Comparative study on the compressive strength of porcelain crown with different base materials
10.3969/j.issn.1001-3733.2015.05.002
- VernacularTitle:不同基底材料烤瓷冠抗压缩破坏力的对比研究
- Author:
Jie WU
;
Zhiyu CHEN
;
Yafei QIU
;
Ning LI
;
Changjun GUO
- Publication Type:Journal Article
- Keywords:
Co-Cr;
Titanium;
Zirconia;
Porcelain crown;
Compressive strength
- From:
Journal of Practical Stomatology
2015;(5):607-610
- CountryChina
- Language:Chinese
-
Abstract:
Objective:To compare the compressive strength of porcelain crown with Co-Cr,CAD/CAMpure titanium and CAD/CAM zirconia respectively.Methods:Metal models of simulating crown core of the ideal premolar were manufactured,digital data of the met-al model were obtained by CAD/CAMsystem,the basement crowns of Co-Cr,CAD/CAMpure titanium and CAD/CAMzirconia were respectively made(n =5),size of each crown was kept the same and the spcimens were set as group A,B and C respectively.Then masking porcelain and body porcelain were fired on basement crowns according to the instructions.The thickness of the porcelain was kept the same.All of the porcelain crowns were located on the Instron testing machine,the compression strength force values were measured.Data were statistically analysed by SPSS 1 3.0 software.The bonding surface of basement material and porcelain was observed by SEMafter compressive failure.Results:The compressive strength(N)of group A,B and C was 2 990 ±1 88,2 305 ±1 57,2 1 50 ± 1 31 ,A vs B or C,P <0.05,B vs C,P >0.05.Conclusion:All the 3 base materials with porcelain crown satisfy the clinical require-ments.The compressive strength of Co-Cr porcelain crown is stronger than that of CAD/CAMpure titanium porcelain crown and CAD/CAMzirconia porcelain crown.