chinese
-
Abstract:
Objective To explore the biocompatibility of nano-hydroxyapatite/polyamide 66 (nHA/PA66) with human bone mesenchymal stem cells (hBMSCs) after osteogenic induction.Methods After hBMSCs were isolated and cultured in vitro,the experiment was conducted in 3 groups.Group A were hBMSCs subjected to no osteogenic induction,group B hBMSCs subjected to osteogenic induction,and group C was the composite of nHA/PA66 with hBMSCs subjected to osteogenic induction.Adhesion of the cells onto the nHA/PA66 in group C was observed by electron microscope scanning.Growth and proliferation of the cells in groups B and C were detected by MTI test at 1,2 and 3 weeks.The ability of osteogenic differentiation of hBMSCs in vitro was analyzed by alkaline phosphatase (ALP) activity and alizarin red staining.The ability of osteogenic differentiation of hBMSCs on nHA/PA66 was tested by ALP activity.Results Electron microscope scanning showed that the cells spread and attached well on the surface of the composite scaffold in group C;the proliferation of the cells in groups B and C showed no significant difference (P ＞ O.05).These suggested that the proliferation of hBMSCs was not affected by nHA/PA66.The number of mineralized nodules in group B was significantly larger than in group A (P ＜ O.05);the ALP activity of the cells in group A was significantly lower than in group B at 6 and 12 days (P ＜ 0.05);no significant differences were observed between groups B and C (P ＞ 0.05).These indicated that the hBMSCs were capable of osteogenic differentiation which was not affected by nHA/PA66.In groups B and C,the ALP activity of the cells at 12 days was significantly higher than at 6 days,indicating the ALP activity increased with increased induction time (P ＜ 0.05).Conclusion nHA/PA66 can be used as a carrier of hBMSCs in bone tissue engineering because hBMSCs can well adhere to,proliferate,and differentiate into bone on nHA/PA66 scaffolds.