Biocompatibility of a new medical nickel-free stainless steel
10.3969/j.issn.2095-4344.2015.47.011
- VernacularTitle:新型医用无镍不锈钢的生物相容性评价
- Author:
Ying LIU
;
Wenjun ZHANG
;
Xuesong HAN
;
Desong ZHAN
- Publication Type:Journal Article
- From:
Chinese Journal of Tissue Engineering Research
2015;(47):7608-7612
- CountryChina
- Language:Chinese
-
Abstract:
BACKGROUND:BIOSSN4 nickel-free stainless steel is an austenitic medical stainless steel material, which has passed the standard hemolysis test, cytotoxicity assays and sensitization test of the National Institute for the Control of Pharmaceutical and Biological Products. OBJECTIVE:To evaluate theinvitro cytotoxicity and corrosion resistance of a new medical BIOSSN4 nickel-free stainless steel. METHODS:The L929 mouse fibroblasts suspension was seeded in 96-wel plates at a concentration of 1×108 /L, and were divided into five groups. BIOSSN4 nickel-free stainless steel extract, 316L stainless steel extract, gold aloy extract, lead material extract (positive control) and RPMI1640 medium (negative control) were added respectively. After 1, 2 and 3 days of culture, cel morphology was observed. The absorbance value in each group was determined using MTT assay. The relative cel proliferation rate was calculated. Toxicity grading was evaluated. In the simulated oral environment, the eletric potential of corrosion, current density of corrosion and polarization resistance of BIOSSN4 no-nickel stainless steel, 316L stainless steel and gold aloy were determined. RESULTS AND CONCLUSION:Within 3 days of culture, in lead material extract group, cels shrunk; the number of cels significantly reduced; the relative growth rate was lower than that in the other four groups (P < 0.05). In the other four groups, the cel morphology was good, and the relative growth rate was over 75%. The toxicity of BIOSSN4 nickel-free stainless steel extract, 316L stainless steel extract and gold aloy extract was grade 1. The toxicity of lead material extract was grades 2-3. These results demonstrate that BIOSSN4 nickel-free stainless steel has good biocompatibility. The corrosion resistance of BIOSSN4 nickel-free stainless steel is higher than that of the 316L stainless steel but lower than that of the gold aloys.