Biocompatibility of Fe-Cr-Mo soft magnetic alloy with chromium plating
10.3969/j.issn.2095-4344.2015.47.021
- VernacularTitle:铁铬钼软磁合金表面镀铬后的生物相容性
- Author:
Yinhua XIA
;
Ermin NIE
;
Rui JIANG
;
Chunyuan ZHANG
;
Jindi ZENG
;
Jizhou TAN
- Publication Type:Journal Article
- From:
Chinese Journal of Tissue Engineering Research
2015;(47):7660-7664
- CountryChina
- Language:Chinese
-
Abstract:
BACKGROUND:Studies have demonstrated that Fe-Cr-Mo soft magnetic aloy has desired magnetic properties and machining properties. Surface Cr6+ plating treatment can significantly enhance the corrosion resistance in oral environment, but its biosecurity needs further testing. OBJECTIVE: To evaluate the biocompatibility of Fe-Cr-Mo soft magnetic aloy with chromium plating. METHODS:Logarithmic growth phase L929 cel suspension was obtained and seeded in 96-wel plates at a cel concentration of 6×107/L. Pure titanium extract, Fe-Cr-Mo soft magnetic aloy original extract, Cr6+-plated Fe-Cr-Mo soft magnetic aloy and PVC extract were added respectively. After 5 days of culture, cel morphology and adherent circumstances were observed. The absorbance value was detected using cel counting kit-8 assay. The relative growth rate of cels in each group was calculated. The cytotoxicity grades of materials were evaluated. RESULTS AND CONCLUSION:In the pure titanium extracts group, the cels with normal morphology showed good adherent growth and no cytotoxicity. In the Fe-Cr-Mo soft magnetic aloy original extract group, the cel morphology and growth status were both good, with occasionaly individual cel lysis. Scattered reddish brown particles were visible in the culture solution, showing no or very mild cytotoxicity. In Cr6+-plated Fe-Cr-Mo soft magnetic aloy extract group, the cels grew wel and showed no or very mild cytotoxicity. In PVC extract group, more than 70% of cels were vacuole-shaped and presented with pyknosis or dissolution, there was a large number of cel debris, and cel growth was inhibited in over 50% cels, showing moderate cytotoxicity or above. The cytotoxicity of Cr6+-plated Fe-Cr-Mo soft magnetic aloy extract was grade 0-1. These results demonstrate that Fe-Cr-Mo soft magnetic aloywith chromium plating has good biocompatibility.